What is the limitation on the thickness of specimens for a hardness test? What are limitations for distance from specimen edge to indentation and distance betwe indentations? Explain why these limitations exist in both cases

What is the limitation on the thickness of specimens for a hardness test? What are limitations for distance from specimen edge to indentation and distance betwe indentations? Explain why these limitations exist in both cases

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Which of the following can be approximately obtained from a conventional micro- or macro- hardness…

A: The micro and macro hardness test are used to measure the hardness of the metal by calculating BHN.…

Q: Q4- Answer the following 1- Classification of plastic deformation 2- What is the difference between…

A: Dear student, According to the guidelines I am allowed to answer only three…

Q: what is the function of measuring lines in the Digital Micro-Vickers Hardness er? What do they…

A: Main functions and features of the DIGITAL Micro-vicker hardness tester:The machine can be connected…

Q: if the coldworked radius is twenty mm, now what is the radius before being deformed if the ductility…

Q: outline the significant differences between rockwell and brinell hardness test

Q: Briefly discuss the differences between the Engineering Stress versus Engineering Strain and the…

A: Solution is attached below:

Q: Determine Brinell Hardness Number for a specimen that has a surface area of indentation as 12 mm2…

A: Data given- F = 15 kN = 15 × 101.972 = 1529.57 kgf A = 12 mm2 BHN = ?

Q: Your manager asked you to explain the difference between three-point bending test and four-point…

Q: Small and medium industries could not have afforded to buy an expensive universal testing machine to…

A: Tensile testing, often known as tension testing, is a basic materials science and engineering…

Q: Your manager asked you to explain the difference between three-point bending test and four-point…

A: The three-point bending test and four-point bending test are used to determine the bending strength…

Q: (c) A tensile test uses a copper test specimen that has a gauge length of 80 mm and a di.ameter of…

A: c)

Q: Determine Brinell Hardness Number for a specimen that has a surface area of indentation as 12 mm2…

A: Surface area of indentation (A)= 12 mm2 Applied force = 15 kN = 15000 N Applied load…

Q: Discussion: 1- What are the differences between the types of hardness test? 2- Mention another type…

A: 1. Different types of hardness test as given below, Brinell Hardness test : This test employs a…

Q: What is the difference between tensile and compression testing?

A: Given:- Tensile testing Compression testing To find:- Difference between tensile testing and…

Q: Determine the surface area of indentation for a specimen that has Brinell hardness number as 851 and…

A: Given: The Brinell hardness number is, 851. The magnitude of applied force is, F=15 kN×103 N1…

Q: Your manager asked you to explain the difference between three-point bending test and four-point…

A: The force is F=30 kN. The thickness is t=5 cm=0.05 m The width is b=10 cm=0.1 m. The length is L=25…

Q: Determine Brinell Hardness Number for a specimen that has a surface area of indentation as 10 mm?…

Q: 1. As an Engineer how do you improve the fracture toughness of different metals? 2. How is a…

A: 1 2

Q: 1. In a tensile test, two pairs of values of stress and strain were measured for the specimen metal…

A: Note:As per our guidelines we are supposed to answer only one question. Kindly repost other…

Q: 3 (a) Give the meanings of the terms tensile stress and Yourg's modulus. Define the quantity which…

A: To determine the various properties of a material like stress, strain, young's modulus, yield…

Q: Determine the indentation diameter and the surface area of indentation of a copper material…

A: Given: BHN = 955 D = 10 mm W = 9.4 kN Thus, F=Wg=9.4×1039.81=958.2 kg

Q: Why would engineers use Vickers Hardness testing (HV) over Brinell Testing for hardened tool steel…

A: Hardness is the property of the material that can be understand as the resistance to scratch and…

Q: When making hardness measurements, whether by nanoindentation or by conventional indentation…

A: A preexisting indent in the vicinity of the new indent influences the hardness value, thus resulting…

Q: In a tensile test, initial length of the experimental specimen is the final length of the specimen.

A: we have to determine the effect of tensile test on the length of specimen

Q: A square cross-section v-notched specimen of height 75 mm has each side of 10 mm has been selected…

A: Given data height of specimen (h) = 75 mm side = 10 mm thickness of notch = 1.9 mm To determine…

Q: An aluminum specimen subjected to the Brinell hardness test, the indenter and indentation diameters…

Q: Small and medium industries could not have afforded to buy an expensive universal testing machine to…

A: Universal Testing machines or UTMs are used to accurately measure tensile strength of various…

Q: Describe tensile test in detail considering the steps. Define stress, strain (equations a elasticity…

A: elastic range = it is the point in the stress-strain curve up to which the material remains elastic…

Q: Briefly comment on the values obtained for the Elastic Modulus, Yield Strength, Ultimate Strength…

A: Given data Yield strength of the given material = σyield = 186 MPaElastic Modulus of the given…

Q: In what situations would you use a hardess test instead of a Tensile test?

