Textbook Question
Chapter 9, Problem 32QLP
When the American Plains states were settled, no trees existed for the construction of housing. Pioneers cut bricks from sod—basically, prairie soil as a matrix and grass and its root system as reinforcement. Explain why this approach was successful.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
Q4: The well-known that glass fibers are widely used in the manufacture of
composite materials:
1. What are the general drawbacks and benefits of glass fibers?
2. Classify the types of glass fibers.
3. Explain each type briefly.
4. How can recognize among each type by a designer?
5. Why there is a difference in the physical properties in comparison to each
other?
Q5: If the affordability of equipment does not matter for a designer,
1. What is the best technique can be used by the designer to produce missiles
parts made of a fiber with high strength/weight proportion? |
2. What are the benefits and drawbacks of that technique?
3. Give examples for other engineering applications of that technique.
4. What is the best type of polymer resins can be used in this technique and
why?
5. Explain this technique briefly.
"Donald breyer; Design of wood structures 6th edition" ,problem number 6.18
If you are the manufacturing engineer in a plant that produces composite materials to be used in different products, your customers require a tough, strong, and light material for their products What in terms of material will you recommend for the matrix, and for the reinforcement agent. What will be the form of reinforcement agent. What will be the direction of it. Your answer should be related only to the subjects you have studied in this course inly.
Chapter 9 Solutions
Manufacturing Engineering & Technology
Ch. 9 - Distinguish between composites and metal alloys.Ch. 9 - Describe the functions of the matrix and the...Ch. 9 - Name the reinforcing fibers generally used to make...Ch. 9 - What is the range in length and diameter of...Ch. 9 - List the important factors that determine the...Ch. 9 - Comment on the advantages and limitations of...Ch. 9 - What are the most commonly used matrix materials?...Ch. 9 - Describe the advantages of hybrid composites over...Ch. 9 - What material properties are improved by the...Ch. 9 - Describe the purpose of the matrix material.
Ch. 9 - What are the most common types of glass fibers?Ch. 9 - Explain the difference between a carbon fiber and...Ch. 9 - How can a graphite fiber be made electrically and...Ch. 9 - What is a whisker? What is the difference between...Ch. 9 - Describe the composition of boron fibers. Why are...Ch. 9 - Give a succinct definition of fiber, yarn, and...Ch. 9 - How do you think the use of straw mixed with clay...Ch. 9 - What products have you personally seen that are...Ch. 9 - Describe applications that are not well suited for...Ch. 9 - Is there a difference between a composite material...Ch. 9 - Identify metals and alloys that have strengths...Ch. 9 - What limitations or disadvantages do composite...Ch. 9 - Give examples of composite materials other than...Ch. 9 - Explain why the behavior of the materials depicted...Ch. 9 - Explain why fibers are so capable of supporting a...Ch. 9 - Do metal-matrix composites have any advantages...Ch. 9 - Give reasons for the development of ceramic-matrix...Ch. 9 - Explain how you would go about determining the...Ch. 9 - How would you go about trying to determine the...Ch. 9 - Glass fibers are said to be much stronger than...Ch. 9 - Describe situations in which a glass could be used...Ch. 9 - When the American Plains states were settled, no...Ch. 9 - By incorporating small amounts of a blowing agent,...Ch. 9 - Referring to Fig. 9.2c, would there be an...Ch. 9 - Calculate the average increase in the properties...Ch. 9 - In Example 9.1, what would be the percentage of...Ch. 9 - Calculate the percent increase in the mechanical...Ch. 9 - Calculate the stress in the fibers and in the...Ch. 9 - Repeat the calculations in Example 9.1 if (a)...Ch. 9 - Refer to the properties listed in Table 7.1. If...Ch. 9 - Plot the elastic modulus and strength of an...Ch. 9 - For the data in Example 9.1, what should be the...Ch. 9 - It is desired to obtain a composite material with...Ch. 9 - A rectangular cantilever beam, 100 mm high, 20 mm...Ch. 9 - What applications for composite materials can you...Ch. 9 - Using the information given in this chapter,...Ch. 9 - Would a composite material with a strong and stiff...Ch. 9 - Make a list of products