Textbook Question
Chapter 11, Problem 44QTP
Estimate the clamping force for a die-casting machine in which the casting is rectangular with projected dimensions of 100 mm × 150 mm (4 in. × 6 in.). Would your answer depend on whether it is a hot-chamber or cold-chamber process? Explain.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
For sand-casting a steel rectangular plate with dimensions 80mm×120mm×20mm, a cylindrical
riser has to be designed. The height of the riser is equal to its diameter. The total solidification
time for the casting is 2 minutes. In Chvorinov‟s law for the estimation of the total solidification
time, exponent is to be taken as 2. For a solidification time of 3 minutes in the riser, the diameter
(in mm) of the riser is ____
Describe the die casting process in detail. Use neat sketches for clarity. Differentiate clearly between hot-chamber die casting and cold-chamber die casting processes.
What is the difference between true centrifugal and semi-centrifugal casting? Describe the centrifugal casting process in detail. Use neat sketches to elaborate your description.
A mould having dimensions 100 mm x 90 mm x 20 mm is filled with molten metal through a gate with height h and CS area A, the mould filling time is t1. The height is now quadrupled and the crosssectional area is halved. The corresponding filling time is t2 .
What is the ratio t2/t1 ?
Chapter 11 Solutions
Manufacturing Engineering & Technology
Ch. 11 - Describe the differences between expendable and...Ch. 11 - Name the important factors in selecting sand for...Ch. 11 - What are the major types of sand molds? What are...Ch. 11 - List important considerations when selecting...Ch. 11 - What is the function of a core?Ch. 11 - What is the difference between sand-mold and...Ch. 11 - What are composite molds? Why are they used?Ch. 11 - Describe the features of plaster-mold casting.Ch. 11 - Name the type of materials typically used for...Ch. 11 - What are the advantages of pressure casting over...
Ch. 11 - List the advantages and limitations of die...Ch. 11 - What is the purpose of a riser? What is a blind...Ch. 11 - Explain the purpose of a vent and a runner in a...Ch. 11 - How are shell molds produced?Ch. 11 - What keeps the mold together in vacuum casting?Ch. 11 - What is squeeze casting? What are its advantages?Ch. 11 - What are the advantages of the lost-foam casting...Ch. 11 - Prob. 18RQCh. 11 - What are the reasons for the large variety of...Ch. 11 - Why are risers not as useful in die casting as...Ch. 11 - Describe the drawbacks to having a riser that is...Ch. 11 - Why can blind risers be smaller than open-top...Ch. 11 - Why does die casting produce the smallest cast...Ch. 11 - Why is the investment-casting process capable of...Ch. 11 - What differences, if any, would you expect in the...Ch. 11 - Recently, cores for sand casting have been...Ch. 11 - Would you recommend preheating the molds used in...Ch. 11 - Give reasons for, and examples of, using die...Ch. 11 - Referring to Fig. 11.3, do you think it is...Ch. 11 - Explain why squeeze casting produces parts with...Ch. 11 - How are the individual wax patterns attached on a...Ch. 11 - Describe the measures that you would take to...Ch. 11 - You have seen that, even though die casting...Ch. 11 - How are hollow parts with various cavities made by...Ch. 11 - It was stated that the strength-to-weight ratio of...Ch. 11 - How are risers and sprues placed in sand molds?...Ch. 11 - In shell-mold casting, the curing process is...Ch. 11 - Why does the die-casting machine shown in Fig....Ch. 11 - Prob. 39QLPCh. 11 - What are the benefits to heating the mold in...Ch. 11 - The slushy state of alloys refers to that state...Ch. 11 - Can a chaplet also act as a chill? Explain.Ch. 11 - Rank the casting processes described in this...Ch. 11 - Estimate the clamping force for a die-casting...Ch. 11 - In sand casting, it is important that the...Ch. 11 - If an acceleration of 100 g is necessary to...Ch. 11 - A jeweler wishes to produce 24 gold rings in one...Ch. 11 - Describe the procedures that would be involved in...Ch. 11 - The optimum shape of a riser is spherical to...Ch. 11 - Sketch and describe a casting line consisting of...Ch. 11 - Outline the casting processes that would be most...Ch. 11 - Make a list of the mold and die materials used in...Ch. 11 - Write a brief paper on the permeability of molds...Ch. 11 - Light metals commonly are cast in vulcanized...Ch. 11 - It sometimes is desirable to cool metals more...Ch. 11 - The part shown in Fig. P11.59 is a hemispherical...Ch. 11 - Porosity that has developed in the boss of a...Ch. 11 - In Fig. II.1b the gemstones have been cast in...