A: The objective of the question is to understand the scenarios where a hardness test would be more…

Q: Determine the indentation diameter and the surface area of indentation of a copper material…

A: Given: The test force, P = 9.4 kN The diameter of the steel ball, D = 10 mm The Brinell hardness…

Q: A brittle fracture of a test specimen in an impact test is usually characterised by; A plastically…

A: Explanation: Brittle metals absorb a very small amount of energy during the impact test. The…

Q: Determine the surface area of indentation for a specimen that has Brinell hardness number as 851 and…

A: We have to find surface area

Q: What are the different types of Indenters used in Rockwell Hardness Testing?

Q: Luestion One In a tensile test, material mechanical properties are determined by relating…

A: Solution is attached below:

Q: 1. Write a note on toughness mechanism in brief. 2. What is the standard size of square and round…

Q: Determine Brinell Hardness Number for a specimen that has a surface area of indentation as 19 mm2…

Q: Small and medium industries could not have afforded to buy an expensive universal testing machine to…

A: The tensile strength and compressive strength of materials are tested using a universal testing…

Q: Vickers microhardness tests have been conducted on a brass specimen. For an applied load (P) of 1000…

Q: What are the experimental techniques used to measure the strain?

A: The experimental techniques used to measure the strain of material under the action of load comes…

Q: 1. Define ultimate compressive strength. What are are the specific conditions of a compression test…

A: According to our guidelines we are supposed to answer first question only. 1. The compressive…

Concept explainers

Thermal Properties of Materials

In mechanical engineering, the thermal property is represented as the physical quantity that is relevant to the application of heat. The thermal properties are evaluated by variations in any specific material due to low heat or high heat. The quantities that influence the thermal property of the materials are mass, density, temperature, and many others.

Question

What is the limitation on the thickness of specimens for a hardness test? What are the
limitations for distance from specimen edge to indentation and distance between
indentations? Explain why these limitations exist in both cases.

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 2 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Properties of Engineering Materials

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

In a micro-Vickers hardness test, the diagonals of the indentation are 54 and 55 um when a load of 200 g was applied to the specimen. Determine the micro-Vickers hardness (HV) of the tested specimen. (Input the answer with two decimal places: like 20.32, 36.26, etc.).
Engineering strain of a mild steel sample is recorded as 0.100%, determine true strain.
Determine the indentation diameter and the surface area of indentation of a copper material subjected to a Brinell hardness test with a test force of 7.3 kN using a hardened steel ball indentor of 11 mm. Take the Brinell Hardness Number as 948. Solution: i) Indentation Diameter (in mm) = ii) Surface Area of Indentation (in mm2) =
the creep data for two different samples. You have been asked to analyse the results, if you know that the original length of specimen is 17.4625 mm and the original width is 4.8 mm and the original thickness 1.6 mm and the cross sectional area is 7.68 mm: 1. Compare the lifetime for these samples.2. Determine the rapture lifetime for the samples below. 3. Calculate the creep rate for all of them
small crack, 4mm deep, is found on the edge of a large, thick plate structure. The plate is continuously subjected to a uniform cyclic tensile stress (in the direction perpendicular to the crack plane) which varies from 0 MPa to 100 MPa and back to 0 MPa every 40 seconds. If the next inspection is to take place in 30 days, would it be safe to delay the replacement or repair of the plate until that time? The stress intensity factor, KI, for this type of crack is related to the nominal stress, G, and the crack length, a, via the relationship is K, = 1.12a Va %3D For the plate material, the yield stress is 800 MPa, the fracture toughness is 50 MN/m2 and threshold stress intensity factor range is 6 MN/m3/2, The fatigue-crack growth rate per cycle for the material, da/dN, can be defined by: 3/2 da / dN = 2.8 x 10-12 (AK,) ^PY (m/cycle) Where AK1 has unit MN/m e 8:34 /
A hammer of mass 5 kg is released in the impact testing machine from the height 1.5 m. After it breaks the specimen, hammer raised to the height 0.5 m. Calculate toughness of the material. a. 98.1 J b. 36. 8J C. 49.05 J d. 24.5 J
Define the given terms related to mechanical properties of materials. 1. Nanoindentation 2. Neckling 3. Newton’s material 4. Notch sensitivity test 5. Offset strain value
7. Explain the major and minor loads used in the Rockwell hardness test. Which of these loads did we manually apply?
Compare the three hardness tests and what can we conclude from this comparison
Describe ductile fracture and brittle one. what is the difference between them in tensile test specimen, Explain in detail.
i need the answer quickly
List the factors that you would consider in selecting a hardness test. Explain why. 1|Page