A steel specimen is tested in tension. The specimen is 25 mm wide by 5 mm thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 55 kN and fractured at 78 kN.a. Determine the tensile stresses at yield and at fracture.b. Estimate how much elongation would occur at 60% of the yield stress in a 50-mm gauge length.

A steel specimen is tested in tension. The specimen is 25 mm wide by 5 mm thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 55 kN and fractured at 78 kN.a. Determine the tensile stresses at yield and at fracture.b. Estimate how much elongation would occur at 60% of the yield stress in a 50-mm gauge length.

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.6P: The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular...

See similar textbooks

Similar questions

The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.
A tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.
A steel specimen is tested in tension. The specimen is 25 mm wide by 12.5 mm thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 160 kN and fractured at 214 kN. a. Determine the tensile stress at yield and at fracture. b. If the original gauge length was 100 mm, estimate the gauge length when the specimen is stressed to 1/2 the yield stress.
A steel specimen is tested in tension. The specimen is 1 in. wide by 0.5 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 36 kips and fractured at 48 kips.a. Determine the tensile stress at yield and at fracture.b. If the original gauge length was 4 in., estimate the gauge length when the specimen is stressed to 1/2 the yield stress.
3. A steel specimen is tested in tension. The specimen is 1.0 in. wide by 0.25 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 12.5 kips and fractured at 17.5 kips. а. Determine the tensile stresses at yield and at fracture. b. Estimate how much increase in length would occur at 60% of the yield stress in a 2-in. gauge length
A steel specimen is tested in tension. The specimen is 1.0 in. wide by 0.25 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 12.5 kips and fractured at 17.5 kips. a. Determine the tensile stresses at yield and at fracture. b. Estimate how much increase in length would occur at 60% of the yield stress in a 2-in. gauge length. Step-by-step solution: Step 1 of 4 Given that: Width of the specimen, b = 1 in Thickness of the specimen, t = 0.25 in Yield load on the specimen, Py = 12.5 kips Fracture load on the specimen, Pf = 17.5 kips Gauge length, L = 2 in Percentage of yield stress = 60%
A steel specimen is tested in tension. The specimen is 1.0 in. wide by 0.25 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 12.5 kips and fractured at 17.5 kips.a. Determine the tensile stresses at yield and at fracture.b. Estimate how much increase in length would occur at 60% of the yield stress in a 2-in. gauge length.
A steel specimen is tested in tension. The specimen is 2 in. wide by 2.3 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 30 kips and fractured at 40 kips. a) Determine the tensile stress at yield and fracture; b) If the original gauge length was 4 in., estimate the gauge length when the specimen is stressed to 2 the yield stress.
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At the fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the proportional limit, modulus of elasticity (i.e the slope of initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percentage reduction in area Tensile-Test Data Load(kN) Elongation (mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
A specimen of steel 20 mm diameter with a gauge length of 200 mm is tested to destruction. It has an extension of 0.25 mm under a load of 80 kN and the load at elastic limit is 102 kN. The maximum load is 130 kN. The total extension at fracture is 56 mm and diameter at neck is 15 mm. Find . The stress at elastic limit. • Young's modulus. . Percentage elongation. Percentage reduction in area. Ultimate tensile stress. .
During a tensile test on a specimen of steel the following data was recorded diameter of the specimen is 6.6mm,gage length 5mm,elongation of a load of 6.0KN is 0.043mm.load at yield point is 9.7KN at failure is 14.2KN ,reduction of the area is 45 percent. Calculate Young's modulus of elasticity, the yield stress and the ultimate stress