M 1:AI. 3,O photo_2021-02-1..->200streas(MPa)10050strainFrom the tensile stress-strain behavior fer thebrass specimen d the diamcter is 12-8 mm Calculatethe faibuding :-|- The Yield stress.2-Modulus of elasticity.3 - The Tensile strength .II

1- The yield stress - The yield stress is obtained at the yield point i.e. where the plastic…

200 150 streas (MPa) 100 50 e-2 strain From the tensile stress-strain behavior for the brass specimen the diamcter is 12-8 mm Calculate the folluwoing :- |- The Yield stres 2-Modulus of elasticity. 3- The Tensile strength -

200 150 streas (MPa) 100 50 e-2 strain From the tensile stress-strain behavior for the brass specimen the diamcter is 12-8 mm Calculate the folluwoing :- |- The Yield stres 2-Modulus of elasticity. 3- The Tensile strength -

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

A steel specimen is tested in tension. The specimen is 25 mm wide by 12.5 mm thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 160 kN and fractured at 214 kN. a. Determine the tensile stress at yield and at fracture. b. If the original gauge length was 100 mm, estimate the gauge length when the specimen is stressed to 1/2 the yield stress.
Need neat and clean handwritten solution
Engineering strain of a mild steel sample is recorded as 0.100%. The true strain is 1. 2. 3. 4. 0.010% 0.055% 0.099% 0.101%
A 50 mm diameter steel hanger rod carries an axial load of 271 kilonewtons. Under this load, it's average unit strain is 0.00069. determine the modulus of elasticity for the steel.
I need the answer as soon as possible
A steel component is subjected to alternate cyclical loading. The steel follows Basquin's law for high cycle fatigue, o, x N = C, (where the stress amplitude is in MPa). Ignore the geometric detail and assume that Marin's modifying factors are all equal to 1. You are given the minimum stress ain = -213 MPa, the maximum stress omax = 213 MPa. The material data are Tensile strength oUTS = 539 MPa, Basquin's constant c, = 875 MPa, Basquin's exponent a = 0.085. a) Calculate the stress ratio R, the stress amplitude o, in MPa and the mean stress am in MPa. The answers are acceptable with a tolerance of 0.01 for R and of 1 MPa the stresses. R: MPa MPа b) Calculate the corresponding life, in 10° cycles, (tolerance of 0.1 106 cycles) N :
Note:please help us in this sample given problem thank you
7) A specimen of steel 20 mm diameter with a gauge length of 200 mm is tested to destruction. It has an extension of 0.25 mm under a load of 80 kN and the load at elastic limit is 102 kN. The maximum load is 130 kN. The total extension at fracture is 56 mm and diameter at neck is 15 mm. Find (i) The stress at elastic limit. (ii) Young's modulus. (iii) Percentage elongation. (iv) Percentage reduction in area. (v) Ultimate tensile stress.
The following information about the o-e curve is given for a steel alloy. E = 0.001527 at o = 300 MPa and ɛ = 0.003054 for o = 600 MPa. (a) Draw the stress-strain diagram and calculate the E for this alloy.
A sheet of aluminum is stretched in the xy-plane. If the strains in the sheet are ϵx = 0.3 x10-3 and ϵy = 0.25 x10-3, compute σx and σy. Use E = 110 GPa and v = 0.35.
Given: metal specimen x-section (circular) = 0.5sin Gaye length Fractured final final diameter Determine ^ = 2.030 In occured at 28, 500 # length = 2.30in dia = 0.43 in al Ultimate b7 Elongation c) Reduction tensile stress in ksi a percentage as of x-section area as a percentage