Textbook Question
Chapter 23, Problem 7P
At a speed of 90 fpm, feed of 0.030 ipr, and depth at 0.625, calculate the input parameters for a lathe if the diameter to be machined (bored) is 6 in. Find the rpm
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
Q1: Determine the length, angle of contact, and width of a 9.75 mm thick
leather belt required to transmit 15 kW from a motor running at 900 r.p.m. The
diameter of the driving pulley of the motor is 300 mm. The driven pulley runs at
300 r.p.m. and the distance between the centers of two pulleys is 3 meters. The
density of the leather is 1000 kg/m³. The maximum allowable stress in the
leather is 2.5 MPa. The coefficient of friction between the leather and pulley is
0.3. Assume open belt drive.
5. A 15 kW and 1200 r.p.m. motor drives a compressor at 300 r.p.m. through a pair of spur gears having
20° stub teeth. The centre to centre distance between the shafts is 400 mm. The motor pinion is made
of forged steel having an allowable static stress as 210 MPa, while the gear is made of cast steel
having allowable static stress as 140 MPa. Assuming that the drive operates 8 to 10 hours per day
under light shock conditions, find from the standpoint of strength,
1. Module; 2. Face width and 3. Number of teeth and pitch circle diameter of each gear.
Check the gears thus designed from the consideration of wear. The surface endurance limit may be
taken as 700 MPa. [Ans. m = 6 mm; b= 60 mm; Tp=24; T=96; Dp = 144mm; DG = 576 mm]
4.
G
A micarta pinion rotating at 1200 r.p.m. is to transmit 1 kW to a cast iron gear at a speed of 192 r.p.m.
Assuming a starting overload of 20% and using 20° full depth involute teeth, determine the module,
number of teeth on the pinion and gear and face width. Take allowable static strength for micarta as 40
MPa and for cast iron as 53 MPa. Check the pair in wear.
Chapter 23 Solutions
Degarmo's Materials And Processes In Manufacturing
Ch. 23 - How is the tool-work relationship in turning...Ch. 23 - What different kinds of surfaces can be produced...Ch. 23 - How does form turning differ from ordinary...Ch. 23 - What is the basic difference between facing and a...Ch. 23 - Which operations shown in Figure 23.3 do not form...Ch. 23 - Why is it difficult to make heavy cuts if a form...Ch. 23 - Show how equation 23.6 is an approximate equation.Ch. 23 - Why is the spindle of the lathe hollow?Ch. 23 - What function does a lathe carriage have?Ch. 23 - Why is feed specified for a boring operation...
Ch. 23 - Why are depths of cut in boring usually smaller...Ch. 23 - How can work be held and supported in a lathe?Ch. 23 - How is a workpiece that is mounted between centers...Ch. 23 - What will happen to the workpiece when turned, if...Ch. 23 - Why is it not advisable to hold hot-rolled steel...Ch. 23 - How does a steady rest differ from a follow rest?Ch. 23 - What are the advantages and disadvantages of a...Ch. 23 - Why should the distance the cutting tool overhangs...Ch. 23 - Prob. 19RQCh. 23 - How can a tapered part be turned on a lathe?Ch. 23 - Why might it be desirable to use a heavy depth of...Ch. 23 - If the rpm for a facing cut (assuming given work...Ch. 23 - Why is it usually necessary to take relatively...Ch. 23 - How does the corner radius of the tool influence...Ch. 23 - What effect does a BUE have on the diameter of the...Ch. 23 - How does the multiple-spindle screw machine differ...Ch. 23 - Why does boring ensure concentricity between the...Ch. 23 - Why are vertical spindle machines better suited...Ch. 23 - Prob. 29RQCh. 23 - Prob. 30RQCh. 23 - In which figures in this chapter is a dead center...Ch. 23 - Prob. 32RQCh. 23 - In which figures in this chapter showing setups do...Ch. 23 - How many form tools are being utilized in the...Ch. 23 - Prob. 35RQCh. 23 - Select the speed, feed, and depth of cut for...Ch. 23 - Calculate the rpm NS to run the spindle on a lathe...Ch. 23 - The lathe in problem 2 has rpm settings of 20, 30,...Ch. 23 - Calculate the cutting time if the length of cut is...Ch. 23 - Calculate the metal removal rate for machining at...Ch. 23 - Determine the speed, feed, and depth of cut when...Ch. 23 - At a speed of 90 fpm, feed of 0.030 ipr, and depth...Ch. 23 - Calculate the cutting time for a 4-in. length of...Ch. 23 - For a boring operation at V=90,fr=0.030, and...Ch. 23 - A cutting speed of 100 sfpm has been selected for...Ch. 23 - The following data apply for machining a part on a...Ch. 23 - A finish cut for a length of 10 in. on a diameter...Ch. 23 - A workpiece 10 in. in diameter is to be faced down...Ch. 23 - A hole 89 mm in diameter is to be drilled and...
Additional Engineering Textbook Solutions
Find more solutions based on key concepts
The following is a multiplication problem in traditional base ten notation. Each letter represents a different ...
Computer Science: An Overview (13th Edition) (What's New in Computer Science)
(Displaying a Square of Asterisks) Write a method squareOfAsterisks that displays a solid square (the same numb...
Java How to Program, Early Objects (11th Edition) (Deitel: How to Program)
Look at the following class definition: public class ClassD extends ClassB { (Member Declarations ) } Because C...
Starting Out with Java: From Control Structures through Objects (7th Edition) (What's New in Computer Science)
How is the hydrodynamic entry length defined for flow in a pipe? Is the entry length longer in laminar or turbu...
Fluid Mechanics: Fundamentals and Applications
16. In a simple electric circuit, the current (I) must remain below 40 milliarr.ps (I < 40 mA) and must also sa...
Thinking Like an Engineer: An Active Learning Approach (4th Edition)
Why is the study of database technology important?
