Textbook Question
Chapter 17, Problem 27RQ
Why are friction effects in metalworking difficult to scale�down for laboratory testing, or scale�up from laboratory conditions to production conditions?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
I need the answer as soon as possible
Please solve no 4 (engineering tribology)
What are assessments that measure strength, speed,
agility, or high-speed strength? What are the
protocols and norms for each?
Chapter 17 Solutions
Degarmo's Materials And Processes In Manufacturing
Ch. 17 - What is plasticity?Ch. 17 - What are some of the general assets of the...Ch. 17 - Why might large production quantities be necessary...Ch. 17 - What types of deformation may occur in forming...Ch. 17 - What is an independent variable in a...Ch. 17 - What are some considerations regarding selection...Ch. 17 - What is the significance of tool and die geometry...Ch. 17 - Why is lubrication often a major concern in metal...Ch. 17 - What are some of the secondary effects that may...Ch. 17 - Prob. 10RQ
Ch. 17 - Why is it important to be able to predict the...Ch. 17 - Prob. 12RQCh. 17 - Prob. 13RQCh. 17 - Prob. 14RQCh. 17 - Prob. 15RQCh. 17 - Prob. 16RQCh. 17 - Prob. 17RQCh. 17 - What are some of the features that may be...Ch. 17 - What features have contributed to the expanded use...Ch. 17 - What are some of the uses or applications of...Ch. 17 - Prob. 21RQCh. 17 - Prob. 22RQCh. 17 - Prob. 23RQCh. 17 - What type of information about the material being...Ch. 17 - Prob. 25RQCh. 17 - Why is friction such an important parameter in...Ch. 17 - Why are friction effects in metalworking difficult...Ch. 17 - Prob. 28RQCh. 17 - Prob. 29RQCh. 17 - Prob. 30RQCh. 17 - Prob. 31RQCh. 17 - Discuss the significance of wear in metal forming:...Ch. 17 - Lubricants are often selected for properties in...Ch. 17 - What is tribology?Ch. 17 - What are some of the common types of metal forming...Ch. 17 - What is hydrodynamic lubrication? What are some of...Ch. 17 - If the temperature of a material is increased,...Ch. 17 - Define the various regimes of cold working, warm...Ch. 17 - What is an acceptable definition of hot working?...Ch. 17 - What are some of the attractive manufacturing and...Ch. 17 - What are some of the negative aspects of hot...Ch. 17 - Prob. 42RQCh. 17 - Prob. 43RQCh. 17 - If the deformed grains recrystallize during hot...Ch. 17 - Why might a rolled thread offer improved strength...Ch. 17 - How might the temperature of a deforming workpiece...Ch. 17 - Why are heated dies or tools often employed in...Ch. 17 - What generally restricts the upper temperature to...Ch. 17 - What is the primary cause of residual stresses in...Ch. 17 - What is cold working?Ch. 17 - Compared to hot working, what are some of the...Ch. 17 - What are some of the disadvantages of...Ch. 17 - How could cold working be used to reduce the cost...Ch. 17 - Why are cold�forming processes best suited for...Ch. 17 - How can the tensile test properties of a metal be...Ch. 17 - Why is elastic springback an important...Ch. 17 - What is pickling, and how does it remove surface...Ch. 17 - Prob. 58RQCh. 17 - What engineering properties are likely to decline...Ch. 17 - Prob. 60RQCh. 17 - Prob. 61RQCh. 17 - Prob. 62RQCh. 17 - What are some of the advantages of warm forming...Ch. 17 - Prob. 64RQCh. 17 - What material feature is considered to be the...Ch. 17 - Why is isothermal forming considerably more...Ch. 17 - Prob. 67RQCh. 17 - Prob. 1PCh. 17 - Prob. 2PCh. 17 - List and discuss the various economic factors that...Ch. 17 - Prob. 4PCh. 17 - Prob. 5PCh. 17 - Prob. 6PCh. 17 - Prob. 1.1CSCh. 17 - Prob. 1.2CSCh. 17 - Which stainless steel would you recommend? Begin...Ch. 17 - Prob. 1.4CSCh. 17 - Prob. 1.5CSCh. 17 - After drawing and perforating, the residual...Ch. 17 - One of the blades has struck a rock and is badly...Ch. 17 - A second propeller, identical to the one above,...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Estimate the force required for punching a 25mm diameter hole through a 3.2mm thick annealed titanium alloy Ti-6Al-4V sheet at room temperature. POCO SHOT ON POCO F2 PRO Data: UTS = 1000MPA.arrow_forwardThe average number of articles produced by two machines per day are 200 and 250 with S.D 20 and 25 respectively on the basis of records of 25 days production.Can you regard both the machines equally efficient at 1% level of significant?arrow_forwardComplete the following table comparing cold, warm and hot work: Note: Preferably, if possible, the answer should be digital, not on a physical sheet. :3arrow_forward
- Hi, could you show workings out if possible please, thanks youarrow_forwardA process engineer is trying to improve the life of a cutting tool. He has run a 23 experiment using (1) cutting speed, (2) metal hardness, (3) and cutting angle as the factors. The data from the 2 replicates are shown below. (a) Do any of the 3 factors affect tool life? (b)what combination of the factor levels produces the longest tool life? (c) Is there a combination of cutting speed and cutting angle that always gives good results regardless of metal hardness? Replicate Run I II (1) 221 311 a 325 435 b 354 348 ab 552 472 c 440 453 ac 406 377 bc 605 500 abc 392 419arrow_forward(a) Figure 1 shows surface roughness and tolerances obtained in Chemical Machining (CM) and Electrochemical Machining (ECM) process for different types of electronic products. Comment on the differences between chemical and electrochemical machining process in terms of surface roughness and tolerance of the machined product as illustrated in Figure 1. 0.9 CM 0.8 0.7 Z ECM 0.6 0.5 0.4 0.3 0.2 0.1 Product A Product B Product C Product D Products 25 E ČM 20 Z ECM 15 10 Product A Product B Product C Product D Products Figure 1: Surface roughness and tolerances of various electronic products Surface roughness, Ra Tolerance, (t mm x 10)arrow_forward
- Q1) The redesigned brake caliper is manufactured using SLM from Titanium Ti6Al-4V alloy powder. How many SLM machines are required to manufacture parts for 450 vehicleswhich are to be built in a 20-month production period. The following parameters are in effect:• A single caliper is built at a time• The caliper has a height of 173mm.• Each layer is 32 µm thick• Only one laser is used• The average laser scanning time for each layer with a single laser is 63 seconds• The powder recoating time for every odd numbered layer is 12 seconds and 25 for every evennumbered layer• Every 8th layer is scanned twice, at 2.3 times the usual laser scan speed to provide additional heatinput for in-situ heat treatment• The SLM machine operates at a duty rate of 42% of the 24-hour day, Monday to Friday, for 48 weeksof the year, with 10% of production time lost to unscheduled downtime.arrow_forwardDear Tutor please help me pleasearrow_forwardManufacturing Processes Explain the causes of lay on surfaces.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
HOME SHOP JIGS & FIXTURES PART 1, TYPES OF JIGS & ACCESSORIES AND THE THEORIE BEHIND THE TOOLS; Author: THATLAZYMACHINIST;https://www.youtube.com/watch?v=EXYqi42JimI;License: Standard Youtube License