A three-point bending test was performed on an aluminum oxide specimen having a circular cross section of radius 6.7 mm; the specimen fractured at a load of 3190 N when the distance between support points was 46 mm. Another test is to be performed on a specimen of this same material, but one that has a square cross section of 16 mm in length on each edge. At what load would you expect this specimen to fracture if the support point separation is maintained at 46 mm? Ff = ____________ N

A three-point bending test was performed on an aluminum oxide specimen having a circular cross section of radius 6.7 mm; the specimen fractured at a load of 3190 N when the distance between support points was 46 mm. Another test is to be performed on a specimen of this same material, but one that has a square cross section of 16 mm in length on each edge. At what load would you expect this specimen to fracture if the support point separation is maintained at 46 mm? Ff = ____________ N

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.1P

See similar textbooks

Similar questions

The (G-E) diagram obtained in the tensile test performed on a metal sample with a diameter of 16 mm is as follows. The loads at points A, B and C and the elongation measured on l. 16 cm gauge length were determined as follows: B A B C Load (kgf) 4800 8400 7200 Elongation (mm) 0.192 28.8 38.4 c) Calculate the fracture work and the maximum elastic energy the metal rod can store. d) Find the cross-sectional area of a 6 m long rod made of this metal such that it can carry 12 tons of load with 2 times the safety of yield strength. How long does the rod extend under this load?
A three-point bending test was performed on an aluminum oxide specimen having a circular cross section of radius 5.3 mm; the specimen fractured at a load of 3000 N when the distance between the support points was 40 mm. Another test is to be performed on a specimen of the same material, but one that has a square cross section of 18 mm length on each edge. At what load would you expect this specimen to fracture if the support point separation is maintained at 40 mm?
Question 4. A tensile test is carried out on a bar of mild steel of diameter 2 cm. The bar yields under a load of 80 Kn. It reaches a maximum load of 150 kN, and breaks finally at a load of 70 kN. Estimate: a)the tensile stress at the yield point b)the ultimate tensile stress c)the average stress at the breaking point if the diameter of the fractured neck is 1 cm.
A three-point bending test was performed on an aluminum oxide specimen having a circular cross section of radius 5.0 mm (0.20 in.); the specimen fractured at a load of 3000 N (675 lbf) when the distance between the support points was 40 mm (1.6 in.). Another test is to be performed on a specimen of this same material, but one that has a square cross section of 15 mm (0.6 in.) length on each edge. At what load would you expect this specimen to fracture if the support point separation is maintained at 40 mm (1.6 in.)?
The following observations were made during a tensile test on a mild steel specimen 40 mm in diameter and 200 mm long. Elongation is with 40 kN load (with in limit of proportionality) 8=0.0304mm, yield load = 161 kN, Maximum load = 242 kN Length of specimen at fracture = 249mm Find: 1) Young's Modulus of elasticity ; E 2) Yield point stress Ultimate stress 3) 4) Percentage elongation
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At the fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the proportional limit, modulus of elasticity (i.e the slope of initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percentage reduction in area Tensile-Test Data Load(kN) Elongation (mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
A metal specimen with a square cross-sectional area having a gauge length of 50.0 mm is pulled in tension.If its width at the point of fracture is 5 mm and fractured gauge length is 75 mm. Calculate the ductility interms of:a) percent elongation b) percent reduction in area (Assume that its original width is 9 mm.)
Question 1 a) A standard mild steel tensile test specimen has a diameter of 16mm and a gauge length of 80mm. the specimen was tested to destruction and the following results obtained, Load at yield point = 87KN Extension at yield point = 173 x 10“ m Ultimate load = 124KN %3D Total extension at fracture = 24mm Diameter of specimen at fracture = 9.8mm Cross-sectional area at fracture = 75.4mm? Cross-sectional area "A" = 200mm² Compute the followings: Modulus of elasticity of steel. Ultimate tensile stress. i. ii. iii. Yield stress iv. Percentage elongation.
A tensile test was performed on a metal specimen with a circular cross section. The diameter was measured to be 0.550 inch. Two marks were made along the length of the specimen and were measured to be 2.030 inches apart. This distance is defined as the gage length, and all length measurements are made between the two marks. The specimen was loaded to failure. Fracture occurred at a load of 28,500 pounds. The specimen was then reassembled, and the diameter and gage length were measured to be 0.430 inch and 2.300 inches. Determine the a. Ultimate tensile stress in ksi. b. Elongation as a percentage. c. Reduction in cross-sectional area as a percentage
A steel specimen is tested in tension. The specimen is 25 mm wide by 12.5 mm thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 160 kN and fractured at 214 kN. a. Determine the tensile stress at yield and at fracture. b. If the original gauge length was 100 mm, estimate the gauge length when the specimen is stressed to 1/2 the yield stress.
Example 8.4. A specimen of steel 20 mm diameter with a gauge length of 200 mm is tested to destruction. It has an extension of 0.25 mm under a load of 80 kN and the load at elastic limit is 102 kN. The maximum load is 130 kN. The total extension at fracture is 56 mm and diameter at neck is 15 mm. Find (i) The stress at elastic limit. (ii) Young's modulus. (iii) Percentage elongation.
Question: A structural component in the form of a wide plate is to be fabricated from a steel alloy that has a plane strain fracture toughness of 98.9 MPa sqrt(m) (90 ksi sqrt(in.)) and a yield strength of 860 MPa (125,000 psi). The flaw size resolution limit of the flaw detection apparatus is 3.0 mm (0.12 in.). If the design stress is one-half of the yield strength and the value of Y is 1.0, determine whether or not a critical flaw for this plate is subject to detection.