(a) What is the effect of increasing the carbon content in steel on each of the each of the following items? 1. Yield strength 2. Modulus of elasticity 3. Ductility (b) Materials are generally classified into three categories based on the predominant types of bond. What are these three and what are the predominant types of bond in each category? For each category, provide two examples of common ma by civil engineers.

(a) What is the effect of increasing the carbon content in steel on each of the each of the following items? 1. Yield strength 2. Modulus of elasticity 3. Ductility (b) Materials are generally classified into three categories based on the predominant types of bond. What are these three and what are the predominant types of bond in each category? For each category, provide two examples of common ma by civil engineers.

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter14: Material Selection

Section: Chapter Questions

Problem 8ETSQ

See similar textbooks

Similar questions

The frame of a space shuttle type vehicle must have a high yield strength and high stillness, and the most important design factor is weight. Of all the materials presented in this chapter, what material might be the most suitable for the frame of a space shuttle? Assume that there will be both tensile and compressive stresses. For a space shuttle, cost is not a limiting factor. (a) You can eliminate entire classes of materials from consideration with a brief statement about their unsuitability. (b) What material has the highest specific yield strength? Give the yield strength, specific gravity, specific yield strength, elastic modulus, and specific elastic modulus for this material. (c) What material has the highest specific elastic modulus? Give the yield strength, specific gravity, specific yield strength, elastic modulus, and specific elastic modulus for this material. (d) Compare the materials with the highest specific yield strength and highest specific elastic modulus for suitability in the space shuttle frame. (C) Discuss the suitability of the top-rated material for this design from the viewpoint of the ability to produce a frame.
Which of the following terms indicate "the ability of the material to not to undergo change in shape when loads are applied" a. Weldability b. Formability c. Conductivity d. Rigidity
Explain in detail the effect of Temperature on the Elastic Modulus and Yield Strength ofEngineering materials.
1. The tensile strength vs. temperature curves of aluminum are plotted below. Explain the meaning of these two curves. 400 Ultimate strength 300 Yield strength 200 100 -200 -150 -100 -50 50 100 150 200 250 Temperature, °C Strength, kPa
The following figure shows the tensile stress-strain curve for a plain-carbon steel. 600 80 500 MPa 600 10 psi 60 80 400 400 60- 300 40 40 200 200 20 20 100 0.005 0.05 0.10 0.15 Strain (a) What is this alloy's tensile strength? MPа (b) What is its modulus of elasticity? GPa (c) What is the yield strength? i MPa Stress (MPa) Stress (10 psi)
c). Interpret the following diagram? The effect of carbon and heat treatment on the properties of plain carbon steels. 160 140 Tensile 120 strength 100 Impact energy | 100 Annealed 80 80 Normalized 60 60 Annealed 40 `Yield strength 20-% Elongation Annealed 20 Normalized- 0.2 0.4 0.6 0.8 1.0 Weight percent carbon Figure-4 Yield and tensile strength (ksi) Normalized % Elongation or impact energy (ft • Ib)
strength of material subject columns chapter about reduction factor, in working stress
I need to solve this question of strength materials
Three materials X, Y, and Z are available for a certain usage. Any material selected must have a good weldability. Tensile strength, stiffness, stability and fatigue strength are required with fatigue strength considered being the most important and stiffness the least important of these factors. The three materials are rated as follows in these factors. Properties X Y Weldability Excellent Рoor Good Tensile strength G E Fair Stiffness Very Good G G Stability G E G Fatigue strength F G E Which material should be selected? Explain your choice.
Explain how dislocations have paradoxically rationalized why metals can be bothmechanically weak and strong. How have dislocations helped to explain work hardening of metals.
Q2c) Listed in the table below is the tensile stress-strain data for different grades of steels. Utilizing the data given answer the three queries given below. Material Yield Tensile Strain at Fracture Elastic StrengthStrengthFractureStrengthModulus (MPa) (MPa) (MPa) (GPa) A 410 1440 0.63 265 410 В 200 220 0.40 105 250 C 815 950 0.25 500 610 D 800 650 0.14 720 210 E Fractures before yielding 650 550 1) Which will experience the greatest percent reduction in area? Why? 2) Which is the strongest? Why? 3) Which is the stiffest? Why?
10 Which is not an elastic constant? Bulk modulus Shear Modulus none of the choices Modulus of elasticity