for which the use of...Ch. 9 - Inspect Fig. 9.1 and explain what other components...Ch. 9 - Name applications in which both specific strength...Ch. 9 - What applications for composite materials can you...Ch. 9 - As with other materials, the mechanical properties...Ch. 9 - Developments are taking place in techniques for...Ch. 9 - As described in this chapter, reinforced plastics...Ch. 9 - Comment on your observations on the design of the...Ch. 9 - Make a survey of various sports equipment and...Ch. 9 - Several material combinations and structures were...Ch. 9 - It is possible to make fibers or whiskers with a...Ch. 9 - Describe how you can produce some simple composite...Ch. 9 - Gel spinning is a specialized process used in...Ch. 9 - Figure P9.65 shows a section of a...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Please highlight the area where the candidate materials are located in the figure.arrow_forwardProject 7: Decide whether you choose an amorphous or crystalline polymer for the following products and/or applications and justify your answer: A. Graphite: B. Tempered glass: C. High thermal conductivity ceramics: D. Hot coffee cups Briefly explain why amorphous polymers are transparent, while predominantly crystalline polymers appear opaque or translucent.arrow_forwardI need the solution of this question,please. Prove that the area fraction equal to volume fraction when using aligned fibers in composite materials.arrow_forward
- What are the main characteristics of concrete?arrow_forward2. Briefly describe one method for creating a hollow composite component. Sketch the component that you are considering. Explain what process you would use and describe all the steps, tooling and materials that are required (order is important for process steps). Describe any potential problem areas and how they could be avoided or compensated for.arrow_forwardQuestion 1 A composite material consists of 40% parallel carbon fibres with a Young’s modulus of 405 GPa in a matrix of epoxy resin with a Young’s modulus of 2.5 GPa. Calculate the Young’s modulus of the composite in the parallel and in the perpendicular directions of the fibres. Use the graphical method seen in class to show the possible value of the overall young modulus of your composite material.arrow_forward
- Q4) Why do we need orthotropic analysis for composite laminates? Q5) What are "kink-band" failure modes? Q6) How does moisture impact tension and compression strength in composites? Q7) What is the difference between a design value and an allowable and how does variability in material properties impact this behavior?arrow_forward16) Composite material with plastic as a matrix material can be used as biomaterials Select one: True Falsearrow_forwardd) A carbon fibre reinforced composite is made using a volume fraction of 77% carbon. The material properties of the constituent materials are listed below: E (GPa) Strength (MPa) 1500 900 Carbon fibre Epoxy 60 3 The composite is loaded in tension and a Young's modulus of 12.9GPa is measured. Is this the maximum modulus the composite can experience? Explain your answer. For a modulus of 12.9GPa, can the strength be estimated? Explain your answer. Relevant formulae: (4 marks) 1 E Vf E₁ 'm Em E = EfVf + EmVm o = ofV₁ + 0mVm +arrow_forward
- QUESTION 11 Compaction is. O Densification by the squeezing out of water from pores under load. O A decrease in the settlement potential of soil. O Densification by rearranging soil particles without the outfilow of water. O Densification by the squeezing out of water while maintaining the same volume. QUESTION 8 For a fill that is being compacted, increasing the water content: O May help to improve compaction of the fill. O May make compaction of the fill more difficult. O May have little or no effect on compaction of the soil. All of these answers.arrow_forwardb. i. Calculate the tensile modulus of elasticity of a unidirectional Kevlar-49 fibers epoxy composite material that contains 63% by volume of Kevlar 49 fibers and is stressed under isostrain conditions. The Kevlar 49 fibers have a tensile modulus of elasticity of 189.8 GPa and the epoxy matrix a tensile modulus of elasticity of 3.8 GPa.arrow_forwardCan you specify the thickness of composite wall used ?....because in question it is 96mm but in solution it is 92mm.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
composite-materials; Author: Tonya Coffey;https://www.youtube.com/watch?v=Vu6ik-bcKf4;License: Standard youtube license