Three steel bars with a diameter of 25 mm and carbon contents of 0.2, 0.5, and 0.8%, respectively. The specimens were subjected to tension until rupture. The load versus deformation results were as shown in Table below If the gauge length is 50 mm, determine the following: a. The tensile stresses and strains for each specimen at each load increase. b. Plot stresses versus strains for all specimens on one graph. c. The modulus of elasticity for each specimen. d. ultimate strength for each specimen. e. The strain at rupture for each specimen. f. the percentage of the total elongation. 3. Specimen No. Carbon Content (%) Deformation (mm) 2 0.2 0.5 0.8 Load (kN) 0.00 0. 0. 0. 0.07 133 133 133 0.10 137 191 191 0.15 142 196 285 0.50 147 201 324 1.00 140 199 383 2.50 155 236 447 196 295 491 (Rupture) 5.00 7.50 226 336 10.00 241 341 12.50 218 304 (Rupture) 13.75 196 (Rupture)

Three steel bars with a diameter of 25 mm and carbon contents of 0.2, 0.5, and 0.8%, respectively. The specimens were subjected to tension until rupture. The load versus deformation results were as shown in Table below If the gauge length is 50 mm, determine the following: a. The tensile stresses and strains for each specimen at each load increase. b. Plot stresses versus strains for all specimens on one graph. c. The modulus of elasticity for each specimen. d. ultimate strength for each specimen. e. The strain at rupture for each specimen. f. the percentage of the total elongation. 3. Specimen No. Carbon Content (%) Deformation (mm) 2 0.2 0.5 0.8 Load (kN) 0.00 0. 0. 0. 0.07 133 133 133 0.10 137 191 191 0.15 142 196 285 0.50 147 201 324 1.00 140 199 383 2.50 155 236 447 196 295 491 (Rupture) 5.00 7.50 226 336 10.00 241 341 12.50 218 304 (Rupture) 13.75 196 (Rupture)

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.6P: The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular...

