Outline the steps involved in processing (a) ceramic and (b) glasses.
a)
Outline the steps involved in processing of ceramics and (b) glasses.
Explanation of Solution
Steps of Ceramics Processing:-
Step #1: Milling & Raw Material Procurement
The raw materials used in the process are milled materials typically found in mining sites that have been reduced from a larger size to a smaller size or even in some cases, it will be pulverized depends upon the end product required.
Step #2: Sizing
Here it is! During this step of the processing sequence, the materials which have gone through the milling, as well as the procurement process should be sized in order to separate the material desirable, from the ones non-usable. By means of controlling the size of the particle, it would result in a proper bonding along with a smooth surface of the finished product.
Step #3: Batching
This part of the process may be called “blending”. It calculates weighing, amounts and an initial blend of the raw materials. To have a material flow consistently into a pub mill hopper, in this process, Vibratory Feeders may be applied if you are having a lighter load capacity and the dusty hazardous environment.
Step #4: Mixing
To get a more physically and chemically homogeneous material before forming, the ceramic powder constituents are combined applying the process of blinging or mixing. Pug mills are the most favored piece of machinery utilized in the concerned step of the process while dealing with dry mixes.
Step #5: Forming
For forming, the materials including pastes, dry powders, or slurries are first consolidated, then molded to form a cohesive body of the desired end product. When it comes to dry forming, to get the desired shape, vibratory compaction may be used.
Step #6: Drying
The formed materials not only hold water but also a binder in its mix. This may lead to shrinkage, distortion, or warping of the product. Usually, convection drying happens to be the most used method where heated air gets circulated around the piece of ceramic which lessens the risk of those imperfections in the finished product.
Step #7: Glazing
This step is added to the process prior to firing. Typically, the glaze consists of oxides that give the product the desired finish look. All the raw materials are grounded in an attrition mill and ball mill. Customers are provided withVibratory Screeners which screened the glaze for giving the mixture a consistency which is not just uniform, but when applied to any of the ceramics, would be even and smooth. The glaze may be applied by dipping or spraying.
Step #8: Firing
The ceramics pass through a controlled heat process where the oxides are consolidated into a dense, cohesive body made up of uniform grain.
b)
Outline the steps involved in processing of glasses.
Explanation of Solution
Steps involved in processing glasses:-
Step #1: Melting and Refining
In order to make clear glass, the right set of raw materials is required. It comprises of Na2O (sodium oxide) from soda ash, SiO2 (silica sand), MgO (dolomite),CaO (calcium oxide) from limestone/dolomite, and Al2O3 (feldspar). The ingredients get mixed in their right proportions. The entire batch gets flown into a furnace that is heated as much as to 1500 degree Celsius.
Step #2: Float bath
From the furnace, the molten material goes into the float bath comprising of a mirror-like surface created from the molten tin. This material, then, flows into the bath at 1500 degree Celsius. It leaves the bath approximately at 650 degree Celsius. At the exit, its shape looks like a solid ribbon.
Step #3: Coating for reflective glass
If a reflective glass surface which helps in having the indoors cooler, is produced, then the procedures of coating are followed where either a soft or a hard coat gets applied on the ribbon surface which was cooled at high temperatures.
Step #4: Annealing
For removing the internal stresses built up in the glass, a procedure known as annealing is conducted. The procedure helps the glass ribbon to get through a layer that gets rid of any stresses on the surface of the glass, gradually cooling it to create the final hardened form. Because of it, cutting the glass and shaping it accordingly become easier.
Step #5: Inspecting
Through advanced and acute inspection technology, over 100 million inspections may be conducted throughout the glass manufacturing process for identifying stresses, air bubbles, or grains of sand which refuse to melt. It is vital in quality-proofing the finished form of glass.
Step #6: Cutting to order
Diamond steels are used to trim and cut the glass ribbons into square shapes.
Want to see more full solutions like this?
Chapter 18 Solutions
Manufacturing Engineering & Technology
- What is Gorilla Glass from Corning? Why does it outperform regular window glass in terms of mechanical properties? Briefly explain utilizing basic mechanical principles. When necessary, provide diagrams to further explain your response.arrow_forwardWhat are the differences between mud casting, hollow casting and full casting in ceramics?arrow_forwardBriefly explain why the properties of polycrystalline materials are most often isotropic.arrow_forward
- In a viscoelastic material, why does tan delta peak at the glass transition temperature?arrow_forwarda) : What is sintering process and classification of Ceramics? (b) : Explain the different types of ceramics materials, its properties and applications.arrow_forwardWhat is packing factor at the atomic level? What is the worth of its face-centered cubic crystal?arrow_forward
- You are working as a quality control engineer in a glass manufacturing company. What characterization technique would you use for routine and quick analysis to decide whether any impurities from the glass melting furnaces are introduced to your glass products? Explain your reasoningarrow_forwardIf we strain an FCC and an HCP single crystal, which of the two will have a larger amount of easy glide, and why?arrow_forwardExplain how macroscopic hardening occurs in semicrystalline polymers from the point of view of microscopic mechanisms (covered in the chapters indicated in the Callister's book). (maximum of 3 lines, not counting the space for possible schematic figures).arrow_forward
- P3 Examine the properties and applications of ceramic products manufactured using the sintering, hot pressing, chemical vapour deposition (CVD) and, reaction bonding processes.arrow_forwardIn BCC crystal system, write down the number of tetrahedral sites that could exist only in one face in the cellarrow_forwardCalculate the surface to volume ratio of nanomaterials obtained by breaking a cube of bulkmaterial into 8 small cubes of equal edge. The edge of the bulk cube is 6 cm.arrow_forward
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY