Textbook Question
Chapter 10, Problem 34QLP
Explain why, as shown in Table 10.1, gray cast iron undergoes expansion rather than contraction during solidification.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
Describe the stages involved in the contraction of metals during casting.(a) Contraction of the molten metals as it cools prior to its solidification.(b) Contraction of the metal during phase change from liquid to solid.(c) Contraction of the solidified metals as its temperature drops to ambient temperature.(d) All of above.(e) None of above.2. What kinds of defects in castings?(a) Hot tear.(b) Surface scar.(c) Plastic deformation.(d) Ductile flow.3. How does porosity have detrimental effects on the mechanical and physical properties ofcastings?(a) Pores in castings are resulted from internal discontinuities when that are prone topropagate under external stresses.(b) The toughness of a material will decrease as a result of porosity.(c) Physical properties, such as thermal and electrical conductivity, also be adverselyaffected by porosity.(d) Pores increase the strength and elastic modulus.(e) Porosity increases both the thermal and electrical conductivity4. Thermosetting plastics can…
2) Explain the reasons for shrinkage that occurs during solidification of a cylindrical
casting
What do you make for compensation of shrinkage depending on the
casting operation?
A riser in the shape of a sphere is to be designed for a sand casting mould at Simon Castings. The casting is a rectangular plate, with length = 400 mm, width = 250 mm, and thickness = 15 mm. If the total solidification time of the casting itself is known to be 7 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify.
Chapter 10 Solutions
Manufacturing Engineering & Technology
Ch. 10 - Explain why casting is an important manufacturing...Ch. 10 - Why do most metals shrink when they are cast?Ch. 10 - What are the differences between the...Ch. 10 - What are dendrites? Why are they called so?Ch. 10 - Describe the difference between short and long...Ch. 10 - What is superheat? Is it important? What are the...Ch. 10 - Define shrinkage and porosity. How can you tell...Ch. 10 - What is the function of chills? What are they made...Ch. 10 - Why is the Reynolds number important in casting?Ch. 10 - What is a sprue? What shape should a sprue have if...
Ch. 10 - How is fluidity defined? Why is it important?Ch. 10 - Explain the reasons for hot tearing in castings.Ch. 10 - Why is it important to remove dross or slag during...Ch. 10 - Why is Bernoullis equation important in casting?Ch. 10 - Describe thixocasting and rheocasting.Ch. 10 - What is Chvorinovs Rule?Ch. 10 - How is a blister related to a scab?Ch. 10 - Is there porosity in a chocolate bar? In an ice...Ch. 10 - Describe the stages involved in the contraction of...Ch. 10 - Explain the effects of mold materials on fluid...Ch. 10 - It is known that pouring metal at a high rate into...Ch. 10 - Describe the events depicted in Fig. 10.5.Ch. 10 - Would you be concerned about the fact that...Ch. 10 - Review Fig. 10.8 and make a summary, explaining...Ch. 10 - Make a sketch of volume vs. temperature for a...Ch. 10 - What practical demonstrations can you suggest to...Ch. 10 - Explain why a casting may have to be subjected to...Ch. 10 - List and explain the reasons why porosity can...Ch. 10 - Why does porosity have detrimental effects on the...Ch. 10 - A spoked handwheel is to be cast in gray iron. In...Ch. 10 - Which of the following considerations are...Ch. 10 - Explain why the constant C in Eq. (10.7) depends...Ch. 10 - Are external chills as effective as internal...Ch. 10 - Explain why, as shown in Table 10.1, gray cast...Ch. 10 - Referring to Fig. 10.11, explain why internal...Ch. 10 - Note the shape of the two risers shown in Fig....Ch. 10 - Is there any difference in the tendency for...Ch. 10 - What is the influence of the cross-sectional area...Ch. 10 - It has long been observed that (a) low pouring...Ch. 10 - In casting metal alloys, what would you expect to...Ch. 10 - If you inspect a typical cube of ice, you are...Ch. 10 - How can you tell whether cavities in a casting are...Ch. 10 - Describe the drawbacks to having a riser that is...Ch. 10 - Reproduce Fig. 10.2 for a casting that is...Ch. 10 - List the process variables that affect the...Ch. 10 - Assume that you have a method of measuring...Ch. 10 - A round casting is 0.2 m (7.9 in.) in diameter and...Ch. 10 - A cylinder with a diameter of 2.0 in. and a height...Ch. 10 - The constant C in Chvorinovs rule is given as 2.5...Ch. 10 - Pure copper is poured into a sand mold. The metal...Ch. 10 - For the sprue described in Problem 10.58, what...Ch. 10 - When designing patterns for casting, pattern...Ch. 10 - Can you devise fluidity tests other than that...Ch. 10 - Figure P10.55 indicates various defects and...Ch. 10 - The fluidity test shown in Fig. 10.9 illustrates...Ch. 10 - Utilizing the equipment and materials available in...Ch. 10 - One method of relieving stress concentrations in a...Ch. 10 - Describe the effects on mold design, including the...Ch. 10 - Small amounts of slag often persist after skimming...Ch. 10 - Design an experiment to measure the constants C...