Textbook Question
Chapter 17, Problem 31QLP
What will be stronger: a blend of stainless steel and copper powder that is compacted and sintered, or a stainless steel powder that is compacted, sintered, and infiltrated by copper? Explain.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
For a powder binding process that mixes a 1:2 volume ratio mixture of semi-crystalline polyethylene powder with a density of 0.900 g/cm3 andcrystalline polyethylene powder, what is the percent crystallinity of the manufactured parts? (The density of polyethylene in its amorphous andcrystalline states is 0.870 g/cm3 and 0.998 g/cm3 respectively)(This question has only one correct answer)% Crystallinity = 55.45%% Crystallinity = 65.50%% Crystallinity = 76.99%% Crystallinity = 82.30%% Crystallinity = 57.25%
Your die setter brings you a print of a cylinder with a 2 inch outside diameter and a 1.75 inch inside
diameter. The cylinder is to be molded of iron powder with a green density of 6.8 g/cc. The apparent
density of the powder is 2.9 g/cc. What is the die fill if the green part is to have a height of 2.5 inches?
(show your work)
What is the maximum amount of Zinc Stearate (PL
=
1.09 g/cc) that can be added to an Iron powder (pp =
7.8 g/cc) if a green density of 7.0 g/cc is desired?
Provide your answer in wt%.
Chapter 17 Solutions
Manufacturing Engineering & Technology
Ch. 17 - Describe briefly the production steps involved in...Ch. 17 - Name the various methods of powder production and...Ch. 17 - Explain why metal powders may be blended.Ch. 17 - Describe the methods used in metal powder...Ch. 17 - What is isostatic pressing? How is it different...Ch. 17 - What hazards are involved in PM processing?...Ch. 17 - Describe what occurs to metal powders during...Ch. 17 - Prob. 8RQCh. 17 - Why might secondary and finishing operations be...Ch. 17 - Prob. 10RQ
Ch. 17 - Prob. 11RQCh. 17 - Prob. 12RQCh. 17 - Prob. 13RQCh. 17 - What is screening of metal powders? Why is it...Ch. 17 - Why are protective atmospheres necessary in...Ch. 17 - Why is there density variation in the compacting...Ch. 17 - What is the magnitude of the stresses and forces...Ch. 17 - List the similarities and differences of forging...Ch. 17 - Give some reasons that powder-injection molding is...Ch. 17 - How does the equipment used for powder compaction...Ch. 17 - Explain why the mechanical and physical properties...Ch. 17 - What are the effects of the different shapes and...Ch. 17 - Describe the relative advantages and limitations...Ch. 17 - How different, if any, are the requirements for...Ch. 17 - The powder metallurgy process can be competitive...Ch. 17 - What are the reasons for the shapes of the shown...Ch. 17 - Should green compacts be brought up to the...Ch. 17 - Because they undergo special processing, metal...Ch. 17 - In Fig. 17.12, it can be seen that the pressure is...Ch. 17 - Why do the compacting pressure and the sintering...Ch. 17 - What will be stronger: a blend of stainless steel...Ch. 17 - Name the various methods of powder production and...Ch. 17 - Estimate the maximum tonnage required to compact a...Ch. 17 - Refer to Fig. 17.11a. What should be the volume of...Ch. 17 - Determine the shape factors for (a) a cylinder...Ch. 17 - Estimate the number of particles in a 500-g sample...Ch. 17 - Prob. 37QTPCh. 17 - A coarse copper powder is compacted in a...Ch. 17 - A gear is to be manufactured from iron powders. It...Ch. 17 - What volume of powder is needed to make the gear...Ch. 17 - The axisymmetric part shown in Fig. P17.41 is to...Ch. 17 - Prepare an illustration similar to Fig. 13.1,...Ch. 17 - Prob. 44SDPCh. 17 - Compare the design considerations for PM products...Ch. 17 - Prob. 46SDPCh. 17 - Prob. 47SDPCh. 17 - Using the Internet, locate suppliers of metal...Ch. 17 - Explain why powder metal parts are commonly used...Ch. 17 - Prob. 50SDPCh. 17 - Describe how the information given in Fig. 17.15...Ch. 17 - It was stated that, in the process shown in Fig....Ch. 17 - Prob. 53SDPCh. 17 - The axisymmetric parts shown in Fig. P17.54 are to...Ch. 17 - Assume you are working in technical sales. What...