See similar textbooks

Similar questions

The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.
HW:No.2 (The deadline for submitting your homework on Sandety (404.2014). Three steel bars with a diameter of 25 mm and carbon contents of 0.2, 0.5, and 0.8%, respectively. The specimens were subjected to tension until rupture. The load versus deformation results were as shown in Table below If the gauge length is 50 mm, determine the following: a. The tensile stresses and strains for each specimen at each load increase. b. Plot stresses versus strains for all specimens on one graph. c. The modulus of elasticity for each specimen. d. ultimate strength for each specimen. e. The strain at rupture for each specimen. f. the percentage of the total elongation. 3. Specimen No. Carbon Content (%) 1. 2 0.2 0.5 0.8 Deformation (mm) Load (kN) 0.00 0. 0.07 133 133 133 0.10 137 191 191 0.15 • 142 196 285 0.50 147 201 324 1.00 140 199 383 2.50 155 236 447 5.00 196 295 491 (Rupture) 7.50 226 336 10.00 241 341 12.50 218 304 (Rupture) 13.75 196 (Rupture)
Three steel bars have a diameter of 25 mm and carbon contents of 0.2, 0.5, and 0.8%, respectively. The specimens were subjected to tension until rup- ture. The load versus deformation results were as shown in Table P3.19. If the gauge length is 50 mm, determine the following: a. The tensile stresses and strains for each specimen at each load increment. b. Plot stresses versus strains for all specimens on one graph. TABLE P3.19 Specimen No. Carbon Content (%) Deformation (mm) 1 2 3 0.2 0.5 0.8 Load (kN) 0.00 0.07 133 133 133 0.10 137 191 191 0.15 142 196 285 0.50 147 201 324 1.00 140 199 383 2,50 155 236 447 5.00 196 295 491 (Rupture) 7.50 226 336 10.00 241 341 12.50 218 304 (Rupture) 13.75 196 (Rupture) c. The proportional limit for each specimen. d. The 0.2% offset yield strength for each specimen. e. The modulus of elasticity for each specimen. f. The strain at rupture for each specimen. g. Comment on the effect of increasing the carbon content on the following: i. Yield strength ii.…
A grade 36 round steel bar with a diameter of 0.5 inches and a gauge length of 2 inches wassubjected to tension to rupture following ASTM E-8 test procedure. The load and deformation data wereas shown in the following table: Using a spreadsheet program obtain the following:a. A plot of the stress-strain relationship. Label the axes and show units.b. A plot of the linear portion of the stress-strain relationship. Determine modulus of elasticity usingthe best fit approach.c. Proportional limit.d. Yield stress.e. Ultimate strength.f. When the applied load was 4.07 kips, the diameter was measured as 0.499905 inches. DeterminePoisson’s ratio.g. After the rod was broken, the two parts were put back together and the diameter of at the neckwas measured as 0.416012 inches. What is the true stress value at fracture? Is the true stress atfracture larger or smaller than the engineering stress at fracture? Why?h. Do you expect the true strain at fracture to be larger or smaller than the…
hree steel bars with a diameter of 25 mm and carbon contents of 0.2, 0.5, and 0.8%, respectively. The specimens were subjected to tension until rupture. The load versus deformation results were as shown in Table P3.19. If the gauge length is 50 mm, determine the following: The tensile stresses and strains for each specimen at each load increment. Plot stresses versus strains for all specimens on one graph. The proportional limit for each specimen. The 0.2% offset yield strength for each specimen. The modulus of elasticity for each specimen. The strain at rupture for each specimen. Comment on the effect of increasing the carbon content on the following: Yield strength ii. Modulus of elasticity iii. Ductility
A 32-mm rebar with a gauge length of 200 mm was subjected to tension to fracture according to ASTM E-8 method. The load and deformation data were as shown in Table P3.33. Using a spreadsheet program obtain the following: a. A plot of the stress-strain relationship. Label the axes and show units. b. A plot of the linear portion of the stress-strain relationship. Determine modulus of elasticity using the best-fit approach. c. Proportional limit. d. Yield stress. e. Ultimate strength. f. If the rebar is loaded to 390 kN only and then unloaded, what is the permanent change in length? TABLE P3.3 3 Load (kN) Displacement (mm) Load (kN) Displacement (mm) 472.9 8.4 62.2 0.1 487.1 9.7 188.9 0.2 496.4 11.1 329.8 0.4 505.7 12.4 383.4 1.7 512.8 13.7 426.0 4.0 522.6 15.3 447.3 5.9 532.4 18.5 462.5 7.2 525.9 22.4
Three steel bars have a diameter of 25 mm and carbon contents of 0.2, 0.5, and 0.8%, respectively. The specimens were subjected to tension until rupture. The load versus deformation results were as shown in Table P3.19. If the gauge length is 50 mm, determine the following: a. The tensile stresses and strains for each specimen at each load increment. b. Plot stresses versus strains for all specimens on one graph. TABLE P3.19 Specimen No. Carbon Content (%) 1 3 0.2 0.5 0.8 Deformation (mm) Load (kN) 0.00 0.07 133 133 133 0.10 137 191 191 0.15 142 196 285 0.50 147 201 324 1.00 140 199 383 2.50 155 236 447 5.00 196 295 491 (Rupture) 7.50 226 336 10.00 241 341 12.50 218 304 (Rupture) 13.75 196 (Rupture) c. The proportional limit for each specimen. d. The 0.2% offset yield strength for each specimen. e. The modulus of elasticity for each specimen. f. The strain at rupture for each specimen. g. Comment on the effect of increasing the carbon content on the following: Yield strength ii.…
A 32-mm rebar with a gauge length of 200 mm was subjected to tension to fracture according to ASTM E-8 method. The load and deformation data were as shown in TableUsing a spreadsheet program obtain the following:a. A plot of the stress–strain relationship. Label the axes and show units.b. A plot of the linear portion of the stress–strain relationship. Determine modulus of elasticity using the best-fit approach.c. Proportional limit.d. Yield stress.e. Ultimate strength.f. If the rebar is loaded to 390 kN only and then unloaded, what is the permanent change in length?
Calculate the steel ratio that will produce a tension-controlled failure if compressivestrength f’c = 28 MPa and steel yield strength fy the answer is 0.02167 but i don't know how to solve it please help
A No. 10 steel rebar is tested in tension. By monitoring the load reading of the testing machine, it was found that the specimen yielded at a load of 41,600 lb and fractured at 48,300 lb.a. Determine the tensile stresses at yield and at fracture.b. Estimate how much increase in length would occur at 70% of the yield stress in a 2-in. gauge length.
A rectangular steel bar 0.5 inch thickness by 1.5 inches width and 220 ft long is subjectedto a 6000 lbs tensile load acting along its width. Find the deformation along its length andthickness if poison’s ratio is 0.27.