Use the exact values you enter to make later calculations. Consider the following figure. Temperature (°C) 400 300 200 100 05 Pb Solidus 19 -Solvus 20 Liquidus a+L 183" a + ß 61.9 40 60 Weight percent tin % Is the alloy hypoeutectic or hypereutectic? O hypoeutectic O hypereutectic Liquidus B+L 97.5 Solvus- 80 Solidus -B Sn A Pb-Sn alloy contains 55.7% a and 44.3% 6 at 100°C. Estimate the compositions (in wt% Sn) of a and 6 at 100°C. wt% Sn of a % % wt% Sn of B Determine the composition (in wt% Sn) of the alloy.

Use the exact values you enter to make later calculations. Consider the following figure. Temperature (°C) 400 300 200 100 05 Pb Solidus 19 -Solvus 20 Liquidus a+L 183" a + ß 61.9 40 60 Weight percent tin % Is the alloy hypoeutectic or hypereutectic? O hypoeutectic O hypereutectic Liquidus B+L 97.5 Solvus- 80 Solidus -B Sn A Pb-Sn alloy contains 55.7% a and 44.3% 6 at 100°C. Estimate the compositions (in wt% Sn) of a and 6 at 100°C. wt% Sn of a % % wt% Sn of B Determine the composition (in wt% Sn) of the alloy.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

QI/ Draw a thermal equilibrium diagram for the binary alloy system (Si –Au), from the following data:- a- Si melts at 1414 °C, and Au melts at 1064 °C , and identify all phases are present in the diagram. b- Eutectic is formed at 360°C containing 20 Wt% Si -80 Wt% Au . c- Determine the amount of each phase for the alloy which consist 60 Wt% Si- 40Wt % Au at 1200 °C and 800 °C ,then determine the amount of eutectic at 200 °C?
Temperature (°C) Based on the Ti-Al phase diagram (important for standard commercial alloy Ti-6Al- 4V) shown below, identify a) the type of reaction (e.g., peritectic) of the marked points (1) and b) list the phases before and after the reactions. 10 20 Weight percent aluminum 30 40 50 60 70 80 90 100 1800 1700 1670°C (1) 1600 L 1500 1400 a (ẞTi) 1300 1285 y-TiAl 1200 1100 1125 لسسسلسسسل 1000 Ti, Al (L10) 900 ር? 882°C 800 (aTi) (D019) 700 600 500 0 10 20 Ti Superlattice structures -TiAl, 665°C 660.452°C TiAl₂ aTiAl3 (Al). 20 30 40 50 60 70 80 90 100 Atomic percent aluminum PM Al
Consider Al- Cu system below. When Al-40%Cu is heated above 600°C and cooled slowly to a temperature of 545°C . Answer the following. Use the values of composition given in the phase diagram , no estimation .Each has two marks. 700 1200 600 L a + L 6 +L 548 1000 500 (CUAL) a + 6 800 400 600 300 5.65 10 20 30 32.7 40 50 52.5 (AI) Composition (wt % Cu) a. Percentage of the pro-eutectic phase present (% no decimal places) b. Composition of the pro- eutectic phase present (in %Cu one decimal place) c. What is the percentage of larger eutectic component present (% no decimal places) Temperature (°C) Temperature (°F)
Is it possible to have a copper-nickel alloy that, at equilibrium, consists of a liquid phase of composition 20 wt% Ni-80 wt% Cu and also an a phase of composition 37 wt% Ni-63 wt% Cu? If so, what will be the approximate temperature of the alloy? If this is not possible, explain why. Temperature (°C) 1600 1500 1400 1300 1200 1100 1000 0 1085°C (Cu) 20 Liquid Liquidus line L B 40 a+L a A 60 Composition (wt% Ni) (a) 1455°C Solidus line 80 2800 2600 2400 2200 2000 100 (Ni) Temperature (°F) Temperature (°C) 1300 1200 20 Liquid Tie line. a + Liquid a 1 KR I 1 1 B ↑ Co a + Liquid -S 30 CL Composition (wt% Ni) (b) 40 1 Ca a 50
Calculate the weight fraction for phases at point B? what are those phases? Is there any eutectic rection? How many phases are present in this diagram? Cu-Ni system T(°C) TA 1300 -L (liquid): A tie ļine liquidus L +a Тв EB solidus (solid) 1200 TD ID 20 3032 35: 4043 50 Ca wt% Ni