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- With a solidification factor of 0.97 x 106 s/m², the solidification time (in seconds) for a spherical casting of 200 mm diameter is...arrow_forwardTranslate the given information in your words, figures given below. Time-temperature cooling curve for the solidification of a small crucible of 50 percent antimony, 50% bismuth alloy.arrow_forwardA slab of 1500 mm x 750 mm x 500 mm is required to be cast using a sand casting process. It was observed previously that the total solidification time (T) for this casting = 1.6 min. Find out the cylindrical riser dimensions (diameter to height ratio = 1) for a solidification time T = 5 min.arrow_forward
- A cylinder with a diameter of 40 mm and height of 80 mm solidifies in 3 minutes in a sand casting operation. What is the solidification time if the cylinder height is doubled? What is the time if the diameter is doubled?arrow_forwardUnder uniform cooling, a spherical casting of 25 mm diameter undergoes volumetric solidification shrinkage and volumetric solid contraction of 2.5% and 6.2%, respectively. Determine the diameter of the casting after solidification.arrow_forward/The total solidification times of three casting shapes are to be compared: (1) a sphere with diameter= 10 cm, (2) a cylinder with diameter and length both = 10 cm, and (3) a cube with each side = 10 cm. The same casting alloy is used in the three cases. (a) Determine the relative solidification timesfor each geometry. (b) Based on the results of part (a), which geometric element would make the best riser? (c) If the mold constant = 3.5 min/cm2 in Chvorinov's rule, compute the total solidification time for each casting.arrow_forward
- A 5 cm cube solidifies in 4.6 min. Assume n=2. Calculate (a) the mold constant in Chvorinov’s rule and (b) the solidification time for a 1.25 cm X 12.5 cm X 15 cm bar cast under the same conditionsarrow_forwardA riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with length = 100 mm, width = 50 mm, and thickness = 10 mm. If the total solidification time of the casting itself is known to be 2.5 min, determine the diameter of the riser so that it will take 20% longer for the riser to solidify. %3D %3!arrow_forwardA flat plate is to be cast in an open mold whose bottom has a square shape that is 200 mm by 200 mm. The mold is 40 mm deep. A total of 106 mm3 of molten aluminum is poured into the mold. Solidification shrinkage is known to be 6.0%. The linear shrinkage due to thermal contraction after solidification is 1.3%. If the availability of molten metal in the mold allows the square shape of the cast plate to maintain its 200 mm by 200 mm dimensions until solidification is completed, determine the final dimensions of the plate.arrow_forward
- For sand-casting a steel rectangular plate with dimensions 80mm×120mm×20mm, a cylindrical riser has to be designed. The height of the riser is equal to its diameter. The total solidification time for the casting is 2 minutes. In Chvorinov‟s law for the estimation of the total solidification time, exponent is to be taken as 2. For a solidification time of 3 minutes in the riser, the diameter (in mm) of the riser is ____arrow_forwardA flat plate is to be cast in an open mold whose bottom has a square shape of 12.5 cm by 12.5 cm. The mold is 7.0 cm deep. A total of 350 cm³ of molten aluminum is poured into the mold. Solidification shrinkage is known to be 6.25%, which is a volumetric contraction, not a linear contraction. Table 7.1 lists the linear shrinkage due to thermal contraction after solidification. If the availability of molten metal in the mold allows the square shape of the cast plate to maintain its square dimension until solidification is completed, determine the final dimensions (width and height) of the plate.arrow_forwardIs it possible to manufacture a propeller of a commercial-scale heavy-duty ship using the Investment Casting Process? Briefly support your explanation with reasoning if it is not possible.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Explanation of Solidification of Metals & Alloys | Manufacturing Processes; Author: Magic Marks;https://www.youtube.com/watch?v=G5z9KknF_s8;License: Standard Youtube License