Question
Chapter 16.13, Problem 56KCP
To determine
Explain the unit cell of the inverse spinel structure along with the tetrahedral and octahedral interstitial sites occupied by the ions.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
6- Determine the minimum radius of an atom that will just fit into
(a) The tetrahedral interstitial FCC nickel, lattice parameter: 0.35167 nm
(b) The octahedral interstitial site in BCC lithium, lattice parameter: 0.35089 nm
1- The density of the elemental magnesium crystal structure, which is in the face centered cubic structure, is 1,738 g / cm3. Specify the side lengths of the crystal lattice.
2-Polonium is an element with a simple cubic crystal arrangement. Find the radius of the polonium atoms in this structure with a density of 9.4 g / cm3 and a weight of 209 g / atom.
3- A wire with a diameter of 9.6 mm is pulled with a force of 18,000 N. With this loading, the initial length of the wire that grows 1.5 mm is 400 mm. Find the engineering voltage.
In FCC iron-carbon atoms enter the lattice (a)/(b) sites to form austenite, and in BCC iron, carbon enters (c)/(d) sites to form ferrite. Choose from the options (a) or (b) and (c) or (d) to complete the sentence correctly.
A.
(a) octahedral and tetrahedral
B. (c) tetrahedral
C.
(b) octahedral
D. (d) octahedral and tetrahedral
Chapter 16 Solutions
Foundations of Materials Science and Engineering
Ch. 16.13 - Prob. 1KCPCh. 16.13 - Prob. 2KCPCh. 16.13 - Prob. 3KCPCh. 16.13 - Prob. 4KCPCh. 16.13 - What is the relationship between B and H?Ch. 16.13 - Prob. 6KCPCh. 16.13 - Prob. 7KCPCh. 16.13 - Prob. 8KCPCh. 16.13 - Prob. 9KCPCh. 16.13 - Prob. 10KCP
Ch. 16.13 - Prob. 11KCPCh. 16.13 - Prob. 12KCPCh. 16.13 - Prob. 13KCPCh. 16.13 - Prob. 14KCPCh. 16.13 - Prob. 15KCPCh. 16.13 - Prob. 16KCPCh. 16.13 - Prob. 17KCPCh. 16.13 - Prob. 18KCPCh. 16.13 - Prob. 19KCPCh. 16.13 - Prob. 20KCPCh. 16.13 - Prob. 21KCPCh. 16.13 - Prob. 22KCPCh. 16.13 - Prob. 23KCPCh. 16.13 - Prob. 24KCPCh. 16.13 - Prob. 25KCPCh. 16.13 - Prob. 26KCPCh. 16.13 - Prob. 27KCPCh. 16.13 - Prob. 28KCPCh. 16.13 - Prob. 29KCPCh. 16.13 - Prob. 30KCPCh. 16.13 - Prob. 31KCPCh. 16.13 - Prob. 32KCPCh. 16.13 - Prob. 33KCPCh. 16.13 - Prob. 34KCPCh. 16.13 - Prob. 35KCPCh. 16.13 - What are eddy currents? How are they created in a...Ch. 16.13 - Prob. 37KCPCh. 16.13 - Prob. 38KCPCh. 16.13 - Prob. 39KCPCh. 16.13 - Prob. 40KCPCh. 16.13 - What compositions of NiFe alloys are especially...Ch. 16.13 - Prob. 42KCPCh. 16.13 - Prob. 43KCPCh. 16.13 - Prob. 44KCPCh. 16.13 - Prob. 45KCPCh. 16.13 - Prob. 46KCPCh. 16.13 - Prob. 47KCPCh. 16.13 - Prob. 48KCPCh. 16.13 - Prob. 49KCPCh. 16.13 - Prob. 50KCPCh. 16.13 - Prob. 51KCPCh. 16.13 - Prob. 52KCPCh. 16.13 - Prob. 53KCPCh. 16.13 - Prob. 54KCPCh. 16.13 - Prob. 55KCPCh. 16.13 - Prob. 56KCPCh. 16.13 - Prob. 57KCPCh. 16.13 - Prob. 58KCPCh. 16.13 - Prob. 59KCPCh. 16.13 - Prob. 60KCPCh. 16.13 - Prob. 61KCPCh. 16.13 - Prob. 62AAPCh. 16.13 - Prob. 63AAPCh. 16.13 - Prob. 64AAPCh. 16.13 - Prob. 65AAPCh. 16.13 - Prob. 66AAPCh. 16.13 - Gadolinium at very low temperatures has an average...Ch. 16.13 - Prob. 68AAPCh. 16.13 - Prob. 69AAPCh. 16.13 - Prob. 70AAPCh. 16.13 - Prob. 71AAPCh. 16.13 - Prob. 72AAPCh. 16.13 - Prob. 73AAPCh. 16.13 - Prob. 74AAPCh. 16.13 - Prob. 75AAPCh. 16.13 - Draw a hysteresis B-H loop for a ferromagnetic...Ch. 16.13 - Describe what happens to the magnetic induction...Ch. 16.13 - What happens to the magnetic domains of a...Ch. 16.13 - What are desirable magnetic properties for a soft...Ch. 16.13 - What are hysteresis energy losses? What factors...Ch. 16.13 - How does the AC frequency affect the hysteresis...Ch. 16.13 - How can eddy currents be reduced in metallic...Ch. 16.13 - Why does the addition of 3% to 4% silicon to iron...Ch. 16.13 - What disadvantages are there to the addition of...Ch. 16.13 - Why does a laminated structure increase the...Ch. 16.13 - Prob. 86AAPCh. 