A billet 100 mm long and 30 mm in diameter is to be extruded in a direct extrusion operation with extrusion ratio r, = 3.5. The extrudate has a round cross section. The die angle (half angle) = 60°. The work metal has a strength coefficient = 720 MPa, and strain hardening exponent = 0.17. Use the Johnson %3D formula with a = 0.8 and b= 1.2 to estimate extrusion strain. Determine the following: 1. Diameter of the extrudate = mm 2. Butt volume = mm3 3. Actual extrudate length = mm 4. The pressure applied to perform the extrusion process = MPa 5. Ram force =

A billet 100 mm long and 30 mm in diameter is to be extruded in a direct extrusion operation with extrusion ratio r, = 3.5. The extrudate has a round cross section. The die angle (half angle) = 60°. The work metal has a strength coefficient = 720 MPa, and strain hardening exponent = 0.17. Use the Johnson %3D formula with a = 0.8 and b= 1.2 to estimate extrusion strain. Determine the following: 1. Diameter of the extrudate = mm 2. Butt volume = mm3 3. Actual extrudate length = mm 4. The pressure applied to perform the extrusion process = MPa 5. Ram force =

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The team is extruding a billet that is 80 mm long with diameter of 40 mm is directly to a diameter of 20 mm. The extrusion die has a die angle of 75°, see Figure 1. For the work metal, K = 600 MPa and n = 0.25. In the Johnson extrusion strain equation, a = 0.8 and b = 1.4. Remaining billet length 75 Ram pressure, p Do Figure 1: Extrusion process. Determine the following design parameters: (a) Extrusion strain (b) Ram pressure at L = 80, 40, and 10 mm. (c) Draw the relationship between the ram pressure and billet length and discuss the results. What are your recommendations to decrease the required ram pressure?
A 3in long and 1in diameter billet is extruded in a direct extrusion operation with an rx = 4.0. The extrusion has a cross section. The angle of the die (half angle) is 90o. The work metal has a resistance coefficient of 60ksi and a strain hardening exponent of 0.18. Use Johnston's formula with a = 0.8 and b = 1.5 to estimate the extrusion stress. Determine the pressure applied to the end of the billet when the piston moves forward.
A cylindrical 4135 cold-rolled steel workpiece has an upsetting load applied at room temperature using an open-die forging with flat dies to a new height, ha = 50 mm, as shown below. The initial diameter is do = 220 mm, the initial height is ho = 180 mm. 4135 cold-rolled MPa=1100 Psi= 16000 Strain hardening exponent, n = 0.14 A) What is the diameter of the forging at the end of the forging stroke? B) What is the longitudinal true strain of the forging at the end of the forging stroke? C) What is the true (flow) stress required in the material at the end of the forging stroke? D) Using the average pressure formula, what is the corresponding coefficient of friction if the upsetting force at the end of the stroke is 170 MN?
A direct extrusion operation the cross section shown in Figure is produced from a copper billet whose diameter 225mm and length = 500 mm. In the flow curve for copper, the strength coefficient = 400 MPa and strain hardening exponent = 0.30. In the Johnson strain equation, a = 0.8 and b = 1.5. Determine: 1. The extrusion ratio, 2. The shape factor, 3. The force required to drive the ram forward during extrusion at the point in the process when the billet length remaining in the container = 325 mm ,4.The length of the extruded section at the end of the operation if the volume of the butt left in the container is 225,000 mm3. * 100
A tube with outer diameter i5mm and inner diameter 10mm, is to be manufactured by direct extrusion. The billet has a diameter of Do and a length of 200mm. The product is extruded at a speed Vf Assume deformation efficiency 80% and material follows O =110(7) N / mm The extrusion pressure and power are 20 MPa and 300KW, respectively. Calculates: c) Extrusion force in KN? d) The speed Vf? e) The tube final length? ) If the power cost is 2 SR/KW.Hr what is the production cost of producing 50 bars having 2-meters length each from the same cross-section?
The team performs a cold heading operation to produce the head on a steel nail. The strength coefficient for this steel is K = 550 MPa, and the strain hardening exponent n = 0.24. Coefficient of friction at the die- work interface = 0.10. The wire stock out of which the nail is made is 4.75 mm in diameter. The head is to have a diameter = 9.5 mm and a thickness = 1.5 mm. (a) What length of stock must project out of the die in order to provide sufficient volume of material for this upsetting operation? (b) Compute the maximum force that the punch must apply to form the head in this open-die operation. Discuss the result?
Calculate (1) die pressure distribution and (2) forging force for plane strain forging (open die forging). Assume yield strength of the material is Y, and yielding criterion is von Mises. ho 2Lo h Forged to 2L xdx L 'x+value Note: Assume Zo Constant Plane strain Die pressure distribution h L L Die pressure distribution h MATERIAL L dx -(-1) Friction Hill Y L When 0; =Y P=Y' = Calculate forging force X L dF elemental volume Average pressure
A billet 100 mm long and 40 mm diameter is to be extruded in a direct extrusion with final diameter of product 32 mm. The semi die angle is 60°. The work metal has a strength coefficient 500 Map, and strain hardening 0.2 use the Johnson formula with a=0.8 and b=1.45 to estimate the extrusion strain. Determine the pressure applied to the end of the billet as the ram moves forward.
Wire is drawn through a draw die with entrance angle a= 17°. Starting diameter is 3.0 mm and final diameter = 2.4 mm. The coefficient of friction at the work-die interface = 0.08. The metal has a strength coefficient K = 205 MPa and a strain-hardening exponent n = draw force in this operation. Why are multiple passes usually required to achieve the desired reduction? (Hint: Observe the draw stress value found in this question) 0.20. Determine the draw stress and Lubricant box Initial wire stock (in coil form) Multiple pass/draft drawing Draw die V2, F V3, F shown in figure. Capstan drum (holds multiple loops of wire) (1) (2) (3)
An indirect extrusion operation produces the cross-section shown in Figure 1 (Dimensions in cm) from an aluminum alloy (annealed) billet whose diameter is 300 mm and length of 500 mm. In the Johnson strain equation, a=0.8 and b=1.2 1.1 calculate shape factor of the product 1.2 If the butt left in the container at the end of the stroke is 25 mm thick, what is the (5)length of the extruded section?
A direct extrusion operation produces a product with a 20 mm x 60 mm cross sectional area from a brass billet whose diameter = 125 mm and length = 350 mm. The flow curve parameters of the brass are K = 700 MPa and n = 0.35. In the Johnson strain equation, a = 0.7 and b = 1.4. Determine (a) the extrusion ratio, (b) the shape factor, (c) the force required to drive the ram forward during extrusion at the point in the process when the billet length remaining in the container = 300 mm, and (d) the length of the extruded section at the end of the operation if the volume of the butt left in the container is 600,000 mm3
During a direct extrusion process for a billet with 5 in long and diameter 2.5 in to 1.6 in. For the work metal, strength coefficient is 75000 Ib/in, and strain hardening exponent is 0.4, also the die angle of extrusion is 90. In Johnson extrusion strain equation a = 0.8, and b= 1.5. Determine: (a) extrusion ratio (b) true strain (c) extrusion strain, and (d) ram pressure at length 5, 4.2, 2.3,1.5,and 0 in.