In a compression testing of concrete cylinders, stress and strain obtained from theexperiment are presented in the following tableex 103It was found that a function which can describe theo (MPa)7.10.265relationship between stress and strain is9.70.40011.80.500O = aɛe-bɛ14.40.70016.70.950Please determine a and b and make a plot tocompare the results with the data obtained fromthe model19.01.36020.72.08019.72.45018.52.940

given relation between stress and strain σ=aεe-bεand experiment table

In a compression testing of concrete cylinders, stress and strain obtained from the experiment are presented in the following table o (MPa) ex 10 It was found that a function which can describe the 7.1 0.265 relationship between stress and strain is 9.7 0.400 11.8 0.500 O = aɛe-bɛ 14.4 0.700 16.7 0.950 Please determine a and b and make a plot to 19.0 1.360 comparo the rOcults with tho data ohtainod from

In a compression testing of concrete cylinders, stress and strain obtained from the experiment are presented in the following table o (MPa) ex 10 It was found that a function which can describe the 7.1 0.265 relationship between stress and strain is 9.7 0.400 11.8 0.500 O = aɛe-bɛ 14.4 0.700 16.7 0.950 Please determine a and b and make a plot to 19.0 1.360 comparo the rOcults with tho data ohtainod from

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Q1- The engineering tensile stress-strain data were obtained for AA6061-T6 aluminum alloy shown: note stress unit is (MPa). 314 294 266 226 287 325 329 337 334 a.(stress) 0 52 159 E.(strain) 0 1.07 1.70 2.23 3.07 4.80 7.13 9.13 11.33 12.97 14.40 16.10 Plot the stress-strain curves then determine the mechanical properties as followings, ay, ou, elastic zone, plastic zone, Young modulus, fracture stress and ductility if you know L - 30 mm, and Lf - 33.7 mm.
You have been given the following set of data from a soil-geotextile friction test: Normal stress (kPa) Peak shear strength (kPa) Residual shear strength (kPa) 17 20.2 13 35 31 22 70 52 39.5 140 94 74.5 (a) Plot the Mohr-Coulomb failure envelope (x-axis=normal stress; y-axis=shear stress) (b) Determine the peak friction angle, and the residual friction angle, . (c) Determine the peak adhesion and the residual adhesion. (d) Calculate the fabric efficiency based on a soil friction angle of = 35-degrees using the peak friction angle. **HINT: the equation for efficiency of soil friction angle mobilization is:
Tutorial Mechanical properties 1. Based on data collected as Table 1, plot graph Stress vs strain, determine YS, TS and E. | Table 1: Data load and length for tensile test Gage length (mm) Load Gage length Load (N) (mm) (N) 35,220 35,720 40,540 50.8000 50.9778 50.8102 50.8203 4,890 51.0032 9,779 51.8160 14,670 50.8305 48,390 53.3400 19,560 24,450 27,620 29,390 32,680 33.950 34,580 50.8406 59,030 65,870 69,420 69,670 (maximum) 55.8800 50.8508 50.8610 58.4200 60.9600 50.8711 61.4680 50.9016 68,150 63.5000 50.9270 60,810 (fracture) 66.0400 (after fracture) 50.9524 Original, specimen diameter: 12.7 mm.
Force P and length change AL data are given in table below for the initial portion of a tension test on 7075-T651 Al alloy. The diameter before testing was 9.07 mm., and the gage length Linitial for t length change measurement was 50.8 mm. What tension force is required to cause yielding in a bar of the same material but with a diameter of 20 mm? P, kN AL mm 7.22 0.0839 14.34 0.1636 21.06 26.8 31.7 34.1 35.0 0.241 0.308 0.380 0.484 0.614 36.0 0.924 36.5 1.279 36.9 37.2 1.622 1.994
A specimen with cylindrical shape was subjected to tensile test. Please plot the stress vs. strain curve for the specimen and calculate Young's modulus. Diameter of test specimen, do = 11.600 mm Length of test specimen, lo = 50.500 mm Load vs. elongation data for the test specimen Load (N) Length (mm) 7.150 50.594 14.840 50.768 22.760 50.942 30.220 51.116 33.980 51.290 37.900 51.464 41.120 51.892 44.220 52.320 45.540 52.748 47.120 53.684 46.760 54.620 45.280 55.550 44.620 56.238 41.700 56.920 36.220 57.602
