1.5-6 The data shown in the table were obtained from a tensile test of a metal specimen with a diameter of 0.500 inch and a gage length (the length over which the elongation is measured) of 2.00 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Use the slope of the best-fit line to estimate the modulus of elasticity. Load (kips) OINN35 CSIN 2.5 3.5 8 9 10 55 11.5 12 Elongation (in.) 0 0.0010 0.0014 0.0020 0.0024 0.0036 0.0044 0.0050 0.0060 0.0070 0.0080 0.0120 0.0180

1.5-6 The data shown in the table were obtained from a tensile test of a metal specimen with a diameter of 0.500 inch and a gage length (the length over which the elongation is measured) of 2.00 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Use the slope of the best-fit line to estimate the modulus of elasticity. Load (kips) OINN35 CSIN 2.5 3.5 8 9 10 55 11.5 12 Elongation (in.) 0 0.0010 0.0014 0.0020 0.0024 0.0036 0.0044 0.0050 0.0060 0.0070 0.0080 0.0120 0.0180

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.5P: The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen...

See similar textbooks

Similar questions

During a tension test, measurements for the applied load and the corresponding elongation are taken at frequent intervals. These data points are then used to: a. calculate the stress caused by the applied load at each data point. b. calculate the strain in the specimen induced by the applied load at each data point. c. plot a stress-strain diagram. d. all of the above
The data shown in the table were obtained from a tensile test of a metal specimen with a rectangular cross-section of 0.2 in.? in area and a gage length (the length over which the elongation is measured) of 2.000 inches. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2% offset method to determine the yield stress.
1.5-7 The data shown in the table were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2 in.² in area and a gage length (the length over which the elongation is measured) of 2.000 inches. d. Estimate the value of the proportional limit. e. Use the 0.2% offset method to determine the yield stress. Load (kips) 0 0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 ܩܙ ܘ 5.5 6.0 6.5 Elongation × 10³ (in.) 0 0.160 0.352 0.706 1.012 1.434 1.712 1.986 2.286 2.612 2.938 3.274 3.632 3.976 Load (kips) 7.0 7.5 8.0 8.5 9.0 9.5 10.0 10.5 11.0 11.5 12.0 12.5 13 Elongation × 10³ (in.) 4.386 4.640 4.988 5.432 5.862 6.362 7.304 8.072 9.044 11.310 14.120 20.044 29.106
An aluminium specimen with an initial gauge diameter d, = 10 mm and gauge length, 1, = 100 mm is %3D subjected to tension test. A tensile force P= 50 kN is applied at the ends of the specimen as shown, resulting in an elongation of 1 mm in gauge length. The Poisson's ratio (µ) of the specimen is Take shear modulus of material, G = 25 GPa. Consider engineering stress-strain conditions. P
A steel bar, whose cross section is 0.60 inch by 4.10 inches, was tested in tension. An axial load of P = 31,025 lb. produced a deformation of 0.115 inch over a gauge length of 2.10 inches and a decrease of 0.0080 inch in the 0.60-inch thickness of the bar. a. Determine the lateral strain. b. Determine the axial strain. c. Determine the Poisson’s ratio v. d. Determine the decrease in the 4.05-in. cross-sectional dimension (in inches).
The stress concentration occurs whenever there is an abrupt change in the cross-section of a component or there is any discontinuity in the material. The figure given below shows a flat plate with a hole of diameter d. The plate is fixed at one end and the other end is subjected to a tensile load of P = 44 kN due to which there is a change in length of 0.4 mm. The thickness of the plate is 11.5 mm. The maximum stress developed in the flat plate is 228 MPa. Take Young's modulus(E) = 210 GPa and theoretical stress concentration factor =2, Calculate the following values: i) Width of the plate (W2) in mm ( ii) Nominal Stress in MPa ( iii) Diameter of the hole (d) in mm
1.5-7 The data shown in the table were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2 in.² in area and a gage length (the length over which the elongation is measured) of 2.000 inches. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. Load (kips) 0 0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 5.5 50 6.0 6.5 Elongation × 10³ (in.) 0 0.160 0.352 0.706 1.012 1.434 1.712 1.986 2.286 2.612 2.938 3.274 3.632 3.976 Load (kips) 7.0 7.5 8.0 8.5 9.0 9.5 10.0 10.5 11.0 11.5 12.0 12.5 13 Elongation × 10³ (in.) 4.386 4.640 4.988 5.432 5.862 6.362 7.304 8.072 9.044 11.310 14.120 20.044 29.106
Sketch the stress-strain curve of the following tension test??? In the tension test of a metal fracture occurs at maximum load. The conditions at fracture were: A = 100 mm and L, = 60 mm, the initial values were: A = 150 mm and L. 40 mm.
2. For the state of stress shown, determine the range of value of for which the normal is equal to or less than 100 MPa and 50 MPa. stress x' + 90 MPa 60 MPa =
The components of plane stress at a critical point on a steel shell are shown in the figure below. The yield stress (Gy) of the material in simple tension is 250 MPa. 60 MPa 40 MPa 70 MPa (a) Determine the magnitude of the principal stresses and maximum shear stress. Sketch these on appropriately orientated elements. (b) Calculate the factor of safety against yield on the basis of i. Tresca failure criterion ii. Von Mises failure criterion
Q4) The dumbell shaped specimen is made from steel rod and is cylindrical in shape, knowing that its value for elasticity is 29000 ksi, Analyze the load which produces deflection of 0.005 inches in the specimen (b) indiviual strain at each portion in it 8 in L= 6 in L= 2 in D = 2 in D= 1.5 in D = 2 in L = 2 in
The stress concentration occurs whenever there is an abrupt change in the cross-section of a component or there is any discontinuity in the material. The figure given below shows a flat plate with a hole of diameter d. The plate is fixed at one end and the other end is subjected to a tensile load of P = 41 kN due to which there is a change in length of 0.4 mm. The thickness of the plate is 11 mm. The maximum stress developed in the flat plate is 235 MPa. Take Young's modulus(E) = 210 GPa and theoretical stress concentration factor =2, Calculate the following values: i) Width of the plate (W2) in mm ii) Nominal Stress in MPa iii) Diameter of the hole (d) in mm Hole with stress concentration factor 2 35 mm W2 35 mm P 300 mm 350 mm- 250 mm