A tension test was carried out on a rounded mild steel specimen with a diameter of 16 mm and divided for 10 equal parts with length 16 mm each. The recorded length after the failure was as follow: No 1 2 3 4 5 6 7 8 10 The recorded 20 20.5 21 25 21 19.5 19 18.5 18.5 18 length It's required to: Draw the distribution of the elongation along the specimen then determine the ductility with two different ways if the diameter= 8mm at the failure.

A tension test was carried out on a rounded mild steel specimen with a diameter of 16 mm and divided for 10 equal parts with length 16 mm each. The recorded length after the failure was as follow: No 1 2 3 4 5 6 7 8 10 The recorded 20 20.5 21 25 21 19.5 19 18.5 18.5 18 length It's required to: Draw the distribution of the elongation along the specimen then determine the ductility with two different ways if the diameter= 8mm at the failure.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Please show handwritten solution
Compare and discuss the results. Determine the experimental shear modulus of elasticity. TORSION TEST EXPERIMENT
Hello, I hope you are fine. I need to do this homework in Metal Engineering. I hope to get your help because I have an important homework.
Q1- The following data was obtained tensile test ɔn a specimen of 10 mm diameter and gauge length Lo=50 mm: 0 38 | 76.2 92.7 107 149 160.4 | 155 142 124.7 load(KN) | elongation(mm) 0 0.02 0.12 0.25 0.50 2.03 3.55 4.06 5.1 5.84 Using the graphic paper supplied, Plot engineering stress-strain curves, then determine the (ay, ey), (ou , eu), (of,, ef), modulus of elasticity, then detected in the draw ((stroin hardening (m)), (Necking), (uniform plastic region and non-uniform plastic region) and (elastic & plastic) region))?
Load (N) Elongation (mm) In a tensile test of stainless steel, the following data were obtained: 7,200 11,250 13,500 16,200 18,900 20,200 20,700 13,200 24.90 0.0 0.505 2.03 5.08 10.16 15.24 21.80 The dimensions of the cylindrical specimen were initial length L₁= 50.8 mm and initial area A₁ = 35.8 mm² and the area at fracture was Ar = 10.0 mm². Plot the stress-strain diagram and determine the following: a) Modulus of elasticity b) The yield strength at a strain offset of 0.002 c) Ultimate strength d) Fracture strength
A tension test was performed on a specimen having an original diameter of 13.7 mm and a gauge length of 50 mm. The data are listed in the table. Load (kN) Elongation (mm) 0 11.1 31.9 37.8 40.9 43.6 53.4 62.3 64.5 62.3 58.8 0 0.0175 0.0600 0.1020 0.1650 0.2490 1.0160 3.0480 6.3500 8.8900 11.9380 Plot the stress-strain diagram. Use a scale of 20 mm = 50 MPa and 20 mm = 0.05 mm/mm. Redraw the linear-elastic region, using the same stress scale but a strain scale of 20 mm = 0.001 mm/mm. From the diagram, determine approximately the modulus of elasticity. Express your answer to three significant figures and include the appropriate units. E = Submit Part B συ = Submit Part C ☐☐ μÅ of = Value Determine the ultimate stress. Express your answer to three significant figures and include the appropriate units. Request Answer μĂ Value Request Answer Units μĂ - Value Units Determine the fracture stress. Express your answer to three significant figures and include the appropriate units. ? Units ? ?
Calculate the young’s Modulus in GPa from the data
A test rod of rust-resistant steel, with a diam. of 12.8 mm and a measuring length of 50.8 mm is subjected to a tensile test. The data from the test is shown in the table below.
40. A tensile test specimen has a gage length 2.0 in and diameter 0.875 in. Yielding occurs at a load of 35,500 lb. The corresponding gage length 2.0113 in (neglect the 0.2 percent yield point). The maximum load of 45,000 lb is reached at a gage length 2.543 in. If the specimen necked down to a diameter 0.765 in, determine the percent reduction in area (round to the nearest whole %)
During a tensile test of Aluminum alloy whose initial diameter was 0.505-in and gage length was 2.0-in, the following data was recorded. Load Elongation (in.) Load Elongation (in.) 0.020 (1b) |(Ib) 14 000 2 310 0.00220 14 400 0.025 4 640 0.00440 14 500 0.060 6 950 0.00660 14 600 0.080 9 290 0.00880 14 800 0.100 11 600 0.0110 14 600 0.120 12 600 0.0150 13 600 Fracture a) Determine Stress and strain b) Draw the stress strain diagram c) Determine the following mechanical properties 1) Proportional limit, 2) Modulus of elasticity 3) Yield point 4) Ultimate strength 5) Rupture strength.
A of magnesium having a rectangular cross section of dimension 3.2 mm x 19.1 mm and a gauge length of 63.5 is pulled in tension. Use the load-elongation characteristics tabulated as follows to: Load (KN) Al (mm) 0.0 1.38 2.78 5.63 743 8.14 9,87 12.85 14,10 14.34 13.83 12,59 0.0 0.03 0.06 0.12 0.20 0.25 0.64 1.91 3,18 4.45 5.72 6.99 a) Plot the data as engineering stress versus engineering strain. b) Compute the modulus of elasticity. Determine the tensile strength of this alloy. Sace