F THINNTVERSITY195ProblemAtomic percent silver30If 500 g of a 40 wt % Ag-60 wt %°F°C110010204050607080 90Cu alloy is slowly cooled from1084.5°19001000°C to just below 780°C1000L.961.931700(a) How many grams of liquid and90053L+a1600proeutectic a are present at 850°C?800 F aL+BB1400(b) How many grams of liquid and780°7.971.991.2700-proeutectic a are present at 780°C + AT ?1200600a + B(c) How many grams of a are present in1000the eutectic structure at 780°C - AT ?500850400Cu(d) How many grams of B are present in102030405060708090AgWeight percent silverthe eutectic structure at 780°C - AT ?

Given information, Cu-Ag phase diagram, Find (a) How many grams of liquid and proeutectic a are…

If 500 g of a 40 wt % Ag-60 wt % Atomic percent silver 40 °C °F 10 20 30 50 60 70 80 90 Cu alloy is slowly cooled from 1100 1084.5 1900 1000°C to just below 780°C 1000- L. 961.93 (a) How many grams of liquid and 1700 900- 8 53 L+a 1600 proeutectic a are present at 850°C? 800 F a L+B/ B 1400 780° (b) How many grams of liquid and 7.9 71.9 91.2 700- proeutectic a are present at 780°C + AT ? 1200 600 a + B (c) How many grams of a are present in 1000 500 the eutectic structure at 780°C - AT ? 850 400 Cu (d) How many grams of ß are present in 10 20 30 40 50 60 70 80 90 Ag Weight percent silver the eutectic structure at 780°C - AT ?

If 500 g of a 40 wt % Ag-60 wt % Atomic percent silver 40 °C °F 10 20 30 50 60 70 80 90 Cu alloy is slowly cooled from 1100 1084.5 1900 1000°C to just below 780°C 1000- L. 961.93 (a) How many grams of liquid and 1700 900- 8 53 L+a 1600 proeutectic a are present at 850°C? 800 F a L+B/ B 1400 780° (b) How many grams of liquid and 7.9 71.9 91.2 700- proeutectic a are present at 780°C + AT ? 1200 600 a + B (c) How many grams of a are present in 1000 500 the eutectic structure at 780°C - AT ? 850 400 Cu (d) How many grams of ß are present in 10 20 30 40 50 60 70 80 90 Ag Weight percent silver the eutectic structure at 780°C - AT ?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

