You are an engineer for a steel plant. You are presented with a piece of steel from your rival plant. You investigate the microstructure and find it to contain 60 % ferrite and 40% martensite, and the martensite contains 0.5% carbon. Based on this information, reverse engineer the nominal composition and starting temperature used by your rival. You may assume the composition of ferrite to be 0.022%. (Round the composition to 2 decimal places, and the temperature to the nearest 25 degrees Celsius)

You are an engineer for a steel plant. You are presented with a piece of steel from your rival plant. You investigate the microstructure and find it to contain 60 % ferrite and 40% martensite, and the martensite contains 0.5% carbon. Based on this information, reverse engineer the nominal composition and starting temperature used by your rival. You may assume the composition of ferrite to be 0.022%. (Round the composition to 2 decimal places, and the temperature to the nearest 25 degrees Celsius)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Given the Cu-Zn phase diagram below, determine the amount of the phase/s present of a 75 wt% Zn -25 wt% Cu alloy for the following temperatures. Indicate the required composition for each temperature in the diagram. Round off your final answers up to two decimal places. Show your solutions completely and neatly and follow the table format below, Temperature Phase/s present Phase composition Relative amount 600 °C 570 °C y+ L 700 1200 8+L L 600 P 598°C 560°C 570 |1000 e + L y +e 500 60 68.6 70 74.3 75 78.2 80 90 Composition (wt % Zn) Temperature (°C) ta Temperature (°F)
The TTT diagram for a 1076 eutectoid steel is given: What is the heat treatment process to form 50% Coarse Pearlite + 50% Martensite. 800 A 1400 Eutectoid temperature 700 A 1200 600 1000 500 800 400 A 600 300 M(start) 200 50% 400 M + A M(50%) M(90%) 100 200 10-1 1 10 102 103 104 105 Time (s) Temperature (°C) Temperature (°F)
Excellent combinations of hardness, strength, and toughness are obtained from bainite. One heat treater austenitized a eutectoid steel at 750°C, quenched and held the steel at 250°C for 15 min, and finally permitted the steel to cool to room temperature. Did he produce the required bainitic structure? Use the diagram below in your answer 900 600 700 14 00 Y. 400 12 52 M. 00 57 M. 100 0.3 10 10 10 Answer: Time Temperature ("C) Rockwell Chardnens
800 A Eutectoid temperature H 1400 700 A H 1200 600 1000 500 B 800 400 A 300 600 M(start) 200 M + A 50% 400 M(50%) M(90%) 100 200 10-1 1 10 102 103 104 105 Time (s) Using the isothermal transformation diagram for an iron-carbon alloy of eutectoid composition, specify the final microstructure and approximate amount of each. Assume a small specimen has been held long enough to have achieved a complete and homogeneous austenitic structure prior to treatment. Sample (1): Quickly cool specimen from 800°C to 575°C, hold for 10 s, then quench to room temperature. Sample (2): Quickly cool specimen from 800°C to 500°C, hold for 100 s, then quench to room temperature. O after treatment, sample 1 is 50% pearlite, 50% austenite O after treatment, sample 2 is bauxite O after treatment, sample 1 is 25% pearlite O after treatment, sample 2 is bainite O after treatment, sample 2 is austenite O None of the answers is correct. O after treatment, sample 2 is coarse pearlite O after treatment, sample 1 is…
Figure 1 show Eutectoid Plain Carbon Steel Phase Diagram. Please indicate the phases present and their corresponding weight fraction at points a, b, c and d. Show your tie-line and calculations based on Lever Rules. Temperature (°C) 1100 900 700 500 300 100 0 100% Fe 7 0.02 1.0 Fe,C 1.2 2.0 7 7 7 7 Fe, C Figure 1 Fe,C Pearlite 4.0 3.0 Weight percent carbon 7+ Fe, C 727°C a + Fe₂C 5.0 Fe, C 6.0 6.7
The engineering yield strength of an alloy is 80 ksi.
By using the Iron - Carbon diagram that you have. Find 5 of the following. 1- The microstructure of Cast iron with 3% C. 2- The Liquid and Austinite percent with chemical composition for cast iron with 2% C at 1300°C 3- Find the melting point and microstructure of steel with 0.83% C 4- Define the temperature range for Acm temperature. 5- Find the Ac3, Acl temperature and microstructure of steel with 0.4 % C 6- Find the Eutectic, Eutectoid temperature and microstructure of cast iron with 4.3% C
Q1. Imagine you are working for an automotive manufacturer and are selecting plastic materials for various components. Draw the structure of a material you might use for a soft touch plastic. Now draw the structure of a material you might use in the drive train (i.e., an engineering plastic). What characteristics are you engineering into the material? Q2. Based on what you know about the calorimetry of melting and crystallization, do you expect melting to be endothermic or exothermic? What about condensation? Can we say anything general about heat flow in the process of forming bonds, covalent or van der Waals?
For two hypotetical materials which have limitless solubility for both in the “liquid” and “solid” states in each other, the following data are listed. Melting Temperatures of material A and B are Tm,A and Tm,B respectively, Liquidus and Solidus curves are circular arcs. a- Draw the related “Phase Diagram” of Material A and Material B showing the data given and calculated. b- Calculate/Determine the compositions of phases at T2 , explain the procedure. c- Calculate/Determine the “percentages” of “phases” of Alloy,2 at T2 , explain the procedure. Given: -Tm,A, Celcius =300 -Tm,B, Celcius =800 -T1, Celcius =600 -B percentage of Liquid phase at T1 =25 -B percentage of Solid phase at T1 =70 -B percentage of Alloy 2. =50 -T2, Celcius =650 -B percentage of Liquid phase of Alloy 2 at T2 = to be calculated -B percentage of Solid phase of Alloy 2 at T2 = to be calculated
QI/ Draw a thermal equilibrium diagram for the binary alloy system (Si –Au), from the following data:- a- Si melts at 1414 °C, and Au melts at 1064 °C , and identify all phases are present in the diagram. b- Eutectic is formed at 360°C containing 20 Wt% Si -80 Wt% Au . c- Determine the amount of each phase for the alloy which consist 60 Wt% Si- 40Wt % Au at 1200 °C and 800 °C ,then determine the amount of eutectic at 200 °C?
A certain component is to be carburized to obtain 0.592 wt % C at a depth of 2.0 mm. After carburizing (for 1.2 hours) the heat treater finds that he achieved 04 wt % C at a depth of 2.0 mm. His furnace only operates at a 900 C and maintains a constant atmosphere of 1 wt % C The steel used has an initial carbon content of 0.2 wt %. How long (in hours) should he carburize to achieve his goal?
1 Al-Li Aerospace Alloys When a small amount of Li is added into Al to create an Al-Li alloy, the two elements typically do not mix homogeneously. Instead, most of the material is nearly-pure Al, while some small regions are Li-rich.¹ (These small regions are called precipitates and they are responsible for giving Al-Li alloys much better properties for aerospace applications relative to pure Al. We'll learn more about the alloying process and about precipitates later in the course.) The Li-rich regions have the chemical formula Al3Li and belong to the cubic crystal system.² In the unit cell, the Li atoms are located at 000, while the Al atoms are located at 110, 101, and 01121. (a) Draw the unit cell of Al3Li. (b) Which of the crystal structures from Callister Chapter 3 does this resemble? Why do we not call it that structure? (c) Given that the lattice parameter is 0.401 nm, what is the density of Al3Li?