16.13 - Prob. 87AAPCh. 16.13 - Prob. 88AAPCh. 16.13 - Prob. 89AAPCh. 16.13 - Prob. 90AAPCh. 16.13 - Prob. 91AAPCh. 16.13 - Prob. 92AAPCh. 16.13 - Prob. 93AAPCh. 16.13 - Prob. 94AAPCh. 16.13 - Prob. 95AAPCh. 16.13 - Prob. 96AAPCh. 16.13 - Prob. 97AAPCh. 16.13 - Prob. 98AAPCh. 16.13 - Prob. 99AAPCh. 16.13 - Prob. 100AAPCh. 16.13 - Prob. 101AAPCh. 16.13 - Prob. 102AAPCh. 16.13 - Prob. 103SEPCh. 16.13 - Prob. 104SEPCh. 16.13 - Prob. 105SEPCh. 16.13 - Prob. 106SEP
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- 8- Tungsten W (atomic weight = 183.84 g/mol) forms a body centered cubic (bcc) unit cell. If tungsten has an atomic radius of 147 pm. Calculate the density of the W. * Pm = 10-12 marrow_forwardFor austenitic stainless steel, Cu, and Al (all FCC metals): a. Calculate the actual magnitudes of the full and partial dislocations, assuming that the lattice parameters are 0.365 nm, 0.362 nm, and 0.405 nm, respectively. b. Calculate the equilibrium partial dislocation separation distance d for all three materials. c. Put the numbers from part (b) in context by comparing them to the atomic size (diameter) and lattice parameter for each material. d. In which of the three material(s) is wavy glide very likely to be observed?arrow_forwardCalculate the fraction of atom sites that are vacant for copper at its melting temperature of 1084degC. assume an energy vacancy formation of 0.90eVlatom. * 6.56 x 10^-5 O 0.9992 O 4.56 x 10^-4 O 2.19 X 10^-4arrow_forward
- Find the Miller indices of the plane shown below. (Show all steps and working). Use the correct type of bracket and bar notation for negative indices B 1/4 a C b Chkarrow_forwardCalcium has the Face-Centered Cubic (FCC) crystal structure shown in the figure below. The atomic radius of calcium is r = 0.197 nm at room temperature (20°C). Calculate the edge length "a" of the unit cell Select one: a. None of these O b. 0.612 O c. 0.488 O d. 0.333 e. 0.557arrow_forwardRhodium (Rh) has the Face-Centered Cubic (FCC) crystal structure. The atomic radius of Rhodium is r= 0.134 nm at room temperature (20°C). Calculate the edge length "a" of the unit cell Select one: Oa 0.379 Ob.0.428 Oc 0.612 Od0.488 O e. 0.233 The indices for the direction shown in the figure are: 10:13 PM 15-Apr-2021arrow_forward
- Question-7 Calculate the volume in cubic nanometers of the titanium crystal structure unit cell. Lattice constants for titanium at 20°C are a = 0.29504 nm and c = 0.46833 nm.arrow_forwardRhodium (Rh) has the Face-Centered Cubic (FCC) crystal structure. The atomic radius of Rhodium is r = 0.134 nm at room temperature (20°C). Calculate the edge length “a” of the unit cell  Select one: a. 0.612 b. 0.488 c. 0.379 d. 0.233 e. 0.428arrow_forwardAustenite form of iron has a fcc lattice crystal structure, whereas its alpha form has bcc crystal lattice structure, assuming closest pack arrangements of iron atoms, what will be the ratio of density of austenite to that of alpha ironarrow_forward
- the dislocationarrow_forwardb. Given that Na = 6.022x1023 atoms/mol. Calculate the theoretical density of nickel. Show your calculations.arrow_forwardExplain Face centered cubic structure with neat diagram and calculate the atoming packing factor for face Body centered cubic structure ?arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY