A steel bar is held by two fixed supports as shown in the figure and is subjected to an increase of temperature AT = 100°C. If the coefficient of thermal expansion and Young's modulus of elasticity of steel are 11×10C and 200GPa, respectively, the magnitude of thermal stress (in MPa) induced in the bar is

A steel bar is held by two fixed supports as shown in the figure and is subjected to an increase of temperature AT = 100°C. If the coefficient of thermal expansion and Young's modulus of elasticity of steel are 11×10C and 200GPa, respectively, the magnitude of thermal stress (in MPa) induced in the bar is

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 6.1P

See similar textbooks

Similar questions

A 2 m long axially loaded mild steel rod of 8 mm diameter exhibits the load-displacement (P -8) behavior as shown in the figure. 14000 12000 310000 8000 6000 4000 2000 1 2 3 4 5 7 10 Displacement 8(mm) Assume the yield stress of steel as 250 MPa. The complementary strain energy (in N-mm) stored in the bar up to its linear elastic behavior will be Axial Load, P(kN)
A bronze rod is rigidly attached between an aluminum rod and a steel rod as shown in the figure below. Axial loads are applied at the positions indicated. a) Find the maximum value of P that will not exceed a stress in steel of 140 MPa, in bronze of 100 MPa, or in aluminum of 90 MPa. b) Determine the deformation of the bronze rod if the value of P is 22.50 KN. The moduli of elasticity are 200 GPa for steel, 80 GPa for bronze and 70 GPa for aluminum.
In a steel railroad, the 12 meters long rails are laid with a clearance of 5 mm at a temperature of 20 degrees centigrade. The modulus of elasticity of steel is 200 GPa. a) At what temperature will the rails just touch if the coefficient of linear expansion is 11.7x10^-6/°C.? b) Determine the stress in the rails at 65 °C
Axial Load, P(kN) A 2 m long axially loaded mild steel rod of 8 mm diameter exhibits the load-displacement (P -8) behavior as shown in the figure. 14000 12000 10000 8000 6000 4000 2000 0 1 2 7 8 9 10 3 4 5 6 Displacement 8(mm) Assume the yield stress of steel as 250 MPa. The complementary strain energy (in N-mm) stored in the bar up to its linear elastic behavior will be
A brass wire of diameter d = 2.33 mm is stretched tightly between rigid supports so that the tensile force is T = 93 N (see figure). T The coefficient of thermal expansion for the wire is 19.5 x 106/°c, and the modulus of elasticity is E = 110 GPa. (a) What is the maximum permissible temperature drop (in °C) if the allowable shear stress in the wire is 60 MPa? (Enter the magnitude.) °C (b) At what temperature change (in °C) does the wire go slack? °C
Strain = 600 Stress = Strain = 500 Stress = 400 500 300 400 300 200 200 100 100 0.000 0.002 0.004 0.006 Strain 0.00 0.04 0.08 0.12 0.16 0.20 Strain Stress (MPa)
1.4-7 The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13 mm and a gage length of 50 mm (see figure for Prob. 1.4-3). At fracture, the elongation between the gage marks was 3.0 mm and the minimum diameter was 10.7 mm. Plot the conventional stress-strain curve for the steefor the steel and determine the proportional limit, modulus of elastics of elastic- ity (i.e., the slope of the initial part of the stress-strain,tress-strain curve), yield stress at 0.1% offset, ultimate stress, percent, elongation in 50 mm, and percent reduction in area. 'ess, percent area. TENSILE-TEST DATA FOR PROB. 1.4-7 Elongation (mm) 0.005 0.015 0.048 Load (kN) 5 10 30 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
Two triangular wedges are glued together as shown in the figure. The stress acting normal to the interface, o, is MPa. 100 MPa 100 MPa on 45% 100 MPa -100 MPa
An aluminum alloy [E = 67 GPa; ν = 0.33; α = 23.0 × 10–6/°C] plate is subjected to a tensile load P. The plate has a depth of d = 225 mm, a cross-sectional area of A = 5100 mm2, and a length of L = 4.1 m. The initial longitudinal normal strain in the plate is zero. After load P is applied and the temperature of the plate has been increased by ΔT = 63°C, the longitudinal normal strain in the plate is found to be 2900 με. Determine: (a) the magnitude of load P. (b) the change in plate depth Δd.
A metal bar of length 100 mm is inserted between increased by 10°C. If the coefficient of thermal expansion is 12 × 106 per °C and the Young's two rigid supports and its temperature is increased by 10°C. If the coefficient of thermal expansion is 12 × 10-6 per °C and the Youna's modulus is 2 x105 MPa, the stress in the bar is (a) zero (c) 24 MPa (b) 12 MPa (d) 2400 MPa
Strain, Deformation and Thermal Stress Steel Rod A = 600 mm? L= 4.0 m E= 200 GPa Aluminum Rod A = 900 mm? a = 11.70 um/(m°C) L= 3.0 m E = 70 GPa %3D 2. Determine the stress in a = 23 um/(m°C) the aluminum rod if the 3 m 3 m 3 m temperature of steel is increased by 40 degrees A D Celsius at the same time the 50 KN load is applied to the beam. F = 50 KN Strain, Deformation and Thermal Stress · 600 KN The 600 KN load is horizontal when it is first 1.00 m applied to the columns. After some time, the 600 KN load is still horizontal after deformation took place for all the columns. If the diameter of all the columns is 50 mm. Modulus of elasticity of steel is 200 GPa and modulus of elasticity of bronze is 100 GPa. Compute the strain of the steel. 0.25 m Bronze Steel Bronze
A steel rod having a cross-sectional area of 0.002 sq. m. and length of 1.5 m. is attached to unyielding supports. If the temperature falls 60 degrees Celsius, the modulus of elasticity of steel is 200 x 109 N/m2, and the coefficient of linear expansion is 11.5 x 10–6 per degree Celsius, finda. the deformation due to the temperature drop in mm, andb. the force exerted by the rods on the supports in kN..