22. The below figure is a portion of the Fe-Fe;C phase diagram, fill the represent meaning of thesenumbers in the diagram and answer the below question.T( C)1600321400411200-1148° C9.7100010800727°6001140056.7(Fe)C, wt% C(1)(2)(3).(4).(5)(6)(7)(8)(9)(10)(11)_to

To determine the compositions at the marked position in the Iron-iron carbide diagram.

Answered: TC C) 1600 3 2 1 1400 5 1148 1200아 7…

Engineering

Mechanical Engineering

TC C) 1600 3 2 1 1400 5 1148 1200아 7 100아 10 800 727 600 11

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The figure below shows Pb-Sn phase diagram. What is the composition of Pb and Sn at point 1? 1200 1000 Liquid a +L 779 C (Tg) B+L 6 800 8.0 71.9 G 91.2 600 400 200 20 40 60 80 100 (Pb) Composition (wt% Sni (Sn) Callister Jr., W.D., 2007 O a. 80 wt % Sn and 20 wt % Pb O b. 10 wt % Sn and 90 wt % Pb O c. 90 wt % Sn and 10 wt % Pb O d. 20 wt % Sn and 80 wt % Pb Temperature ("C)
Consider Cu - Ag Phase diagram below: 1200 A -Liquidus 1000 Liquid -Solidus 779°C (TE) 800 Temperature (°C) 600 400 a C 200 0 B 8.0 (Cag) Solvus a +L a + ß E 71.9 (CE) B+L 91.2 (CBE) B H 1 1 1 1 1 { ( L 20 40 60 80 100 (Cu) Composition (wt% Ag) (Ag) Consider 71.9% Ag-28.1% Cu, which is cooled below 779°C. What is the composition of the phases present just below 779°C and give the amount of beta phase present
Temperature ("C) Temperature ($1 Consider 1 kg of Copper - Silver alloy (Cu - Ag) containing 75 wt% Ag. The phase diagram of the alloy is shown in the figure below. The alloy is cooled to 778 °C (just below the eutectic temperature). Calculate the mass in kg of the eutectic phase B (phase B that appears during the eutectic reaction) that forms? Composition (at% Ag 20 40 60 100 2200 80 1200 2000 Liquidus 1000 LIquid 1800 Solidus 1600 800 779°C (T 80 91.2 1400 IC. 1200 600 Solvus T000 400 800 200 20 40 80 100 (Cu) Composioon wt A
For the given Ti-Cu phase diagram, specify all temperature-composition points at which eutectics, eutectoids, peritectic, and congruent phase transformations occur. Also, for each, write the reaction upon cooling. Temperature (°C) 1700 1500 1300 1100 900 700 500 0 (Ti) 1 B a 20 Ti₂Cu 40 Composition (wt% Cu) L TiCu TigCu4 60
Q1 / Two metals Beryllium (Be) and Silicon (Si) have melting points 1282°C and 1414 °C respectively, are completely soluble as liquids but completely insoluble as solids . They form a eutectic at 1090°C containing 61 wt% Si -39wt% Be? Determine the following:- 1- Draw the thermal equilibrium phase diagram and identify all phases are present in diagram ,then sketches what happens in microstructure when the alloys containing , a- 10wt% Si, b-70wt%Si , solidify completely. 2- Determine the composition and the amount of each phase for the alloy which contain 15 wt% Si-85wt% Be at 1150°C If the alloy is hypoeutectic determine the amount of eutectic at 600 °C? or hypereutectic and
For 40 wt% Sn – 60 wt% Pb alloy at 150 oC (at point B) as shown in Figure, i. State the name of phase(s) present. ii. Calculate the composition(s) of the phase(s) present. 600 300 Liquid 500 a+L 200 400 300 100 200 100 20 60 100 (Pb) (Sn) Composition (wt % Sn) Temperature ("C) Temperature ("F)
In the binary phase diagram for the Cu-Ni system in the Figure provided: 1. Draw the microstructures for each point for the alloy upon cooling (A-E) and label ALL phases! 2. What are the compositions (C's) of EVERY phase and the relative phase amounts (W's) for each microstructure A-E? Show all work! T(°C) (liquid) L 20 (a, solid) 30 A BUD E 40 Co OOOOO w 10 50 wt% Ni CL= Ca= CL= Ca= CL= Ca= C₁= Cu= C₁= Ca= WL= Wa= WL= Wα= W₁= W= W₁= Wa= W₁= Wu= A B E
5. For a 33 wt% Sn-67 wt% Pb alloy at 150°C: a. What phase(s) is (are) present? b. (b) What is (are) the composition(s) of the phase(s)? C. Calculate the relative amount of each phase present in terms of mass fraction. Temperature (°C) 300 200 100 327°C (Pb) 20 a + L 18.3 40 20 Composition (at % Sn) 60 183°C 40 a + ß Liquid 61.9 60 Composition (wt% Sn) Lead - Tin Phase Diagram 80 80 B+L 232°C 97.8 100 B | to 600 500 400 300 200 100 100 (Sn) Temperature (°F)
Question: Construct the hypothetical phase diagram for metals A and B between room temperature (20°C) and 700°C given the following information: The melting temperature of metal A is 480°C. The maximum solubility of B in A is 4 wt% B, which occurs at 420°C. The solubility of B in A at room temperature is 0 wt% B. One eutectic occurs at 420°C and 18 wt% B–82 wt% A. A second eutectic occurs at 475°C and 42 wt% B–58 wt% A. The intermetallic compound AB exists at a composition of 30 wt% B–70 wt% A, and melts congruently at 525°C. The melting temperature of metal B is 600°C. The maximum solubility of A in B is 13 wt% A, which occurs at 475°C. ● The solubility of A in B at room temperature is 3 wt% A.
b) Figure 1 shows a Cu-Ag phase diagram. Calculate the phase analysis for 50% Ag-50% Cu at 800 °C. Temperature (°C) 1200 1000 800 600 400 200 ( C (Cu) B 8.0 (C₂g) -Solidus Solvus 20 20 a + L Composition (at% Ag) 40 -Liquidus 779°C (TE) a + B 40 Liquid 60 Composition (wt% Ag) 60 71.9 (CE) 80 80 B+L 91.2 (CBg) G to 100 2200 2000 1800 F 1600 1400 1200 1000 800 600 400 100 Temperature (°F)
1-The microstructural design of Iron-Carbon(Fe-C) alloys has led to the development of vast range of steels for structural material applications. The phase diagram provide means for producing specific microstructures. Using the phase diagram below to answer the following questions A – If the liquid mixture of Fe-3%Wt C is slowly cooled from 1600 C to 1200C indicate the phase(S) that are present at 1200 C . Also calculate the composition of the of phases.(10) B-Describe the sequence of all phase transformation that accour from Fe-1.5%wt C is slowly cooled from 1600 C to 400 C. Use the diagram below to to describe the microstructures for each phase transformation (10)
b) Figure 2 is the tin-gold phase diagram, for which only single-phase regions are labeled. Write one (1) entectic point reaction and label all the non-label regions (i) - (viii). 1000 800 L (viii) Temperature (°C) 600 400 200 0 (Sn) (1) (v) B (vi) (iv) (ii) Y 8 20 40 60 80 Composition (wt% Au) Figure 2 Tin-gold phase diagram !(vii) T 100 (Au)