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A vertical true centrifugal casting process is used to make tube sections with length = 10.0 in and outside diameter = 6.0 in. The inside diameter of the tube 5.5 in at the top and 5.0 in at the bottom. At what speed must the tube be rotated during the operation in order to achieve these specifications?arrow_forwardFor a sand casting a steel rectangular plate with dimensions 80mm x 120mm x 20mm. Calculate shrinkage and draft allowance. And draw the designed pattern. Assume shrinkage of material as 0.1% for 12 inch, pattern material is wood and assume suitable draft anglesarrow_forwardEX.3//A cylindrical riser must be designed for a sand-casting mold. The casting itself is a steel rectangular plate with dimensions 7.5 cm x 12.5 cm x 2.0 cm. Previous observations have indicated that the total solidification time (TTs) for this casting =1.6 min. The cylinder for the riser will have a diameter-to-height ratio=1.0. Determine the dimensions of the riser so that its TTS = 2.0 min.arrow_forward
- 1. A square section riser be designed for a sand-casting mold. The casting itself is a quarter-cylinder with a diameter of 12cm and a length 20cm. The total solidification time for this casting = 0.9 min. The square for the riser will have a height-to-width ratio of 2.0. Determine the dimensions of the riser so that it is total solidification time = 1.2 min.arrow_forwardIn sand casting of hollow part of lead, a cylindrical core of diameter 120 mm and height 180 mm is placed inside the mould cavity. The densities of core material and lead are 1600 kg/m³ and 11300 kg/m³ respectively. The net force (in N) that tends to lift he core during pouring of molten metal will be. . . . .arrow_forward4 In sand casting, the volumetric size of the pattern is (a) bigger than, (b) same size as, or (c) smaller than the cast part? Explain your answerarrow_forward
- Ex.1// A disk 40 cm in diameter and 5 cm thick is to be cast of pure aluminum in an open mold casting operation. The melting temperature of aluminum = 660°C, and the pouring temperature will be 800°C. Assume that the amount of aluminum heated will be 5% more than what is needed to fill the mold cavity. Compute the amount of heat that must be added to the metal to heat it to the pouring temperature, starting from a room temperature of 25°C. The heat of fusion of aluminum = 389.3 J/g... Assume the specific heat has the same value for solid and molten aluminumarrow_forwardWrite down the Experiment “Introduction to Casting Processes and study various stages of casting processes. Give examples of casting products.arrow_forwardA riser in the shape of a sphere is to be designed for a sand casting mould at Simon Castings. The casting is a rectangular plate, with length = 400 mm, width = 250 mm, and thickness = 15 mm. If the total solidification time of the casting itself is known to be 7 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify.arrow_forward
- 6- A pure copper is to be heated for casting a large plate in an open mold. The plate has dimensions: length = 50cm, width = 25cm, and thickness = 7cm. Compute the amount of heat that must be added to the metal to heat it to a temperature of 1176°C for pouring. Assume that the amount of metal heated will be 10% more than what is needed to fill the mold cavity. Properties of the metal are: density = 8.94 g/cm3, melting point = 1082°C, specific heat of the metal = 410 J /kg C° in the solid state and 376 J/Kg C° in the liquid state, and heat of fusion = 186 J/g.arrow_forwardDetermine the time required to fill the mold cavity along with the riser as shown in the following figure. A slab of 1500 mm x 750 mm x 500 mm is required to be cast using a sand casting process. It was observed previously that the total solidification time (T) for this casting = 1.6 min. Find out the cylindrical riser dimensions (diameter to height ratio = 1) for a solidification time T = 5 min.arrow_forwardTrue centrifugal casting is performed horizontally to make large diameter copper tube sections. The tubes have a length = 2.0 m, outside diameter = 0.4 m, and wall thickness = 30 mm. (a) If the rotational speed of the pipe = 600 rev/min, determine the G-factor on the molten metal. (b) Is the rotational speed sufficient to avoid "rain?" (c) What volume of molten metal must be poured into the mould to make the casting if solidification shrinkage and contraction after solidification are considered? Solidification shrinkage for copper = 3.5%, and solid thermal contraction = 6.5%.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Casting Metal: the Basics; Author: Casting the Future;https://www.youtube.com/watch?v=2CIcvB72dmk;License: Standard youtube license