The shear stress-shear strain diagram for a material is shown. The bolt used to hold the lap joint is made of this material and has a diameter of 0.35 in. The material has a Poisson's Ratio of 0.2. T (ksi) T1 G = Values for the figure are given in the following table. Note the figure may not be to scale. Variable T1 71 Value 40 ksi 0.003 rad 71 Ύ (rad) a. Determine the Shear Modulus of the allow, G. b. Determine the Elastic Modulus of the allow, E. c. Determine the force required to cause the material to yield, F. Round your final answers to 3 significant digits/figures. ksi

The shear stress-shear strain diagram for a material is shown. The bolt used to hold the lap joint is made of this material and has a diameter of 0.35 in. The material has a Poisson's Ratio of 0.2. T (ksi) T1 G = Values for the figure are given in the following table. Note the figure may not be to scale. Variable T1 71 Value 40 ksi 0.003 rad 71 Ύ (rad) a. Determine the Shear Modulus of the allow, G. b. Determine the Elastic Modulus of the allow, E. c. Determine the force required to cause the material to yield, F. Round your final answers to 3 significant digits/figures. ksi

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A high-impulse universal testing machine is being used to determine the Young's Modulus of a rectangular solid specimen (l = 20 cm, t = 1.5 cm, w = 2 cm). The machine produces 35,000 Ns that causes the impact force of compression resulted to a 1 mm deformation in the length of the specimen in 0.05 s. Determine the Young's modulus of the specimen expressed in MPa. Round off your answer to the nearest whole number
lin. = 0.2 x 103 in. You test a concrete cylinder having a diameter of 6.00 in and a gauge length of 12 in by applying compression forces. The results of your test are reported in the table as load vs. contraction. Draw, by hand on engineering paper, a stress-strain diagram using scales of: 1 in. = 0.5 ksi in. From the diagram, determine approximately the Modulus of Elasticity. Load (kip) Contraction (in) 0.0 0.0000 5.0 0.0006 9.5 0.0012 16.5 0.0020 20.5 0.0026 25.5 0.0034 30.0 0.0040 34.5 0.0045 38.5 0.0050 46.5 0.0062 50.0 0.0070 53.0 0.0075
Data taken from a stress-strain test for a ceramic are given in the table. The curve is linear between the origin and the first point. Figure σ (ksi) 0 33.2 45.5 49.4 51.5 53.4 € (in./in.) 0 0.0006 0.0010 0.0014 0.0018 0.0022 1 of 1 Part B Determine the modulus of elasticity. E = ksi Submit Part C Determine the modulus of resilience. Ur= in-lb in³ Submit Request Answer Provide Feedback Request Answer
2) The stress-strain diagram for an alloy specimen having an original diameter of 0.5 in. and a gage length of 2 in. is shown in the figure below. TENSILE STRESS (MPA) 450 400 350 300 250 200 150 100 50 Part A 0 0 STRESS VS. STRAIN 0.002 0.004 STRAIN 0.006 Determine the modulus of resilience. Show units. Part B Determine the modulus of elasticity of the material. Part C Estimate the Yield Strength of the material. 0.008 0.01
The data illustrated below have been determined while the tension test of the stainless steel sample by amateur engineers. The gage length of the stainless steel sample was 50.8 mm (2.0in.) and, the original diameter of the steel sample was 12.8 mm (0.505in.). Load (Ib) Elongation (in.) Load (Ib) Elongation (in.) 14000 0.020 2 310 0.0022 14400 0.025 4 640 0.0044 14 500 0.060 6950 0.0066 14600 0.080 9 290 0.0088 14800 0.100 11 600 0.0110 14 600 0.120 13000 0.0150 13600 Fracture With the help of Excel, plot the stress-strain diagram for this test conducted, and define the following mechanical properties: a) Young modulus; b) Proportional limit; c) Yield stress @0.2% offset; d) ultimate stress; e) nominal rupture stress.
Q1- The following data was obtained tensile test ɔn a specimen of 10 mm diameter and gauge length Lo=50 mm: 0 38 | 76.2 92.7 107 149 160.4 | 155 142 124.7 load(KN) | elongation(mm) 0 0.02 0.12 0.25 0.50 2.03 3.55 4.06 5.1 5.84 Using the graphic paper supplied, Plot engineering stress-strain curves, then determine the (ay, ey), (ou , eu), (of,, ef), modulus of elasticity, then detected in the draw ((stroin hardening (m)), (Necking), (uniform plastic region and non-uniform plastic region) and (elastic & plastic) region))?
