A steel plate, which has a fracture toughness in a plane strain state of 83 MPavm, is alternately loaded in tension at 750 MPa and in compression at 20 MPa. The plate must survive 15 years with the stress applied at a frequency of once every 3 min. Calculate the constant C of the material if n=2.8 . Assume that the geometric factor f=1 for all your imperfections. Internal imperfections have a size of 0.0015 mm

A steel plate, which has a fracture toughness in a plane strain state of 83 MPavm, is alternately loaded in tension at 750 MPa and in compression at 20 MPa. The plate must survive 15 years with the stress applied at a frequency of once every 3 min. Calculate the constant C of the material if n=2.8 . Assume that the geometric factor f=1 for all your imperfections. Internal imperfections have a size of 0.0015 mm

Mechanics of Materials (MindTap Course List)

9th Edition

ISBN:9781337093347

Author:Barry J. Goodno, James M. Gere

Publisher:Barry J. Goodno, James M. Gere

Chapter1: Tension, Compression, And Shear

Section: Chapter Questions

Problem 1.6.7P: A wine of length L = 4 ft and diameter d = 0.125 in. is stretched by tensile forces P = 600 lb. The...

See similar textbooks

Similar questions

Determine the strain energy per unit volume (units of psi) and the strain energy per unit weight (units of in ) that can be stored in each or the materials listed in the accompanying table, assuming that the material is stressed to the proportional limit. DATA FOR PROBLEM 2.7-5 Material Weight Density (lb/in3) Modulus of Elasticity (ksi) Proportional Limit (psi) Mild sleel 0.284 30,000 36,000 Tool steel 0.284 30,000 75,000 Aluminum 0.0984 10,500 60,000 Rubber (soft) 0.0405 0.300 300
A wine of length L = 4 ft and diameter d = 0.125 in. is stretched by tensile forces P = 600 lb. The wire is made of a copper alloy having a stress-strain relationship that may be described mathematically by =18,0001+30000.03(=ksi) in which is nondimensional and has units of kips per square inch (ksi). (a) Construct a stress-strain diagram for the material. (bj Determine the elongation, of the wire due to the Forces P. (c) IF the forces are removed, what is the permanent set of the bar? (d) If the forces are applied again, what is the proportional limit?
The data shown in the accompanying table are From a tensile test of high-strength steel. The test specimen has a diameter of 0.505 in. and a gage length of 2.00 in. (see figure for Prob. 1.5-3). At fracture, the elongation between the gage marks is 0.12 in. and the minimum diameter is 0.42 in. Plot the conventional stress-strain curve for the steel and determine the proportional limit, modulus of elasticity (the slope of the initial part of thestress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 2.00 in., and percent reduction in area. TENSILE-TEST DATA FOR PROB. L.5-7 Laid (lb) Elongation (in) 1000 0.0002 2000 0.0006 6000 0.0019 10,000 0.0033 12,000 0.0039 12,900 0.0041 13,400 0.0047 13,600 0.0054 13,800 0.0063 14,000 0.0090 14,400 0.0102 15,200 0.0130 16,800 0.0230 18,400 0.0336 20,000 0.0507 22,400 0.1108 22,600 Fracture
Tensile test specimens are extracted from the "X" and "y" directions of a rolled sheet of metal. "x" is the rolling direction, "y" is transverse to the rolling direction, and "z" is in the thickness direction. Both specimens were pulled to a longitudinal strain = 0.15 strain. For the sample in the x-direction, the width strain was measured to be ew= -0.0923 at that instant. For the sample in the y-direction, the width strain was measured to be gw=-0.1000 at that instant. The yield strength of the x-direction specimen was 50 kpsi and the yield strength of the y-direction specimen was 52 kpsi. Determine the strain ratio for the x direction tensile test specimen. Determine the strain ratio for the y-direction tensile test specimen. Determine the expected yield strength in the z-direction. Give your answer in units of kpsi (just the number). If the sheet is plastically deformed in equal biaxial tension (a, = 0, to the point where & = 0.15, calculate the strain, 6, that would be expected.
The data below are for a thin steel wire suitable for use as a guitar string. Ultimate tensile stress: 1.8 x 109 Pa Young Modulus: 2.2 x 1011 Pa Cross-sectional area: 2.0 x 10-7 m2 In a tensile test, a specimen of the wire, of original length 1.5 m, is stretched until it breaks. Assuming the wire obeys Hooke’s law throughout, calculate the extension of the specimen immediately before breaking.
In the attached picture there is a sketch of a socket wrench. Assume the wrench is held at a fixed point “A”. The yield stress of the material is known to be 500 MPa. Answer the questions below Describe the stresses at point “A” and their causes and calculate the stresses. Determine the factor of safety against yield assuming the Tresca yield criteria. Determine the factor of safety against yield assuming the von Mises yield criteria using both principal stresses and “Cartesian” stresses. Do your values match or not, and is this expected? Explain. Do the calculated values make sense with the respect to the Tresca value? Explain, why or why not?
tensile test is performed to determine the parameters strength constant C and strainrate sensitivity exponent m for a certain metal. The temperature at which the test is performed = 500°C. At a strain rate = 10/s, the stress is measured at 140 MPa; and at a strain rate = 150/s, the stress = 280 MPa. (a) Determine C and m. (b) If the temperature were 600°C, what changes would you expect in the values of C and m?
Sketch a tensile member with (a) a rectangular crosssection, (b) a solid circular cross section, and (c) a circulartubecross section, and label the dimensions symbolically (e.g.,label the radius for the solid circular case). For each member, write out the definition of engineering stress in terms of the actual dimensions of the component. If therectangular member has dimensions of width and thicknessequal to 1 cm 0.3 cm, what would be the radius of a solidcircular member such that the stress is equal for an equaltensile load? If a tube has an outer radius equal to that ofthis same solid cylinder, what is the maximum inner radiussuch that the stress does not exceed 200% of the stress inthe solid cylinder?
Consider a metal rod with a critical resolved shear stress of 40 MPa for a specific crystallographic plane (hkl). The angle between the normal to the plane and the applied force is 30 degrees, and the angle between the slip direction and the force is 15 degrees. Two force levels of F1 = 75 N and F2 = 40 N is applied. The cross-sectional area of the rod is 1 mm^(2). Will the slip initiate at the two force levels? Select one: O a. F1: Yes, F2: No O b. F1: Yes, F2: Yes O C. F1: No, F2: Yes d. F1: No, F2: No
A tensile test is performed to determine the strength constant C and strain-rate sensitivityexponent m for a certain metal. The temperature at which the test is performed is 500ºC. At astrain rate of 12/s, the stress is measured at 160 MPa, and at a strain rate of 250/s, the stress is300 MPa. Determine C and m.
Consider a metal rod with a critical resolved shear stress of 40 MPa for a specific crystallographic plane (hkl). The angle between the normal to the plane and the applied force is 30 degrees, and the angle between the slip direction and the force is 15 degrees. Two force levels of F1 = 75 N and F2 = 40 N is applied. The cross-sectional area of the rod is 1 mm^(2). Will the slip initiate at the two force levels? Select one: a. F1: Yes, F2: No b. F1: No, F2: No OC. F1: Yes, F2: Yes Od. F1: No, F2: Yes
A ceramic part for a jet engine has a yield strength of 66,215 psi and a plane strain fracture toughness of 5000 psi (in) ¾. To be sure that the part does not fail, we plan to assure that the maximum applied stress is only one-third the yield strength. We use a nondestructive test that will detect any internal flaws greater than 0.05 in. Iong. Assuming that f = 1.2 , does our non- destructive test have the required sensitivity? Type 1 for yes and O for no.