Question
Chapter 2, Problem 20SP
To determine
To discuss : The method of isostatic pressing for making machine parts by powder metallurgy.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
لانقطة واحدة
of Warm working
The advantages
over cold working are: 1) forces and
power are higher,2) more intricate
work geometries possible, and 3)
need for annealing may be reduced
.or eliminated
T
F
Blow molding is an important
industrial process for making one-
piece hollow plastic parts with thick
.walls
T
Sly The sequence of the Blow Molding
is automated and often integrated
with downstream operations such
.as bottle filling and labeling
T
لنقطة واحدة
4. A steel rotor of a gas turbine of 400mm outside diameter, 150mm inside diameter and 25mm
thick is shrunk onto a solid steel shaft. At its service speed of 3000rev/min the radial stress on
the outside of the rotor is 1.45MPA. Determine the shrinkage allowance required in order to
avoid failure, if the design stress limit of the material is 200MPA.
For the material assume a Young's Modulus, Poisson Ratio and density of 210GPA, 0.3 and
7850k g/m3
respectively.
Provide information about tempering heat treatment temperature stages, microstructures formed and their effects on mechanical properties.
Chapter 2 Solutions
Machine Elements in Mechanical Design (6th Edition) (What's New in Trades & Technology)
Ch. 2 - Define ultimate tensile strength.Ch. 2 - Define yield point.Ch. 2 - Define yield strength and tell how it is measured.Ch. 2 - What types of materials would have a yield point?Ch. 2 - What is the difference between proportional limit...Ch. 2 - Define Hooke’s law.Ch. 2 - What property of a material is a measure of its...Ch. 2 - What property of a material is a measure of its...Ch. 2 - If a material is reported to have a percent...Ch. 2 - Define Poisson’s ratio.
Ch. 2 - If a material has a tensile modulus of elasticity...Ch. 2 - A material is reported to have a Brinell hardness...Ch. 2 - A steel is reported to have a Brinell hardness of...Ch. 2 - For Problems 14 17, describe what is wrong with...Ch. 2 - For Problems 14 17, describe what is wrong with...Ch. 2 - For Problems 14 17, describe what is wrong with...Ch. 2 - For Problems 14 17, describe what is wrong with...Ch. 2 - Name two tests used to measure impact energy.Ch. 2 - Prob. 19PCh. 2 - Prob. 20PCh. 2 - Prob. 21PCh. 2 - What is the typical carbon content of a low-carbon...Ch. 2 - How much carbon does a bearing steel typically...Ch. 2 - What is the main difference between SAE 1213 steel...Ch. 2 - Name four materials that are commonly used for...Ch. 2 - Name four materials that are typically used for...Ch. 2 - Describe the properties desirable for the auger...Ch. 2 - Prob. 28PCh. 2 - Appendix 3If a shovel blade is made from SAE 1040...Ch. 2 - Describe the differences between through-hardening...Ch. 2 - Describe the process of induction hardening.Ch. 2 - Prob. 32PCh. 2 - Prob. 33PCh. 2 - Prob. 34PCh. 2 - Prob. 35PCh. 2 - Prob. 36PCh. 2 - Name three types of cast iron.Ch. 2 - Prob. 38PCh. 2 - Describe the process of making parts from powdered...Ch. 2 - Prob. 40PCh. 2 - Prob. 41PCh. 2 - Prob. 42PCh. 2 - Prob. 43PCh. 2 - Prob. 44PCh. 2 - Prob. 45PCh. 2 - Prob. 46PCh. 2 - Name three typical uses for titanium alloys.Ch. 2 - Prob. 48PCh. 2 - Prob. 49PCh. 2 - Prob. 50PCh. 2 - Describe the difference between thermosetting...Ch. 2 - Suggest a suitable plastic material for each of...Ch. 2 - Name eight factors over which the designer has...Ch. 2 - Define the term composite.Ch. 2 - Prob. 55PCh. 2 - Name four types of reinforcement fibers used for...Ch. 2 - Prob. 57PCh. 2 - Prob. 58PCh. 2 - Prob. 59PCh. 2 - For what applications are sheet-molding compounds...Ch. 2 - Prob. 61PCh. 2 - Prob. 62PCh. 2 - Prob. 63PCh. 2 - Prob. 64PCh. 2 - Prob. 65PCh. 2 - Prob. 66PCh. 2 - Prob. 67PCh. 2 - Prob. 68PCh. 2 - Discuss the advantages of composite materials...Ch. 2 - Prob. 70PCh. 2 - Prob. 71PCh. 2 - Prob. 72PCh. 2 - Prob. 73PCh. 2 - Describe the general construction of a composite...Ch. 2 - Prob. 75PCh. 2 - Prob. 76PCh. 2 - Prob. 77PCh. 2 - Prob. 78PCh. 2 - Prob. 79PCh. 2 - Prob. 80PCh. 2 - Prob. 81PCh. 2 - Prob. 82PCh. 2 - Prob. 83PCh. 2 - Problems 8290. For composites made with the given...Ch. 2 - Prob. 85PCh. 2 - Prob. 86PCh. 2 - Prob. 87PCh. 2 - Prob. 88PCh. 2 - Prob. 89PCh. 2 - Prob. 90PCh. 2 - Prob. 91PCh. 2 - Prob. 92PCh. 2 - Prob. 93PCh. 