An initially rectangular element of a material is deformed into the shape shown in the figure. Deformed Undeformed 16.6 0.1992 mm 15.7 02 mm Normal strain in the x- direction* -4.0 x 10^-3 O 4.0 x 10^-3 O 10 x 10-3 O -10 x 10^-3 Normal strain in the y- direction* O -4.0 x 10^-3 4.0 x 10^-3 O 10 x 10-3 O -10 x 10^-3 Total shear strain * O 0.6 deg. O 0.7 deg O 0.8 deg O 0.9 deg. |I| O O

An initially rectangular element of a material is deformed into the shape shown in the figure. Deformed Undeformed 16.6 0.1992 mm 15.7 02 mm Normal strain in the x- direction* -4.0 x 10^-3 O 4.0 x 10^-3 O 10 x 10-3 O -10 x 10^-3 Normal strain in the y- direction* O -4.0 x 10^-3 4.0 x 10^-3 O 10 x 10-3 O -10 x 10^-3 Total shear strain * O 0.6 deg. O 0.7 deg O 0.8 deg O 0.9 deg. |I| O O

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

A steel section having a cross section of 20 mm x 30 mm is subjected to an axial force of 240 kN. The steel section has produces a strain of 0.002. If it has a value of Poisson's ratio of 0.30. Which of the following gives the bulk modulus of the steel section. a. 133333 MPa b. 166667 MPa c. 111111 MPa d. 144444 MPa
Table 1 shows the stress-strain data for a new polymeric material rod subjected to an axial load. The last point is observed as the rupture point. Table 1: Stress-strain data for new polymeric matenial Strain, e (dimensionless) Stress, s (Pa) 32 0.1 59 0.2 75 0.3 86 0.4 104 0.5 120 0.6 129 0.7 125 0.8 114 0.9 97 * The yield point is the point on a stress-strain curve that indicates the limit of elastic behaviour and the beginning of plastic behavior. In this case, the yield point occurs at a stress value of 80. Determine the corresponding strain value at the yield point. In any relevant method, use a stopping criterion of 0.05%. e) The ultimate strength is the maxinmum point on the stress-strain curve. This corresponds to the maximum stress that can be sustained by a structure in tension. Compute the ultimate strength point of the polymeric material (strain value that gives maximum stress). In any relevant method, use a stopping criterion of 0.05%. Detemine the absolute error between…
Question 1: The piece of plastic is originally rectangular. Given LCD and LAD are 400 and 300 mm, respectively. If the plastic distorts as shown by the dashed lines, a) Determine the average normal strain that occurs along CD. b) Determine the average normal strain that occurs along AD. c) Determine the shear strain Yxy at corner C. 2 mm LCD 2 mm D LAD mm B 12 mm 3 mm mm
The state of stresses in the x and y directions at a point in a given material is shown in the figure below. If the value of the shear stress in the x-y axes Ty is 17N/mm2, find the maximum shear stress that can be found at this point in any possible direction. Round off your answer to the nearest N/mm2. 10 N/mm2 Txy 20 N/mm2 20 N/mm2 Txy 10 N/mm2
In a laboratory test of a beam loaded by end couples, the fiber at layer AB as shown are found to increase 40 x 10* mm while those at CD decrease 90 x 10 3 mm in the 240-mm-gage length. Using E = 120 GPa, determine the flexural stress at the bottom fiber. Answer must be in MPa. Given: a 50 mm, b = 130 mm, and c 80 mnm. gage length a mm b mm c mm Next>
Take oz = 84 MPa and Tzy = 35 MPa (Figure 1) Part A Determine the equivalent state of stress on an element at the same point that represents the principal stresses at the point. Express your answers in ascending order separated by a comma using three significant figures. VO AEO t vec ? igure 01, 02 = MPа Submit Request Answer Txy Part B Also, find the corresponding orientation of the element with respect to the element shown. Express your answers using three significant figures separated by a comma. Hνα ΑΣφ vec (8,)1. (8,)2 =
1.16 The stress-strain relationship shown in Figure P1.16 was obtained during the tensile test of an aluminum alloy specimen. 60,000 H Stress, psi 40,000 20,000 0 Figure P1.16 0.002 0.004 0.006 0.008 Strain, in./in. Determine the following: a. Young's modulus within the linear portion. b. Tangent modulus at a stress of 45,000 psi c. Yield stress using an offset of 0.002 strain d. If the yield stress in part c is considered failure stress, what is the maximum working stress to be applied to this material if a factor of safety of 1.5 is used? 4
A piece of (A =53 mm × B= 29 mm) material experiences a homogenous deformation. The deformed shape in x-y plane is illustrated by the solid lines. What is the value of the shear strain, provide your answer in six decimal points. 0.25 0.2 Answer: B 0.15 0.3 A
A tensile test was conducted on a specimen with a diameter of 0.5 in. A strain gage was bonded to the specimen so that the strain could be obtained directly. The following data were obtained: Load (lb) 2000 2500 3000 3500 4000 4500 5000 Strain 0.000047 0.000220 0.000500 0.000950 0.001111 0.001200 0.001702 Create a table of stress and strain values Plot these data point, and draw a best-fit straight line through them What is the slope of this line? What does this value represent?
1.17 Figure P1.17 shows the stress-strain relations of metals A and B during tension tests until fracture. Determine the following for the two metals (show all calcu- lations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 in./in. 150 - - Metal A 100 • Metal B 50 0.00 0.02 0.04 0.06 0.08 0.10 0.12 0.14 Strain, in./in. FIGURE P1.17 c. Ultimate strength d. Modulus of resilience e. Toughness f. Which metal is more ductile? Why? Stress, ksi
Question 3 - Strain Transformation The state of strain at a point in a rectangular block of material using an x-y coordinate system is given by: • €xx = 51×10-4 €yy = 18 ×10-4 Yxy=-4x10-4 ● ● Part One a) Which element below best represents the deformed element due to the state of strain in the x-y plane? 6 2 B) D) D) F) Hint: Consider the relative magnitude and sign of each component of strain
The state of stresses in the x and y directions at a point in a given material is shown in the figure below. If the value of the shear stress in the x-y axes Ty is 19N/mm2, find the maximum direct stress that can be found at this point in any possible direction. Round off your answer to the nearest N/mm2. 10 N/mm2 Txy 20 N/mm2 20 N/mm2 Txy 10 N/mm2