The dial gauge readings (measuring the sample deformation) for one loading stage of consolidation test are shown below. The sample is double drained during the test (with porous stones on both sides of the sample), the initial sample thickness before this loading is 16.0 mm, calculate the coefficient consolidation of the sample, Cv? (unit: mm2/min) 6.8 6.6 U 0% `Ro 6.4 It, 6.2 12 = 41, 6.0 13-42 5.8 E 5.6 4 = 41, U= 50% 5.4 5.2 tso = 13.6 min 5.0 4.8 U= 100% 4.6 Primary consolidation R100 Secondary compresslon 4.4 4.2 - 4.0 0.1 1.0 10 100 1000 10000 Time (min) (ww) Buppos je

The dial gauge readings (measuring the sample deformation) for one loading stage of consolidation test are shown below. The sample is double drained during the test (with porous stones on both sides of the sample), the initial sample thickness before this loading is 16.0 mm, calculate the coefficient consolidation of the sample, Cv? (unit: mm2/min) 6.8 6.6 U 0% `Ro 6.4 It, 6.2 12 = 41, 6.0 13-42 5.8 E 5.6 4 = 41, U= 50% 5.4 5.2 tso = 13.6 min 5.0 4.8 U= 100% 4.6 Primary consolidation R100 Secondary compresslon 4.4 4.2 - 4.0 0.1 1.0 10 100 1000 10000 Time (min) (ww) Buppos je

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Viscosity (Pa-s) 400 1016 1014 1012 1010 108 105 104 10² 1 200 800 Borosilicate glass Temperature (°F) 1200 1600 2000 96% silica glass Working range Melting point 400 600 Fused silica 2400 2800 3:200 Strain point Annealing point Softening point Working point Soda-lime glass 1018 1016 1014 1012 1010 108 106 104 10² 800 1000 1200 1400 1600 1800 Temperature (°C) Viscosity (P)
tensile test PCKN) AL (Mm) Dimensions of the sample be fore e xamin ation 4.12 0. 29 D= 9.5mm L=50 7.64 0.55 12 0.91 15, 8 4 l.27 19.5 1.6 2५.3 2. 11 28 3.5 Dimensions of the sample after exam ination 31.2 5.25 d - 5.7 33.6 2=? 35 8.75 35.7 1o.5 36 12.2 31.5 15.7 27.8 15.8
Match the items in columns I and II. Column-I Column-II 1. Fluidity P. Charpy Q. Knoop 2. Microhardness R. Spiral test S. Cupping test 3. Formability 4. Toughness 5. Permeability (a) P-4, Q-5, R-3, S-2 (b) P-3, Q-5, R-1, S-4 (c) P-2, Q-4, R-3, S-5 (d) P-4, Q-2, R-1, S-3
The shear modulus. G. of a material can be determined by applying a torque. T, on a cylindrical material specimen and measuring the angular twist, 0. The modulus can then be calculated from: G each measured variable (L. T.t. 0, R) is 3.4%. 3LT 2 Ree where R and Lare the specimen radius and length, respectively. The relative uncertainty in What is the total relative uncertainty in G? (Provide your amwer as a percentage using two decimal places. Do not include the % symbol.) 1226
The following data were collected from a 12 mm diameter test specimen of Magnesium. LOAD (N) 0 5000 10000 15000 20000 25000 26500 27000 26500 25000 GAUEGE LENGTH (mm) 30.000 30.0296 30.0592 30.0888 30.15 30.51 30.90 31.50 (maximum load) 32.10 32.79 (fracture) After the fracture, the gauge length is 32.61 mm and the diameter is 11.74 mm. a) What is the elastic modulus? b) Percent elongation at fracture? c) Percent elongation after fracture? d) What is the Poisson's ratio? e)Draw the engineering stress-strain diagram corresponding to the values in the table. Call this plot I. Now consider this experiment is repeated at a higher temperature with an identical sample. Draw the new engineering stress-strain diagram, call it plot Il and highlight the differences (on the same graph) between I and II.
In a forming process the length of material changes from 50 mm to 60 mm. Show the maximum true stress value on the graph using the flow stress equation. o = Ke" Where the parameters are o: True Stress in MPa K: Strength Coefficient, K = 200 ɛ : True Strain, s = In () n: Strain Hardening Exponent, n = 0.27
What is self-heating in strain gauges? Why is it caused and what are its implications on end result?
The following data were recorded during the tensile test of a test specimen with a diameter of 12.8 mm. The gage length is 50.8 mm. The given data are as follow; Given: Test specimen material: Aluminum Diameter of test specimen: Do = 12.8 mm Length of test specimen: Lo = 50.8 mm Force and Elongation data for test specimen Assumptions: 1. The given data is accurate and the material is isotropic 2. The direction of applied force is parallel to the length of the cylinder Requirement: To interpret and plot the stress Vs Strain curve for a given specimen DATA: LENGTH, mm STRESS, MPa LOAD, N 0 50.8 7 330 50.851 15 100 50.902 23 100 50.952 30 400 51.003 34 400 51.054 38 400 51.308 41 300 51.816 44 800 52.832 46 200 53.848 47 300 54.864 47 500 55.88 36 100 56.896 44 800 57.658 42 600 58.42 36 400 59.182 STRAIN
%CW (A.- Aa) X 100 %3D Initial Specimen Measurements (% hard is 21% CW) A. % CW W. Ad Calculated A, 1.007 ola5
Asiacell 4,ll ON 76% D19:17 سؤال الواجب.docx Problem :- The following data was obtained tensile test on a specimen of 6 mm diameter and gauge length Lo=30 mm: load(KN) 0 40 80 95 90 135 150.2 145 130 120 elongation(mm) 0 0.022 0.13 0.25 0.55 2.01 3.88 4.12 5.22 6 Plot engineering and True (stress-strain) curves, then determine the (oy, ɛy), (ou, ɛu), (of, , ef), ductility , modulus of elasticity . Then select on the drawing (strain hardening (n)), (Necking), (uniform plastic region and non-uniform plastic region) and (elastic & plastic) region)?
The following curve is a result of a tensile test. The gauge length was 2 in, and the specimen diameter was 0.505 in The fracture area was round with a diameter of 0.391 in. Remember to com 20000 Force (pounds force) 15000 10000 5000 0 16. The yield strength is 0 0.2% O 80,000 pl O 12.000 p 060,000 pl 85,000 p 0.1 0.2 Extension (inch) 0.3 0.4
A 11 in. inner diameter, 0.35 " wall thickness pipe is under a pressure of 2.5 ksi where strain gages installed along axial and circumferential directions register strains of 180 and 900 micro-strains (x10^-6), respectively. A) What is the Poisson's Ratio of this material and it's Elastic Modulus? B) In a uniaxial test, the pipe's material is observed to yield at a longitudinal strain of 0.1 in/in. Assuming a factor of safety of 2, the pipe can withstand impact energy of _______ lb - in per foot without suffering permanent deformation. C) If the pipe is depressurized and then subjected to a torque of 50 lblb - ft.ft., it will experience a shear strain of ________ rad.