A cylinder with a 6.0 in. diameter and 12.0 in. length is put under a compres- sive load of 150 kips. The modulus of elasticity for this specimen is 8,000 ksi and Poisson's ratio is 0.35. Calculate the final length and the final diameter of this specimen under this load assuming that the material remains within the linear elastic region. 1.5

A cylinder with a 6.0 in. diameter and 12.0 in. length is put under a compres- sive load of 150 kips. The modulus of elasticity for this specimen is 8,000 ksi and Poisson's ratio is 0.35. Calculate the final length and the final diameter of this specimen under this load assuming that the material remains within the linear elastic region. 1.5

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

Asap 20 min
Two samples of a metal with an elastic modulus of 130 GPa, diameter 10 mm, and gauge length 100 mm undergo creep at 600°C according to the table below: a) Calculate the extension due to elastic deformation for each sample. b) Calculate the steady state creep rate for each sample. c) Creep occurs according to:
Please provide correct solution
a. Calculate the ductility of the sample as a percentage (%) b. Calculate the stress required to create a neck in the sample, in MPa.
i need the answer quickly
A tensile force of 20 kN is applied to a specimen with a gage length of 50mm. It is then noted that the distance between the gage marks became 50.122mm. a,) What is the modulus of elasticity of the specimen if its diameter is 10mm? b.) What is the axial stress of the specimen?Note: Please show detailed solutions with illustrations.
A sample of metal having a rectangular cross-section; a width of 10.00 in. and a thickness of 0.25 in. is cold worked to a final width of 9.50 and a thickness of 0.20 in. If the plastic behavior of this sample is given by d=100,000€0.5 psi, determine the new yield strength of the sample after cold working.
Mcq
#3 solution?
I. Problem Solving: Answer what is being required. Show you complete solution. 1. Compute the tensile stress from the value acquired from the experiment if the breaking load is 105KN. The diameter of the specimen is 150mm and the height is 300mm. 2. Compute the flexural stress of the sample specimen if its dimension is 150mm x 150mm x 500mm in a 3 point loading. The effective length is 400mm. The specimen failed at 44,300N in the middle third. 3. Compression test was applied to a certain type of wood. Compute the stress based on the following dimensions. The grains are parallel with the length. а. Compression Test Dimension (mm) Load (N) Compressive stress (МРa)
I. Problem Solving: Answer what is being required. Show you complete solution. 1. Compute the compressive stress for the respective ages of the specimen. The diameter of the specimens is 150mm and the height is 300mm. Load (N) 176,000 Stress (MPa) Age 7days 14 days 28 days 252,000 340,000 2. Compute the tensile stress from the value acquired from the experiment if the breaking load is 105KN. The diameter of the specimen is 150mm and the height is 300mm. 3. Compute the flexural stress of the sample specimen if its dimension is 150mm x 150mm x 500mm in a 3 point loading. The effective length is 400mm. The specimen failed at 44,300N in the middle third. 4. Compression test was applied to a certain type of wood. Compute the stress based on the following dimensions. The grains are parallel with the length. а. Dimension (mm) Load (N) Compressive stress (МРа) Compression Test
A metal specimen with 20 mm diameter and 100 mm gauge length is loadedelastically with 5 kN and elongates 0.8 mm. Its diameter under this load is 19.95 mm. Calculate:a) the Bulk Modulus, Kb) the Shear Modulus, G