Part D please A cylindrical 4135 cold-rolled steel workpiece has anupsetting load applied at room temperature using anopen-die forging with flat dies to a new height, ha =50 mm, as shown below. The initial diameter is do220 mm, the initial height is ho = 180 mm.4135 cold-rolledMPa=1100Psi= 16000Strain hardening exponent, n = 0.14A) What is the diameter of the forging at the end ofthe forging stroke?=B) What is the longitudinal true strain of the forgingat the end of the forging stroke?C) What is the true (flow) stress required in thematerial at the end of the forging stroke?D) Using the average pressure formula, what is thecorresponding coefficient of friction if the upsettingforce at the end of the stroke is 170 MN?

The initial diameter is The initial height is The final height is The strain-hardening exponent is…

Answered: A cylindrical 4135 cold-rolled steel…

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

I need only part d) plz answer in 30min A 4-in-thick aluminum slab is 10 in wide and 100 in long. It is reduced in one pass in a two-high rolling mill to a thickness = 3.5 in. The roll rotates at a speed = 12 rev/min and has a radius = 20 in. The aluminum has a strength coefficient = 25,000 lb/in2 and a strain hardening exponent = 0.20. Determine the (a) roll force, (b) roll torque, and (c) power required to accomplish this operation, d) Estimate the GHG emission in an hour for the rolling operation.
Q3- B/A round disk of 150 mm diameter is to be blanked from a strip of 3.2 mm half hard cold-rolled steel whose shear strength =300mpa. Determine a-the appropriate punch and die diameter and b-blanking force Hints a 0.075
The team is extruding a billet that is 80 mm long with diameter of 40 mm is directly to a diameter of 20 mm. The extrusion die has a die angle of 75°, see Figure 1. For the work metal, K = 600 MPa and n = 0.25. In the Johnson extrusion strain equation, a = 0.8 and b = 1.4. Remaining billet length 75 Ram pressure, p Do Figure 1: Extrusion process. Determine the following design parameters: (a) Extrusion strain (b) Ram pressure at L = 80, 40, and 10 mm. (c) Draw the relationship between the ram pressure and billet length and discuss the results. What are your recommendations to decrease the required ram pressure?
For the drawing operation of Problem 3 (Cup Drawing), the tensile strength of the sheet metal (low-carbon steel) = 300 MPa and yield strength = 175 MPa. The die corner radius = 5 mm. Determine: a. the drawing force and, b. the blank-holding force blank diameter =150mm punch diameter= 100mm Equations used Db F = = πD,₁t (TS) (D₂₂ - 0.7) Dp F₁ = 0.015Yπ{D² – (D₂ + 2.2t + 2Ra)
Ex: Wire is drawn through a draw die with entrance angle 15°. Starting diameter is 2.5 mm and final diameter 2.0 mm. The coefficient of friction at the work-die interface 0.07. The metal has a strength coefficient K=205 MPa and a strain- hardening exponent n = 0.20. Determine the draw stress and draw force in this operation.
Wire is drawn through a draw die with entrance angle a= 17°. Starting diameter is 3.0 mm and final diameter = 2.4 mm. The coefficient of friction at the work-die interface = 0.08. The metal has a strength coefficient K = 205 MPa and a strain-hardening exponent n = draw force in this operation. Why are multiple passes usually required to achieve the desired reduction? (Hint: Observe the draw stress value found in this question) 0.20. Determine the draw stress and Lubricant box Initial wire stock (in coil form) Multiple pass/draft drawing Draw die V2, F V3, F shown in figure. Capstan drum (holds multiple loops of wire) (1) (2) (3)
Figure 1. shows the rolling operation. Determine the position bn. of the neutral point? Neglect front and back tensions. Additional data: Hardened steel 0.04 μm and rolling temperature -190°C. rolls, surface roughness of the rolls 0.3 in. 1-5t/s R=4 in. Fig:1 0.1 in. 7 ft/s
A cylindrical part with initial diameter of 45 mm and the initial height of 40 mm is upset forged in an open die to a height = 25 mm. The strength coefficient is 650 MPa and strain- hardening exponent is 0.12. Qa =1.11 (Qa takes into account both friction and workpiece geometry). Calculate the force required for upsetting this part at room temperature. O 1786 kN O 1648 kN O 1247 kN O 1109 kN O none of them
The team performs a cold heading operation to produce the head on a steel nail. The strength coefficient for this steel is K = 550 MPa, and the strain hardening exponent n = 0.24. Coefficient of friction at the die- work interface = 0.10. The wire stock out of which the nail is made is 4.75 mm in diameter. The head is to have a diameter = 9.5 mm and a thickness = 1.5 mm. (a) What length of stock must project out of the die in order to provide sufficient volume of material for this upsetting operation? (b) Compute the maximum force that the punch must apply to form the head in this open-die operation. Discuss the result?
0/ Two thick slabs of 300mm each, the first one is used in cold rolling where μ=0.08 while the second is used in cold rolling where µ-0.5. The mill roll diameter in each case is the same as 600mm. Determine the max draft (reduction) in both cases. Discuss the wide difference in results.
In hot rolling process, the following data was collected: N=20rpm, R=20cm, to-40mm, t-35mm, C=415MPA, m=0.02, w=60cm, one pass rolling. Find Froll, T and Power.
Calculate (1) die pressure distribution and (2) forging force for plane strain forging (open die forging). Assume yield strength of the material is Y, and yielding criterion is von Mises. ho 2Lo h Forged to 2L xdx L 'x+value Note: Assume Zo Constant Plane strain Die pressure distribution h L L Die pressure distribution h MATERIAL L dx -(-1) Friction Hill Y L When 0; =Y P=Y' = Calculate forging force X L dF elemental volume Average pressure

SEE MORE QUESTIONS

Recommended textbooks for you

Elements Of Electromagnetics

Mechanical Engineering

ISBN:

9780190698614

Author:

Sadiku, Matthew N. O.

Publisher:

Oxford University Press

Mechanics of Materials (10th Edition)

Mechanical Engineering

ISBN:

9780134319650

Author:

Russell C. Hibbeler

Publisher:

PEARSON

Thermodynamics: An Engineering Approach

Mechanical Engineering

ISBN:

9781259822674

Author:

Yunus A. Cengel Dr., Michael A. Boles

Publisher:

McGraw-Hill Education

Elements Of Electromagnetics

Mechanical Engineering

ISBN:

9780190698614

Author:

Sadiku, Matthew N. O.

Publisher:

Oxford University Press

Mechanics of Materials (10th Edition)

Mechanical Engineering

ISBN:

9780134319650

Author:

Russell C. Hibbeler

Publisher:

PEARSON

Thermodynamics: An Engineering Approach

Mechanical Engineering

ISBN:

9781259822674

Author:

Yunus A. Cengel Dr., Michael A. Boles

Publisher:

McGraw-Hill Education

Control Systems Engineering

Mechanical Engineering

ISBN:

9781118170519

Author:

Norman S. Nise

Publisher:

WILEY

Mechanics of Materials (MindTap Course List)

Mechanical Engineering

ISBN:

9781337093347

Author:

Barry J. Goodno, James M. Gere

Publisher:

Cengage Learning

Engineering Mechanics: Statics

Mechanical Engineering

ISBN:

9781118807330

Author:

James L. Meriam, L. G. Kraige, J. N. Bolton

Publisher:

WILEY

SEE MORE TEXTBOOKS

A cylindrical 4135 cold-rolled steel upsetting load applied at room tem Open-die forging with flat dies to a 50 mm, as shown below. The initia