Three metal strips, each 40 mm height, are bonded together to form the composite beam shown. The modulus of elasticity is 210 GPa for the steel, 105 GPa for the brass, and 70 GPa for the aluminium. If the allowable bending stress for the aluminum (Gallow)al= 100 MPa, for the steel (Gallow)st 150 MPa and (Gallow)br 200 MPa for brass determine the maximum allowable intensit of w of the uniform distributed load. Aluminum 10 mm

Three metal strips, each 40 mm height, are bonded together to form the composite beam shown. The modulus of elasticity is 210 GPa for the steel, 105 GPa for the brass, and 70 GPa for the aluminium. If the allowable bending stress for the aluminum (Gallow)al= 100 MPa, for the steel (Gallow)st 150 MPa and (Gallow)br 200 MPa for brass determine the maximum allowable intensit of w of the uniform distributed load. Aluminum 10 mm

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter12: Composite Materials

Section: Chapter Questions

Problem 12.11P

See similar textbooks

Similar questions

1. Three metal strips, each 40 mm height, are bonded together to form the composite beam shown. The modulus of elasticity is 210 GPa for the steel, 105 GPa for the brass, and 70 GPa for the aluminium. If the allowable bending stress for the aluminum (Gallow)al= 100 MPa, for the steel (Gallow)s=150 MPa and (Gallow)b= 200 MPa for brass determine the maximum allowable intensit of w of the uniform distributed load. 2w Aluminum 2w 10 mm Brass 10 mm Steel 20 mm 2m - 40 mm
1. Three metal striips, each 40 mm height, are bonded together to form the composite beam shown. The modulus of elasticity is 210 GPa for the steel, 105 GPa for the brass, and 70 GPa for the aluminium. If the allowable bending stress for the aluminum (Galow= 100 MPa, for the steel (Galow)kr=150 MPa and (Galow)or 200 MPa for brass determine the maximum allowable intensit of w of the uniform distributed load. Aluminum 10 mm Brass 10 mm Steel 20 mm 40 mm
Problem 2: A bronze bar is fastened between a steel bar and an aluminum bar as shown. Axial loads are applied at the positions indicated. Find the largest value of P that will not exceed an overall deformation of 3.0 mm, or the following stresses: 140 MPa in the steel, 120 MPa in the bronze, and 80 MPa in the aluminum. Assume that the assembly is suitably braced to prevent buckling. Use Est = 200 GPa, Eal = 70 GPa, and Ebr = 83 GPa. Steel Bronze 480 mm² 650 mm² 3P 1.0 m 4P 2.0 m Aluminum 320 mm² 1.5 m 2P
4. For the composite block shown, determine (a) the value of h if the portion of the load carried by the aluminum plates is half the portion of the load carried by the brass core, (b) the total load if the stress in the brass is 80 Mpa. P Rigid end plate Aluminum Plates (E=70 GPa) Brass Core (E=105 GPa) 40 mm I h 60 mm 300 mm
Situation No. 2 A bronze bar is fastened between a steel bar and an aluminum bar as shown below. Axial loads are applied at the positions indicated. Find the largest value of P that will not exceed an overall deformation of 3.0 mm, or the following stresses: 140 MPa in the steel, 120 MPa in the bronze, and 80 MPa in the aluminum. Assume that the assembly is suitably braced to prevent buckling. Use Est = 200 GPa, Eal = 70 GPa, and Ebr = 83 GPa. Bronze Steel A = 480 mm? Aluminum A = 650 mm A = 320 mm 3P 4P 2P 1.0 m 2.0 m 1.5 m
A composite bar is fabricated by brazing aluminum alloy [E = 10,000 ksi] bars (1) to a center brass [E = 17,000 ksi] bar (2) as shown in the fıgure. Assume d = 0.65 in., a = 0.1835 in., L = 22 in. If the total axial force carried by the two aluminum bars must equal the axial force carried by the brass bar, calculate the thickness b required for brass bar (2). Brass (2) Aluminum (1) (1) P a b = i in.
The composite bar is firmly attached to unyielding supports. Compute the stress (psi) in each material caused by the application of the axial load P = 50 kips Aluminum A = 1.25 in? E = 10 x 10° psi Steel A = 2.0 in? E = 29 x 10° psi 15 in 10 in
The composite bar, firmly attached to unyielding supports, is initially stress free. What maximum axial load P can be applied if the allowable stresses are 80 MPa for aluminum and 144 MPa for steel? Steel Aluminum A = 1125 mm2 E = 70 GPa A = 1800 mm? E = 200 GPa 450 mm- 360 mm-
Q2: A composite beam is made of two brass [E =100 GPa] plates bonded to an aluminum [E =75 GPa] bar, as shown in Figure below. The beam is subjected to a bending moment of 1200 N-m acting about the z axis. Determine: (a)the maximum bending stresses in the brass plates and the aluminum bar. (b) the stress in the brass at the joints where the two materials are bonded together.
a) Determine the location of the centroid with respect to the point P; y = mm Submit part Unanswered b) Determine the moment of inertia l with respect to the centroidal axes. x106 mm*
A steel bar and an aluminum bar are bonded together as shown to form a composite beam. Knowing that the vertical shear in the beam is 4 kips and that the modulus of elasticity is 29 * 106 psi for the steel and 10.6 *106 psi for the aluminum, determine (a) the aver-age shearing stress at the bonded surface, (b) the maximum shearing stress in the beam.
2. The materials that have low values of tensile strain * concrete steel Aluminum O Brass O All above are correct