1000 grams of steel containing 1.5 weight percent carbon is heated to complete melting. After equilibrium is achieved, we slowly cool the alloy. At 720C we keep the alloy to maintain equilibrium. Determine the amounts of the following, in grams. Pearlite Proeutectoid phase Total cementite
2) Answer the following questions according to the given Ag-Cu system. 1200 Liquid 1000 - 800- (Ag) (Cu) 2 600- 400- 200- 10 20 30 40 50 60 70 80 90 100 Ag Mass % Cu Cu e) For the 95Cu-5Ag alloy, determine the amount and the composition of the each phases and draw the microstructures schematically for the 1010°C, 850°C ve 25°C. f) For the Ag-20% Cu and Ag-80% Cu alloy; from 1100°C to room temperature, (a) For equilibrium solidification, (b) For nonequilibrium solidification (very rapid cooling) Show the change in the microstructures schematically for the given temperatures; i) 1100°C ii) Liquidus temperature iii) 20°C below of eutectic temperature iv) Room temperature
For a 20 wt% Pb-80 wt% Sn alloy Find: a) below eutectic temperature. b) eutectic temperature). the weight fraction of proeutectic phase and eutectic solid at the temperature slightly the weight fraction of alpha and beta phase at the same temperature (slightly below Composition (at% Sn) 20 40 60 80 100 327°C 600 300 Liquid 500 232°C 200 400 183°C 18.3 61.9 97.8 300 100 200 100 20 40 60 80 100 (Pb) Composition (wt% Sn) (Sn) Temperature ("C) Temperature ("F)
Given the Cu-Zn phase diagram below, determine the amount of the phase/s present of a 75 wt% Zn -25 wt% Cu alloy for the following temperatures. Indicate the required composition for each temperature in the diagram. Round off your final answers up to two decimal places. Show your solutions completely and neatly and follow the table format below, Temperature Phase/s present Phase composition Relative amount 600 °C 570 °C y+ L 700 1200 8+L L 600 P 598°C 560°C 570 |1000 e + L y +e 500 60 68.6 70 74.3 75 78.2 80 90 Composition (wt % Zn) Temperature (°C) ta Temperature (°F)
Figure 1 show Eutectoid Plain Carbon Steel Phase Diagram. Please indicate the phases present and their corresponding weight fraction at points a, b, c and d. Show your tie-line and calculations based on Lever Rules. Temperature (°C) 1100 900 700 500 300 100 0 100% Fe 7 0.02 1.0 Fe,C 1.2 2.0 7 7 7 7 Fe, C Figure 1 Fe,C Pearlite 4.0 3.0 Weight percent carbon 7+ Fe, C 727°C a + Fe₂C 5.0 Fe, C 6.0 6.7
help pls A two-phase phase diagram is shown. Answer the following questions t -1300 1500+ Temperature 1100 0 34 54! 166 482 80 Composition of Ni % 20 What is the composition (in % Cu) of the solid phase corresponding to the red dot in between the solidus and liquidus lines in the phase diagram? Just write the number. Do not write the % symbol. Question 17 2.33 100 An alloy is being made with 66% Ni and 34% Cu. When it is cooled from 1500°C to the temperature corresponding to the red dot in the phase diagram, how many kg of liquid is present in the mixture?
Consider 1 kg of tin-bismuth alloy (Sn-Bi) containing 40 wt% Bi. The phase diagram of the alloy is shown in the figure below. The alloy is cooled to 138 "C (just below the eutectic temperature). How many kilograms of phase B form? 300 271°C 232°C 200 Bi + L В +L 139 C 21 100 Bi - В + Bi 13°C vate Windows 100gs to activate Windows (Bi) 20 40 60 80 (Sn) 6:37 PM A 4) ENG 57 B. Temperature (°C)