An aluminium specimen with an initial gauge diameter do = 10 mm and gauge length, 1 = 100 mm is subjected to tension test. A tensile force P= 50 kN is applied at the ends of the specimen as shown, resulting in an elongation of 1 mm in gauge length. The Poisson's ratio (u) of the specimen is _ Take shear modulus of material, G = 25 GPa. Consider engineering stress-strain conditions. †P

An aluminium specimen with an initial gauge diameter do = 10 mm and gauge length, 1 = 100 mm is subjected to tension test. A tensile force P= 50 kN is applied at the ends of the specimen as shown, resulting in an elongation of 1 mm in gauge length. The Poisson's ratio (u) of the specimen is _ Take shear modulus of material, G = 25 GPa. Consider engineering stress-strain conditions. †P

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 6.5P

See similar textbooks

Similar questions

The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.
Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.
I5 In a tensile test experiment of carbon steel. a standard specimen (D= 0.505 in. Gauge length=2.0 in & total length 8 in) had a 0.2% offset yield strength of 80.000 psi and engineering strain of 0.010 at the yield strength point Calculate: The load (force) at this point. The instantaneous area of the specimen at this point. c. The true stress at this point. d. The true strain at this point. e. The total length of the specimen. if the load is released at this point.
Consider a cylindrical metal 6 mm in diameter and 50 mm long ispulled in tension. It is known that yield strength and elastic (Young’s) Modulus of thematerial are 200 MPa and 100 GPa, respectively, and its Poisson’s Ratio is 0.3.(a) Determine whether the deformation is elastic or plastic when 6000 N is applied.(b) Calculate specimen elongation (∆l) and reduction in diameter (∆d) when 5000 N isapplied? What are the values ∆l and ∆d when the load is released?(c) If necking occurs at a load of 8850 N, determine the UTS of the metal.(d) Calculate the ductility in terms of % E.L. if the length of the specimen at fracturepoint is 56.0 mm.
An applied torque results in a shear strain (y) of 3.75 x 103 in a solid circular steel shaft. At this strain, a portion of the shaft cross- section yields as shown in Figure 2. Determine the magnitude of the applied torque. Take G = 80 GPa and yy = 2.8125 x %3D 10-3 FIGURE 2: Plastic zone 50 mm 200 mm Elastic core
A metal sample on a tension in the test ,296MPa , a tensile true strain 0.08, and true stress 356 MPa when the strain is 0.27. Determine the strength coefficient and strain hardening exponent in the flow curve equation.
For a point on a steel specimen, the principal stresses are known to be 01 = 360 MPa and O2 = 60 MPa. Calculate the minimum yield stress of the material according to the Tresca criterion. Give your answer in MPa to 3 significant figures.
A cylindrical tensile specimen has an undeformed diameter of 8.6 mm. It is subjected to a tensile load of 100 kN. The elastic modulus (E) is 10 GPa. Poisson's ratio is 0.25. Calculate the change in the diameter (in mm).
The specimen shown is made from a 25 mm diameter cylindrical steel rod with two 38 mm outer-diameter sleeves bonded to the rod as shown. Knowing that E = 200 GPa, determine (a) the load P so that the total deformation is 0.05 mm, (b) the corresponding deformation of the central portion BC. 38 mm diameter P' 25 mm diameter B 38 mm diameter C 50 mm 75 mm 50 mm
The (G-E) diagram obtained in the tensile test performed on a metal sample with a diameter of 16 mm is as follows. The loads at points A, B and C and the elongation measured on l. 16 cm gauge length were determined as follows: B A B C Load (kgf) 4800 8400 7200 Elongation (mm) 0.192 28.8 38.4 c) Calculate the fracture work and the maximum elastic energy the metal rod can store. d) Find the cross-sectional area of a 6 m long rod made of this metal such that it can carry 12 tons of load with 2 times the safety of yield strength. How long does the rod extend under this load?
A steel wire with a diameter of d = 1/16” is bent around a cylindrical drum with a radius ofR = 36”.(a) Determine the maximum normal strain in the wire.(b) What is the minimum acceptable radius of the drum if the maximum normal strain mustremain below yield? Consider an elastic modulus of 30000 ksi and yield stress of 100ksi.(c) If R = 36”, what is the maximum acceptable diameter of the wire if the maximum normalstrain must remain below yield?
A 5-mm-thick rectangular alloy bar is subjected to ajtensile load P by pins at A and B, as shown in the figure. The width of the bar is w = 33 mm. Strain gages bonded to the specimen measure the following strains in the longitudinal (x) and transverse (y) directions: €, =710 με and ε,--255 με (a) Determine Poisson's ratio for this specimen. (b) If the measured strains were produced by an axial load of P = 24 kN, what is the modulus of elasticity for this specimen? Answers: (a) v= (b) E= GPa