A rod specimen of ductile cast iron was tested in a torsion-testing machine. The rod diameter was 18 mm, and the rod length was 160mm. When the applied torque reached 225.2 N-m, a shear strain of 2285 microradians was measured in the specimen. What was theangle of twist in the specimen?Answer:

Arod specimen of ductile cast iron was tested in a torsion-testing machine. The rod diameter was 18 mm, a mm. When the applied torque reached 225.2 N-m, a shear strain of 2285 microradians was measured in the angle of twist in the specimen? Answer: i

Arod specimen of ductile cast iron was tested in a torsion-testing machine. The rod diameter was 18 mm, a mm. When the applied torque reached 225.2 N-m, a shear strain of 2285 microradians was measured in the angle of twist in the specimen? Answer: i

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

A tension test is being conducted on a steel-rod specimen with a gauge length of L0=2 in and initial diameter of d0=0.5 in. Data were collected to form the conventional stress-strain diagram as shown. From the diagram, f = 74.0 ksi, e = 104.0 ksi , g = 85.0 ksi , and h = 0.15 in/in. Assuming that the strain remains constant throughout the region between the gauge points, determine the nominal strain ε experienced by the rod if it is elongated to L = 2.7 in . Assuming that the stress is constant over the cross-sectional area and if the tension force used is P = 11.0 kips, find the nominal stress experienced by the rod. Determine the force P needed to reach the ultimate stress in the steel-rod specimen.
An aluminum shaft has a diameter of 50.1 mm. Determine the maximum shear stress in the shaft when subjected to a torque of 26.5 Nm? (answer in MPa or MN/m² to 1 decimal place, use pi = 3.142)
A specimen of metal of original length 80mm and original diameter 21mm was subjected to tensile a test. The load and extension at the limit of proportionality were found to be 105,000N and 0.082mm. The yield point was at a load of 112,00ON. The maximum load before the material failed was 199,000N. The final length at failure was 91mm. Calculate: i. the stress at the limit of proportionality i. the yield stress iii. the ultimate tensile stress iv. the value of Young's Modulus V. the strain at failure
A circular aluminum tube subjected to pure torsion by torque T (see figure) has an outer radius r, equal to 1.5 times the inner radius r,. T (a) If the maximum shear strain in the tube is measured as 460 x 10-° rad, what is the shear strain y, (in radians) at the inner surface? rad (b) If the maximum allowable rate of twist is 0.126°/m and the maximum shear strain is to be kept at 460 x 10-6 rad by adjusting the torque T, what is the minimum required outer radius (r..min' in mm)? mm
need help asap plsss tq....
1.5-5 A tension test was conducted on a specimen with a circular cross section of diameter 0.5 inch and a gage length of 8 inches. (The gage length is the distance between two marks on the specimen. The deformation is measured within this length.) The stress and strain were computed from the test data and plotted. Two plots are shown here; the first one shows the entire test range, and the second shows a portion near the pro- portional limit. d. Estimate the 0.2% offset yield strength. e. Estimate the ultimate stress. f. If a load of 10 kips is applied and then removed, estimate the permanent defor- mation in inches. Stress (ksi) Stress (ksi) 80 70 60 50 40 30 20 10 0 60 50 40 30 20 10 0 0 0 0.05 0.002 0.1 0.004 0.15 Strain 0.006 Strain FIGURE P1.5-5 0.2 0.008 0.25 0.01 0.3 0.012
A hollow steel cylinder 3.5m which has an inside diameter and outside diameter of 55mm and 35mm. If the steel carry a load (17) KN find the stress in the cylinder also find the deformation in the cylinder if the Modulus of Elasticity is 90 GPA.
Describe a procedure for triaxial testing that raises the deviatoric stress while the nondeviatoric stress remains constant.
A drill rod with a diameter of 10 mm is made of high-strength steel alloy with a shear modulus of 80 GPa. The rod is to be subjected to a torque T. What is the minimum required length L of the rod so that the cross section at one end can be rotated 90° with respect to the other end without exceeding an allowable shear stress of 300 MPa?
Example 8.4. A specimen of steel 20 mm diameter with a gauge length of 200 mm is tested to destruction. It has an extension of 0.25 mm under a load of 80 kN and the load at elastic limit is 102 kN. The maximum load is 130 kN. The total extension at fracture is 56 mm and diameter at neck is 15 mm. Find (i) The stress at elastic limit. (ii) Young's modulus. (iii) Percentage elongation.
In a tensile test for an aluminum alloy, the sample is 2 inches long and 0.5 inches in diameter. The proportional portion of the tension stress-strain diagram for an aluminum alloy is shown below. It the diameter change of the sample was also monitored during the above test, and it was found that the lateral strain of the sample is 1/3 of its axial longitudinal strain, what is the Poisson' ratio of the material under test: ___. Calculate your answer to 2 decimal place.