An Ag-Cu alloy contains 25% a and 75% B at 600°C. The composition of the overall alloy is approximately 1000 L+B 800 8-87 28-12 922 a + B 500 972 400 Ag 10 20 30 40 50 60 70 80 90 Cu %Cu (by weight) A. 80.2% Cu B. 73.5% Cu C. 65.8% Cu D. 89.6% Cu
iii) For a 68 wt% Zn-32 wt% Cu alloy, make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: 1000°C, 760°C, 600°C and 400°C. Label all phases and indicate their approximate compositions. Comportion a In 20 40 60 100 1200 |2200 H2000 Liquid 1000 - 1800 デ+ダ H1600 J400 E 1200 600 400 『+キ 600 200 400 40 60 Conpositon tet% Zro
2) Answer the following questions according to the given Ag-Cu system. 1200 Liquid 1000 - 800- (Ag) (Cu) 2 600- 400- 200- 10 20 30 40 50 60 70 80 90 100 Ag Mass % Cu Cu e) For the 95Cu-5Ag alloy, determine the amount and the composition of the each phases and draw the microstructures schematically for the 1010°C, 850°C ve 25°C. f) For the Ag-20% Cu and Ag-80% Cu alloy; from 1100°C to room temperature, (a) For equilibrium solidification, (b) For nonequilibrium solidification (very rapid cooling) Show the change in the microstructures schematically for the given temperatures; i) 1100°C ii) Liquidus temperature iii) 20°C below of eutectic temperature iv) Room temperature
2. Determine the amount of liquid phase in the a Cu-50% Ni alloy at 1300°C, % L 1500 1400 L. C +L 58 1300 1200 1100 1000 Cu 20 40 60 80 Ni Weight percent nickel Temperature (°C)
QI/ Draw a thermal equilibrium diagram for the binary alloy system (Si –Au), from the following data:- a- Si melts at 1414 °C, and Au melts at 1064 °C , and identify all phases are present in the diagram. b- Eutectic is formed at 360°C containing 20 Wt% Si -80 Wt% Au . c- Determine the amount of each phase for the alloy which consist 60 Wt% Si- 40Wt % Au at 1200 °C and 800 °C ,then determine the amount of eutectic at 200 °C?
Is it possible to have a copper-nickel alloy that, at equilibrium, consists of a liquid phase of composition 20 wt% Ni-80 wt% Cu and also an a phase of composition 37 wt% Ni-63 wt% Cu? If so, what will be the approximate temperature of the alloy? If this is not possible, explain why. Temperature (°C) 1600 1500 1400 1300 1200 1100 1000 0 1085°C (Cu) 20 Liquid Liquidus line L B 40 a+L a A 60 Composition (wt% Ni) (a) 1455°C Solidus line 80 2800 2600 2400 2200 2000 100 (Ni) Temperature (°F) Temperature (°C) 1300 1200 20 Liquid Tie line. a + Liquid a 1 KR I 1 1 B ↑ Co a + Liquid -S 30 CL Composition (wt% Ni) (b) 40 1 Ca a 50
Consider Al- Cu system below. When Al-40%Cu is heated above 600°C and cooled slowly to a temperature of 545°C . Answer the following. Use the values of composition given in the phase diagram , no estimation .Each has two marks. 700 1200 600 L a + L 6 +L 548 1000 500 (CUAL) a + 6 800 400 600 300 5.65 10 20 30 32.7 40 50 52.5 (AI) Composition (wt % Cu) a. Percentage of the pro-eutectic phase present (% no decimal places) b. Composition of the pro- eutectic phase present (in %Cu one decimal place) c. What is the percentage of larger eutectic component present (% no decimal places) Temperature (°C) Temperature (°F)
7. Consider 1.5 kg of a 99.6 wt% Fe-0.4 wt% C steel that is cooled to a temperature just below the eutectoid. (a) How many kilograms of ferrite (a) form? (b) How many kilograms of cementite (Fe;C) form? Include your tie line in the solution. 1600| L 1400 T(°C) 1200 (austenite) y+L 1148°C L+Fe;C 1000 Y + Fe;C 800 727°C 600 a + Fe;C 400 1 2 4 6 6.7 C, wt% C Fe;C (cementite)
Q2: Consider a Cu-80wt% Ni-20% alloy, determine the following: (a) The liquidus and solidus temperature of alloy. (b) The composition of last liquid to solidify. (c) The composition of last solid to melt. (d) The composition of the solid and liquid phases at 1175 °C. (Draw the microstructure at this points) (e) The amount of the solid and liquid phases at 1175 °C. Composition at No 1600 2800 1500 2600 1400 2400 1300 1200 2200 1100 2000 1000 0 1085 C 20 Liquid Liquidus line 40 60 Composition (wt% NO 1453 C Solidus line 80 100
Consider 1 kg of tin-bismuth alloy (Sn-Bi) containing 40 wt% Bi. The phase diagram of the alloy is shown in the figure below. The alloy is cooled to 138 "C (just below the eutectic temperature). How many kilograms of phase B form? 300 271°C 232°C 200 Bi + L В +L 139 C 21 100 Bi - В + Bi 13°C vate Windows 100gs to activate Windows (Bi) 20 40 60 80 (Sn) 6:37 PM A 4) ENG 57 B. Temperature (°C)
Q2: Consider a Cu-80wt% Ni-20% alloy, determine the following: (a) The liquidus and solidus temperature of alloy. (b) The composition of last liquid to solidify. (c) The composition of last solid to melt. (d) The composition of the solid and liquid phases at 1175 °C. (Draw the microstructure at this points) (e) The amount of the solid and liquid phases at 1175 °C. Composition (at% Ni) 0 20 40 60 80 100 1600 T 1500 1400 1300 1200 1100 1000 1085°C 0 (Cu) 20 T Liquid Liquidus line +L 40 60 Composition (wt% Ni) T 1453 C Solidus line 80 رقم الصفحة 1/1 2800 2600 -2400 2200 2000 100 (Ni) Temperature (F)
1000 grams of steel containing 1.5 weight percent carbon is heated to complete melting. After equilibrium is achieved, we slowly cool the alloy. At 720C we keep the alloy to maintain equilibrium. Determine the amounts of the following, in grams. Pearlite Proeutectoid phase Total cementite