A tensile test was performed on a metal specimen with a diameter of 1⁄2 inch and a gage length (the length over which the elongation is measured) of 4 inches. The data were plotted on a load-displacement graph, P vs. ∆L. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P y∆L 5 1392 kips yin. What is the modulus of elasticity?

A tensile test was performed on a metal specimen with a diameter of 1⁄2 inch and a gage length (the length over which the elongation is measured) of 4 inches. The data were plotted on a load-displacement graph, P vs. ∆L. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P y∆L 5 1392 kips yin. What is the modulus of elasticity?

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.4P: A tensile test was performed on a metal specimen with a diameter of 1 2 inch and a gage length (the...

See similar textbooks

Similar questions

The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
A tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.
A tensile test was performed on a metal specimen with a diameter of 1 2 inch and a gage length (the length over which the elongation is measured) of 4 inches. The dam were plotted on a load-displacement graph. P vs. L. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P/L =1392 kips/in. What is the modulus of elasticity?
A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.
5. A tensile test was done on a magnesium sample of original diameter and original length of 12mm 30mm respectively. The final length and diameter were 32.61mm and 11.74mm respectively. Plot the stress versus strain graph and determine: a. 0.2% proof stress b. Tensile strength c. % elongation d. % reduction e. Stress at fracture f. Modulus of Elasticity. 66 Force (N) Ext. 0.0112 0.0157 0.0199 0.0240 1.72 (mm) 177 327 462 797 1350 1720 2220 2690 2690 5.55 8.15 13.07 22.77 25.25
A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1/2 inch. the gage lenght ( the lenght over which the elongation is measured ) is 2 inches. for a load 13.5 kips, the elongation was 4.66x10^-3 inches. if the load is assumed to be with in the linear elastic range of the material , determine the modulus of elasticity
1.5-7 The data shown in the table were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2 in.² in area and a gage length (the length over which the elongation is measured) of 2.000 inches. d. Estimate the value of the proportional limit. e. Use the 0.2% offset method to determine the yield stress. Load (kips) 0 0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 ܩܙ ܘ 5.5 6.0 6.5 Elongation × 10³ (in.) 0 0.160 0.352 0.706 1.012 1.434 1.712 1.986 2.286 2.612 2.938 3.274 3.632 3.976 Load (kips) 7.0 7.5 8.0 8.5 9.0 9.5 10.0 10.5 11.0 11.5 12.0 12.5 13 Elongation × 10³ (in.) 4.386 4.640 4.988 5.432 5.862 6.362 7.304 8.072 9.044 11.310 14.120 20.044 29.106
The (G-E) diagram obtained in the tensile test performed on a metal sample with a diameter of 16 mm is as follows. The loads at points A, B and C and the elongation measured on l. 16 cm gauge length were determined as follows: B A B C Load (kgf) 4800 8400 7200 Elongation (mm) 0.192 28.8 38.4 a) Calculate the proportionality limit, modulus of elasticity, tensile strength, maximum uniform elongation, and contraction-elongation ratio of the metal. b) Since the measured diameter of the metal at break is 12 mm, find the constriction ratio and the actual stress at break.
The (G-E) diagram obtained in the tensile test performed on a metal sample with a diameter of 16 mm is as follows. The loads at points A, B and C and the elongation measured on l. 16 cm gauge length were determined as follows: B A B C Load (kgf) 4800 8400 7200 Elongation (mm) 0.192 28.8 38.4 c) Calculate the fracture work and the maximum elastic energy the metal rod can store. d) Find the cross-sectional area of a 6 m long rod made of this metal such that it can carry 12 tons of load with 2 times the safety of yield strength. How long does the rod extend under this load?
In a standard tensile test, an aluminum rod of 20-mm diameter is subjected to a tension force of P = 30 kN. Knowing that E = 70 GPa, and the change in diameter of the rod= 0.00955 mm, determine the poissons' ratio v. -20-mm diameter gage length=150 mm
In a standard tensile test, an aluminum rod of 20-mm diameter is subjected to a tension force of P- 30 kN. Knowing that E- 70 GPa, and the change in diameter of the rod- 0.00955 mm, determine the poissons' ratio v. 20n diateter gage length-150 0.33 O 0.6 0.29 O 0.35
A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1/2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elonga- tion was 4.66 x 10-3 inches. If the load is assumed to be within the linear elastic range of the material, determine the modulus of elasticity.