Extension Compression Determine the engineering strain "e" and the true strain “e" for each of the following situations of extending a bar of length L or compressing a billet of height h: Extension from L to 1.002 L Compression from h to 0.998 h Extension from L to 1.9L Compression from h to 0.1h Compression from h to zero height

Extension Compression Determine the engineering strain "e" and the true strain “e" for each of the following situations of extending a bar of length L or compressing a billet of height h: Extension from L to 1.002 L Compression from h to 0.998 h Extension from L to 1.9L Compression from h to 0.1h Compression from h to zero height

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

5. Please calculate the strain and stress in the following two prompts a. A 1 cm long section of tendon stretches to 1.011 cm when it is subjected to a tensile force of 40,000 N. What is the strain in this segment of tendon? @? 17 b. The section of the patellar ligament in the previous question is 0.02 m² in the cross section. What is the stress in this section of ligament as a result of 50,000 N tensile force? E = Δι 19 0 = A 1.011 cm 50000 0,02 Scoco 40000 1.25 = T % 2500000 strain N/m² on trito flox your wrist, you may notice that your
For the stress-strain curves below, which statements are correct? Stress (MPa) 60 50 40 30 20 10 0 a. 0 b. O c. e. f. A 1 2 The mechanical behavior shown in C is that of an elastomer with low elastic modulus Polymer B and C have an elastic behavior whereas A has a plastic behavior While the deformation in polymer A is fully reversible until breakage, polymer B and C only display reversible deformation until 0.1X and 5x elongations respectively Od. The polymer with brittle nature is the one that possesses the highest elastic modulus The mechanical behavior shown in B is that of an elastomer with low elasticity The polymer with the necking behavior has the highest strength B с 3 4 5 6 7 8 Strain
! How to compute the strain displacement matrix for each element?
A metal rod of initial length L, is subjected to a drawing process. The length of the rod at any instant is given by the expression, L(t) = Lo(1 + t2), where tis the time in minutes. The true strain %3D rate (in min-1) at the end of one minute is
1. Find the strain that results from a tensile force of 1000 N applied to a 10 m long aluminium bar having cross-sectional area of 4x10 m2. The modulus of elasticity of aluminium is 69 GN/m². 2 A resistance wire strain gauge having a nominal resistance of 350 2 is subjected to a strain of 500 micro-strain. Find the change in the value of resistance neglecting the piezoresistive effect.
For the stress-strain curves below, which statements are correct? Stress (MPa) 60 50 40 30 20 10 0 0 A B C. 1 2 3 4 Strain 5 6 7 8 a. The mechanical behavior shown in C is that of an elastomer with low elastic modulus b. While the deformation in polymer A is fully reversible until breakage, polymer B and C only display reversible deformation until 0.1X and 5x elongations respectively The mechanical behavior shown in B is that of an elastomer with low elasticity d. Polymer B and C have an elastic behavior whereas A has a plastic behavior e. The polymer with the necking behavior has the highest strength Of. The polymer with brittle nature is the one that possesses the highest elastic modulus
After the yield region in the stress-strain curve the strength up to ultimate value because: -Molecules orientation in the direction of applied stress -Molecules fails to withstand the applied stress -Molecules orthogonal to the axis of applied force The following figure shows typical engineering tensile stress vs. strain curves, where: * Stress Strain - Points A, C, E and F correspond to the tensile strength and elongation at yield - Points A, B, D and F correspond to the tensile strength and elongation at break Points A, C, E and F correspond to the tensile strength and elongation at break
You need the shear modulus for a particular material in order to calculate shear strain for a known applied shear shear stress. You can't find shear modulus for the material, but you can find elastic modulus (200 GPa) and Poisson's ratio (0.3). Which of the following could you use as the shear modulus for your calculations? 200 GPa O 60 GPa O 77 GPa O 154 GPa
material with a rectangular cross-section of 4 mm by 25 mm is loaded in tension with a force of 32 kN. A strain gauge bonded to the material measures a strain of 400 microstrain when the sample is loaded. culate Young's modulus of the material, measured to the nearest GPa (GN/m2) and enter your answer in the box below. ung's modulus: [ GPa
From the shear stress - shear strain diagram shown below, all the following are true except: Shear Stress (MPa) 500 450 400 350 300 250 200 150 100 50 0. 0.2 0.4 0.6 0.8 1.2 1.4 1.6 1.8 Shear Strain (rad) Shear Stress-Strain Curve for Brass Select one: O a. Shear stress and Shear strain are 430 MPa and 1.72 rad at fracture. O b. Shear stress and Shear strain are 250 MPa and 0.05 rad at Yielding. Oc. The elastic zone ends at a shear stress of 400 MPa and shear strain of 1 rad Od. The ultimate Shear stress and Shear strain are 430 MPa and 1.72 rad.
When stress is applied to a liquid over an application time tp the liquid needs a relaxation time tc to accordingly deform. Relaxation time tc is a physical property of liquids. The Deborah number is De= tdt, . The lower the Deborah number of a stress applied to a material the more.. : Select one: O The material behaves like a solid O The material behaves like visco-elastic O The material behaves like a liquid
In our previous topic regarding strain, repeat the problem on the strain using thefollowing parameters:F = 150000 +/- 150 lbfSide length = 1.2 +/- 0.025 inModulus of Elasticity = 25000 +/- 11.5 ksiDetermine the relative error. Is it above or below the accepted 5% error?