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- For a powder binding process that mixes a 1:2 volume ratio mixture of semi-crystalline polyethylene powder with a density of 0.900 g/cm³ and crystalline polyethylene powder, what is the percent crystallinity of the manufactured parts? (The density of polyethylene in its amorphous and crystalline states is 0.870 g/cm³ and 0.998 g/cm³ respectively) (This question has only one correct answer) О а. % Crystallinity = 55.45% O . % Crystallinity = 57.25% О с. % Crystallinity = 76.99% Od. % Crystallinity = 82.30% % Crystallinity = 65.50%arrow_forwardFor a powder binding process that mixes a 1:2 volume ratio mixture of semi-crystalline polyethylene powder with a density of 0.900 g/cm³ and crystalline polyethylene powder, what is the percent crystallinity of the manufactured parts? (The density of polyethylene in its amorphous and crystalline states is 0.870 g/cm3 and 0.998 g/cm3 respectively) (This question has only one correct answer) O a. % Crystallinity = 65.50% O b. % Crystallinity = 57.25% С. % Crystallinity = 82.30% O d. % Crystallinity = 76.99% е. % Crystallinity = 55.45%arrow_forwardGranule strength is very important in pressing powders. The force applied to a granule with a radius of 1 mm is 0.5 Newton. Calculate the breaking strength of the granule. b) It is observed that the pressed granules break easily during pressing. Write down the reasons of this situation and what would you take precations to solve this problem? Why? (please write down 3 precautions with reasons). odluckarrow_forward
- For a powder binding process that mixes a 3:1 volume ratio mixture of semi-crystalline polyethylene powder with a density of 0.900 g/cm³ and crystalline polyethylene powder, what is the percent crystallinity of the manufactured parts? (The density of polyethylene in its amorphous and crystalline states is 0.870 g/cm³ and 0.998 g/cm³ respectively)arrow_forwardA Silicon Carbide powder has an internal energy of 3 X 108 J/m³, a surface tension of 1.2 J/m², and a total energy of 2.6 X 10-¹5 J. What is the smallest diameter that this powder may be ground without agglomerating? (show your work)arrow_forward3) Should green compacts be brought up to the sintering temperature slowly or rapidly? Explain your reasoning.4) Name the various methods of powder production and the morphology of the powders produced.5) What are some P/M (powder metallurgy) products that have been intentionally designed to use the porosity or permeability features of the process?arrow_forward
- Discuss the effect of monomodal and bimodal particle size distribution of powderson the microstructure and properties of advanced ceramics. Which starting powders would youprefer and WHY?arrow_forwardFor a powder binding process that mixes a 3:1 volume ratio mixture of semi-crystalline polyethylene powder with a density of 0.900 g/cm³ and crystalline polyethylene powder, what is the percent crystallinity of the manufactured parts? (The density of polyethylene in its amorphous and crystalline states is 0.870 g/cm³ and 0.998 g/cm³ respectively) % Crystallinity = 45.96% O b. % Crystallinity = 35.50% % Crystallinity = 61.20% O d. % Crystallinity = 55.25% O e. % Crystallinity = 53.35% a. C.arrow_forwardGKN Sinter Metals Company pressed iron powders using a compaction pressure of 600 MPa to produced a cylindrical bearing which is 70 cm long and has internal and external diameters of 8 cm and 16 cm, respectively. Determine (a) the most appropriate pressing direction, (b) the required press tonnage to perform this operation, and (c) the final weight of the part if the porosity is 12%, given that the density of iron, ρ = 7.87 g/cm3. Assume shrinkage during sintering can be neglectedarrow_forward
- In solid state sintering of compacted metal powder material, discuss how the progress of microstructure changes in sintering can be observed by microscopy. Support your discussion with suitable schematic diagram.arrow_forwardIn powder processing, a cylinder with a diameter of 2 inches and a height of 10 inches is to be made from fine copper powders. A single-action press is used for compaction. If the average density of the green product is 7 g/cm3 at the bottom half of the cylinder, estimate the compaction pressure at the punch surface. Assume no friction between the powders. The coefficient of friction between particles and containers is 0.2.arrow_forwardFor a powder binding process that mixes a 3:1 volume ratio mixture of semi-crystalline polyethylene powder with a density of 0.900 g/cm³ and crystalline polyethylene powder, what is the percent crystallinity of the manufactured parts? (The density of polyethylene in its amorphous and crystalline states is 0.870 g/cm³ and 0.998 g/cm³ respectively) O a. % Crystallinity = 45.96% O b. % Crystallinity=55.25% O c. % Crystallinity = 53.35% O d. % Crystallinity = 61.20% Oe. % Crystallinity = 35.50%arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Intro to Ceramics and Glasses — Lesson 2, Part 1; Author: Ansys Learning;https://www.youtube.com/watch?v=ArDFnBWH-8w;License: Standard Youtube License