2 - Problems 94 96. For the given specification for a...Ch. 2 - Prob. 95PCh. 2 - Prob. 96PCh. 2 - Prob. 97PCh. 2 - Prob. 98PCh. 2 - Prob. 99PCh. 2 - Describe how CNTs are used in a CMNC and what...Ch. 2 - Prob. 1SPCh. 2 - Prob. 2SPCh. 2 - Prob. 3SPCh. 2 - Prob. 4SPCh. 2 - Prob. 5SPCh. 2 - Prob. 6SPCh. 2 - Name three U.S. organizations whose names are...Ch. 2 - Prob. 8SPCh. 2 - A U.S. designer specifies SAE 4140 steel for a...Ch. 2 - Prob. 10SPCh. 2 - Prob. 11SPCh. 2 - Prob. 12SPCh. 2 - Prob. 13SPCh. 2 - Prob. 14SPCh. 2 - Prob. 15SPCh. 2 - Prob. 16SPCh. 2 - Prob. 17SPCh. 2 - Prob. 18SPCh. 2 - Prob. 19SPCh. 2 - Prob. 20SPCh. 2 - Prob. 21SPCh. 2 - Prob. 22SPCh. 2 - Prob. 23SPCh. 2 - Prob. 24SPCh. 2 - Prob. 25SPCh. 2 - Prob. 26SPCh. 2 - Prob. 27SPCh. 2 - Prob. 28SPCh. 2 - Prob. 29SPCh. 2 - Prob. 30SPCh. 2 - Prob. 31SPCh. 2 - Prob. 32SPCh. 2 - Prob. 33SPCh. 2 - Prob. 34SPCh. 2 - List the six general classifications of materials...Ch. 2 - Prob. 36SPCh. 2 - Prob. 37SPCh. 2 - Prob. 38SPCh. 2 - Prob. 39SPCh. 2 - Prob. 40SP
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Briefly cite the differences between the recovery and recrystallization processes.arrow_forwardDiscuss two property types to consider when selecting a material to process the followingproduct types. Industrial Robotic Manipulator Bicycle Framearrow_forwardDuring thermal tempering, a glass piece is heated to a temperature: A = %3D Above the glass transition temperature. ; B = Below the glass transition temperature. ; C = Above the softening point. ; D = Below the softening point. A & C B & D A & D B & Carrow_forward
- What is the advantage of nitriding? Select all correct answers. Some complex components can be nitride without difficulty. Better wear resistance. Better fatigue resistance. The cheapest method of case hardening. What is the correct definition of plastic deformation? The behavior of a material when its size changes by the addition of heat. The behavior of a material that deforms under load and returns to its original shape when the load is removed. Deformation caused by cleavage, where the material is actually pulled apart across atomic planes within the crystals or along the grain boundaries. The behavior of a material that deforms under load and does not fully return to its original shape when the load is removed.arrow_forwardComplete solution and illustration, thank youarrow_forwardWhat manufacturing processes would you use to make this? Make sure to focus onusing appropriate terminology and include the terms: blanking, punching, flange-rolling, & stamping to describe the process steps for how this stainless-steel colanderwas producedarrow_forward
- A bearing of simple geometry is to be pressed out of bronze powders, using a compacting pressure of 240 MPa. Outside diameter of the bearing 45mm, inside diameter 20 mm, and length 18 mm. What is the required press tonnage to perform this operation? Whole number answer.arrow_forwardDiscussion of the concept of metal springs referring to the factors considered in the design of metal springsarrow_forwardQ. Discuss the following sentences: 1- A wide particle size distribution is preferred for dry pressing. 2- Products with high dimension accuracy are obtained in hot pressed technique.arrow_forward
- Regarding annealing, choose the right answer (One or more): The actual annealing time must be long enough to allow for any necessary transformation reactions that may occur Annealing can be performed to release internal stresses of the material The main purpose of annealing is to decrease or restore material's ductility Time isn't a significant parameter in annealing process If the rate of temperature change is too great, temperature gradients and internal stresses may be induced that may lead to warping or even crackingarrow_forwardThe process of making/production of Ring (washer) from steel plate UTS= 400 MPa thick 3 mm with an inner diameter of 8 mm and an outer diameter of 20 mm which are carried out respectively by the piercing and blanking process. Calculate the blanking forcearrow_forwardAdvanced Physicswhat are the real life applications of cold working and annealing?arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Mechanical SPRING DESIGN Strategy and Restrictions in Under 15 Minutes!; Author: Less Boring Lectures;https://www.youtube.com/watch?v=dsWQrzfQt3s;License: Standard Youtube License