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. Question 1 ;Determine the elastic energy absorption capacity (in N.mm) of that specimen. Question 2; Determine the plastic energy absorption capacity (in N.mm) of that specimen.
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Determine the true stress (in MPa) at yield point. - Determine the true stress (in MPa) at point of ultimate strength. - Determine the true stress (in MPa) at fracture point. - Determine the true strain (in mm/mm) at yield point. (Use at least five decimal units) - Determine the true strain (in mm/mm) at point of ultimate strength. (Use at least five decimal units) - Determine the true strain (in mm/mm) at fracture point. (Use at least five decimal units)
Data taken from a stress-strain test for a ceramic are given in the table. The curve is linear between the origin and the first point. Figure σ (ksi) 0 33.2 45.5 49.4 51.5 53.4 € (in./in.) 0 0.0006 0.0010 0.0014 0.0018 0.0022 < 1 of 1 Part A Plot the stress-strain diagram. (Figure 1) +SGA0 No elements selected σ(ksi) Submit Request Answer 50 40 30+ 20 10 0.5 1.0 1.5 2.0 2.5 €x 10-³(in./in.) ? Select the elements from the list and add them to the canvas setting the appropriate attributes. Press [CTRL+M) to get to the main menu.
1 - A tensile test is carried out on a specimen of mild steel of gauge length 40 mm and diameter 7.42 mm. The results are: Load (kN) 10 17 25 30 34 37.5 38.5 36 Extension (mm) 0 0.05 0.08 0.11 0.14 0.20 0.40 0.60 0.90 At fracture the final length of the specimen is 40.90 mm. Plot the load/ extension graph and determine (a) The modulus of elasticity for mild steel, (b) The yield stress, (c) The ultimate tensile strength, (d) The percentage elongation 2 - An aluminum alloy specimen of gauge length 75 mm and of diameter 11.28 mm was subjected to a tensile test, with these results: Load (kN) 2.0 6.5 11.5 13.6 16.0 18.0 19.0 20.5 19.0 Extension (mm) 0 0.012 0.039 0.069 0.080 0.107 0.133 0.158 0.225 0.310 The specimen fractured at a load of 19.0 kN. Determine (a) the modulus of elasticity of the alloy, (b) The percentage elongation. (c) The ductility in term of reduction of area (d) Fracture stress (e) Tensile strength
The following data was obtained as a result of tensile testing of a standard 0.505 inch diameter test specimen of magnesium. After fracture, the gage length is 2.245 inch and the diameter is 0.466 inch. a). Calculate the engineering stress and strain values to fill in the blank boxes and plot the data. Load(lb) Gage Length (in) Stress (kpsi) Strain 0 2 1000 2.00154 2000 2.00308 3000 2.00462 4000 2.00615 5000 2.00769 5500 2.014 6000 2.05 6200 (max) 2.13 6000 (fracture) 2.255 b). Calculate the modulus of elasticity c). If another identical sample of the same material is pulled only to 6000 pounds and is unloaded from there, determine the gage length of the sample after unloading.
1. A tension test on an aluminum plate resulted in the following engineering stress-engineering strain data as reported in the first and second column of the table below (reduction of area, RA=17%): S (psi) e (in/in) σ (psi) ε (in/in) 10500 0.001 10510.5 0.000995 21000 0.002 31200 0.003 41300 0.004 51200 0.005 61200 0.006 70600 0.007 74700 0.0075 76800 0.008 77600 0.0085 78000 0.009 78400 0.0095 78700 0.01 81200 0.02 83000 0.03 84200 0.04 85400 0.05 86200 0.06 86800 0.07 *87200 0.08 **86200 0.1 Note: * maximum load, ** load at fracture a) Calculate the corresponding true stress and true strain and give your results in a table along with the engineering stress, engineering strain shown in the of table above (column 3 and 4). b) Plot the true stress-true strain curve on a rectangular coordinate. c) Plot the true stress-true strain curve on a log-log graph and determine the plastic flow curve parameters K and n, the yield strength, Y, and the elastic modulus, E of the material.