Problem :- The following data was obtained tensile test on a specimen of 6 mm diameter and gauge length Lo=30 mm: load(KN) 0 40 80 95 90 135 150.2 145 130 120 elongation(mm) 0 0.022 0.13 0.25 0.55 2.01 3.88 4.12 5.22 6 Plot engineering and True (stress-strain) curves, then determine the (oy, ɛy), (ou, ɛu), (of, , ef), ductility, modulus of elasticity. Then select on the drawing ((strain hardening (n)) , (Necking), (uniform plastic region and non-uniform plastic region) and (elastic & plastic) region)?
The following data are taken from a 20mm in diameter bar of length 250mm, the following results were recorded. Assume that the curve of the stress-strain diagram is linear from the origin to the first point. P (load in kN) 8(elongation in mm) 112 0.2 154 0.3 167 0.4 0.5 174 181 0.8 Determine the a. Stress at 187 kN load in MPa b. Strain at 167 kN load in mm/mm (expressed in scientific notation) c. Modulus of elasticity in MPa d. Modulus of resilience in N-mm/mm e. Modulus of toughness in N-mm/mm 234 oo OOO O0
Table B2: Stress-strain data for uniaxial compression test on Sample Normal stress Uniaxial strain (%) Lateral strain (%) (MPa) 0.0 0.0000 0.0000 5.0 0.0319 -0.0150 10.0 0.0720 -0.0275 15.0 0.1025 -0.0425 20.0 0.1450 -0.0600 25.0 0.1755 -0.0725 30.0 0.2150 -0.0875 35.0 0.2455 -0.1025 41.0 0.2815 -0.1125 46.0 0.3125 -0.1209 52.0 0.3515 -0.1285 58.0 0.4000 -0.1325 (f) Based on the plotted curve, calculate the average/tangent Young's modulus and Poisson's ratio for this sample, at 50 % UCS?
stress 0.02 0.018 0.016 0.014 0.012 0.01 0.008 0.006 0.004 0.002 0.05 0.1 0.15 0.2 0.25 0.3 0.35 Determine : 1- Stress, Stratn care 2. elastic Zone 3. yield sbresscoys 4- plastic Zone 5- UItimate Stress Cous 6- Elongation 7- propotionaL stress cops 8-fructurc stress coF)
The following data was obtained tensile test on a specimen of 6 mm diameter and gauge length Lo=30 mm: 142 124.7 5.1 5.84 Using the graphic paper supplied, Plot engineering stress-strain curves, then determine the 0| 38 160.4 155 4.06 3.55 76.2 load(KN) elongation(mm) 00.02 92.7 107 149 0.12 0.25 0.50 |2.03 (gy sy), (gu, eu), (of, sf), modulus of elasticity, then detected in the draw ((strain hardening (n)), (Necking), (uniform plastic region and non-uniform plastic region) and (elastic & plastic) region))?
A 11 in. inner diameter, 0.35 " wall thickness pipe is under a pressure of 2.5 ksi where strain gages installed along axial and circumferential directions register strains of 180 and 900 micro-strains (x10^-6), respectively. A) What is the Poisson's Ratio of this material and it's Elastic Modulus? B) In a uniaxial test, the pipe's material is observed to yield at a longitudinal strain of 0.1 in/in. Assuming a factor of safety of 2, the pipe can withstand impact energy of _______ lb - in per foot without suffering permanent deformation. C) If the pipe is depressurized and then subjected to a torque of 50 lblb - ft.ft., it will experience a shear strain of ________ rad.
A 11 in. inner diameter, 0.35 " wall thickness pipe is under a pressure of 2.5 ksi where strain gages installed along axial and circumferential directions register strains of 180 and 900 micro-strains (x10^-6), respectively. A) What is the Poisson's Ratio of this material and it's Elastic Modulus? B) In a uniaxial test, the pipe's material is observed to yield at a longitudinal strain of 0.1 in/in.in/in. Assuming a factor of safety of 2, the pipe can withstand impact energy of _______ lblb - in.in. per foot without suffering permanent deformation. C) If the pipe is depressurized and then subjected to a torque of 50 lblb - ft.ft., it will experience a shear strain of ________ rad.