Database Concepts (8th Edition)
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- I want to solve these choicesarrow_forward2. A spur gear made of bronze drives a mid steel pinion with angular velocity ratio of 32: 1. The pressure angle is 14½. It transmits 5 kW at 1800 r.p.m. of pinion. Considering only strength, design the smallest diameter gears and find also necessary face width. The number of teeth should not be less than 15 teeth on either gear. The elastic strength of bronze may be taken as 84 MPa and of steel as 105 MPa. Lewis factor for 14½½ pressure angle may be taken 0.684 0.124 y = No. of teeth as [Ans. m 3 mm; b= 35 mm; Dp = 48 mm; D= 168 mm]arrow_forwardQ2. Determine the safety factors for the bracket rod shown in Figure 2 based on both the distortion-energy theory and the maximum shear theory and compare them. Given: The material is 2024-T4 aluminum with a yield strength of 47 000 psi. The rod length /= 6 in. and arm a = 8 in. The rod outside diameter od 1.5 in., id = 1 in, h=2 in., t=0.5 in., Load F= 1000 lb. Assumptions: The load is static and the assembly is at room temperature. Consider shear due to transverse loading as well as other stresses. (Note: solve in SI units) wall tube Figure 2 armarrow_forward
- The question has been set up with all the cuts needed to accurately derive expressions for V(x) and M(x). Using the cuts free body diagrams set up below, derive expressions for V(x) and M(x). If you use the method of cuts then validate your answers using calculus or vice versa.arrow_forwardIt is required to treat 130 kmol/hr of chloroform-air feed gas mixture that contains 12% chloroform. It is required to remove 93% of chloroform using 150 kmol/hr of solvent that contains 99.6% water and 0.4% chloroform. The cross sectional area of the column is 0.8 m². Calculate the column height using the following data; kx'.a = 1.35 (kmol/m³.s (Ax)), and ky'.a = 0.06 (kmol/m³.s (Ay)), kx/ky = 1.35, and the equilibrium data are: X 0 0.0133 0.033 y 0 0.01 0.0266 0.049 0.064 0.0747 0.0933 0.1053 0.0433 0.06 0.0733 0.111 0.1 0.12 0.14arrow_forward४ B: Find the numerical solution for the 2D equation below and calculate the temperature values for each grid point shown in Fig. 2 (show all steps). (Do only one trail using following initial values and show the final matrix) [T1] T₂ T3 [T] 1 = [0] 0 0 d dx dx) (ka)+4(ka) = dy -20xy, k = 1 + 0.3 T ge L=3cm, 4x= Ay B.Cs.: at x=0=LT=0°C at y=0-L T=10°C Fig. (2)arrow_forward
- : +0 العنوان use only Two rods fins) having same dimensions, one made orass (k = 85 Wm K) and the mer of copper (k = 375 W/m K), having of their ends inserted into a furna. At a section 10.5 cm a way from furnace, the temperature of brass rod 120 Find the distance at which the ame temperature would be reached in the per rod ? both ends are ex osed to the same environment. ns 2.05 ۲/۱ ostrararrow_forwardFor the beam show below, draw A.F.D, S.F.D, B.M.D 6 kN/m 1 M B. 3 M Marrow_forward1. Two long rods of the same diameter-one made of brass (k=85w/m.k) and the other made of copper (k=375 w/m.k) have one of their ends inserted into a furnace (as shown in the following figure). Both rods are exposed to the same environment. At a distance of 105 mm from the furnace, the temperature of the brass rod is 120°C. At what distance from the furnace will the same temperature be reached in the copper rod? Furnace 105 mm T₁ Brass rod ⑪ h Too- x2- Ti Copper rodarrow_forward
- : +0 العنوان use only Two rods fins) having same dimensions, one made orass (k = 85 Wm K) and the mer of copper (k = 375 W/m K), having of their ends inserted into a furna. At a section 10.5 cm a way from furnace, the temperature of brass rod 120 Find the distance at which the ame temperature would be reached in the per rod ? both ends are ex osed to the same environment. ns 2.05 ۲/۱ ostrararrow_forwardمشر on ۲/۱ Two rods (fins) having same dimensions, one made of brass(k=85 m K) and the other of copper (k = 375 W/m K), having one of their ends inserted into a furnace. At a section 10.5 cm a way from the furnace, the temperature brass rod 120°C. Find the distance at which the same temperature would be reached in the copper rod ? both ends are exposed to the same environment. 22.05 ofthearrow_forwardThe composite wall of oven with A= 1m² as in Fig.1 consists of three materials, two of with kA = 20 W/m K and kc = 50 W/m K with thickness, LA=0.3 m, L= 0.15 m and Lc 0.15 m. The inner surface temperature T1=900 K and the outer surface temperature T4 300 K, and an oven air temperature of To=1100 K, h=25 W/m². K. Determine kɛ and the temperatures T2 and T3 also draw the thermal resistance networkarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Precision Machining Technology (MindTap Course Li...Mechanical EngineeringISBN:9781285444543Author:Peter J. Hoffman, Eric S. Hopewell, Brian JanesPublisher:Cengage Learning
Precision Machining Technology (MindTap Course Li...
Mechanical Engineering
ISBN:9781285444543
Author:Peter J. Hoffman, Eric S. Hopewell, Brian Janes
Publisher:Cengage Learning
The Most Common Metal Machining Processes (Metal Machining Video 1); Author: Sofeast Ltd;https://www.youtube.com/watch?v=uxVJ3qtezGw;License: Standard YouTube License, CC-BY
Machining process and Machine Tools; Author: Amar Gandhi;https://www.youtube.com/watch?v=X2mUJ8baaE0;License: Standard Youtube License