A stainless-steel rod 16mm in diameter and 300mm long is put under a tensile load of 250 kN. Assuming that the modulus of elasticity for this specimen is 250,000 MPa and the final diameter is 15.96 mm. Calculate the final length, in mm, and the Poisson’s ratio of this specimen under this load assuming that the material remains within the linear elastic region.

A stainless-steel rod 16mm in diameter and 300mm long is put under a tensile load of 250 kN. Assuming that the modulus of elasticity for this specimen is 250,000 MPa and the final diameter is 15.96 mm. Calculate the final length, in mm, and the Poisson’s ratio of this specimen under this load assuming that the material remains within the linear elastic region.

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 6.3P: Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2...

See similar textbooks

Similar questions

The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.
Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.
The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
A)Define poison's ratio B)A tensile-test piece of diameter 10mm is subjected to an axial force of 15KN.If E for the material is 207KN/mm^2 and poison's ratio is 0.29, calculate the lateral strain and the change in diameter.
A steel rod, 12mm in diameter and 150mm long was subjected to a tensile test. After the test, the length increases to 150.40mm. The material remains within the linear elastic region and its modulus of elasticity is 200,000 MPa. Determine the force, in Newton (N), applied to the test. different solution please
An applied torque results in a shear strain (y) of 3.75 x 103 in a solid circular steel shaft. At this strain, a portion of the shaft cross- section yields as shown in Figure 2. Determine the magnitude of the applied torque. Take G = 80 GPa and yy = 2.8125 x %3D 10-3 FIGURE 2: Plastic zone 50 mm 200 mm Elastic core
Problem 11. [Concepts: Calculating stress from internal forces, nonlinear stress-strain response, elongation from strain.] Acetal plastic has a stress-strain diagram as shown. a) Determine the yield strength assuming a 0.2% offset. b) If a bar of this material has a length of 3 ft and cross-sectional area of 0.875 in², and is subjected to an axial load of 2.5 kip, determine its elongation. c) Determine the modulus of toughness just before it fractures if failure occurs at a = 0.12. σ (psi) a = 9.5(10³) €¹/3 € (in./in.)
A cylindrical specimen of stainless steel having a diameter of 12.8 mm (0.505 in.) and a gauge length of 50.800 mm (2.000 in.) is pulled in tension. Use the load–elongation characteristics shown in the following table: (see attached picture) (a) Plot the data as engineering stress versus engineering strain. (b) Compute the modulus of elasticity. (c) Determine the yield strength at a strain offset of 0.002.(d) Determine the tensile strength of this alloy.e) What is the approximate ductility, in percent elongation? (f) Compute the modulus of resilience.
A steel alloy specimen having a rectangular cross section of dimensions 19.1 mm x 3.1 mm (0.7520 in. × 0.1220 in.) has the stress-strain behavior shown in the Animated Figure 6.22b. If this specimen is subjected to a tensile force of 98290 N (22100 Ib;) then (a) Determine the amount of elastic strain induced. (b) Determine the amount of plastic strain induced. (c) If its original length is 610 mm, what will be its final length after this force is applied and then released? The elastic modulus for steel is 207 GPa. (a) i (b) i (c) i mm
A steel wire with a diameter of d = 1/16” is bent around a cylindrical drum with a radius ofR = 36”.(a) Determine the maximum normal strain in the wire.(b) What is the minimum acceptable radius of the drum if the maximum normal strain mustremain below yield? Consider an elastic modulus of 30000 ksi and yield stress of 100ksi.(c) If R = 36”, what is the maximum acceptable diameter of the wire if the maximum normalstrain must remain below yield?
A steel specimen is tested in tension. The specimen is 25 mm wide by 12.5 mm thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 160 kN and fractured at 214 kN. a. Determine the tensile stress at yield and at fracture. b. If the original gauge length was 100 mm, estimate the gauge length when the specimen is stressed to 1/2 the yield stress.
A specimen is originally 300mm long and has a diemter of 11mm and it subjected to a force of 4kN. When the force is increased from 4kN to 7.5kN the specimen elongates 0.225mm. Determine the modulus of elasticity for the material if it remains linear elastic.