An elastoplastic material with strain hardening has the stress–strain relationship shown in Figure 1.6(c). The modulus of elasticity is 175 GPa, yield strength is 480 MPa, and the slope of the strain-hardening portion of the stress–strain diagramis 20.7 GPa.a. Calculate the strain that corresponds to a stress of 550 MPa.b. If the 550-MPa stress is removed, calculate the permanent strain.

An elastoplastic material with strain hardening has the stress–strain relationship shown in Figure 1.6(c). The modulus of elasticity is 175 GPa, yield strength is 480 MPa, and the slope of the strain-hardening portion of the stress–strain diagramis 20.7 GPa.a. Calculate the strain that corresponds to a stress of 550 MPa.b. If the 550-MPa stress is removed, calculate the permanent strain.

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 6.2P

See similar textbooks

Similar questions

An elastoplastic material with strain hardening has the stress-strain relation shown in the figure. The yield point corresponds to 600 MPa stress and 0.003 m/m strain.Determine the following:a. If a bar made of this material is subjected to a stress of 650 MPa and then released, what is the permanent strain?b. What is the percent increase in yield strength that is gained by the strain hardening shown in part (a)?c. After strain hardening, if the material is subjected to a stress of 625 MPa, how much strain is obtained? Is this strain elastic, permanent, or a combination of both?
A steel alloy specimen having a rectangular cross section of dimensions 19.1 mm x 3.1 mm (0.7520 in. × 0.1220 in.) has the stress-strain behavior shown in the Animated Figure 6.22b. If this specimen is subjected to a tensile force of 98290 N (22100 Ib;) then (a) Determine the amount of elastic strain induced. (b) Determine the amount of plastic strain induced. (c) If its original length is 610 mm, what will be its final length after this force is applied and then released? The elastic modulus for steel is 207 GPa. (a) i (b) i (c) i mm
Problem 11. [Concepts: Calculating stress from internal forces, nonlinear stress-strain response, elongation from strain.] Acetal plastic has a stress-strain diagram as shown. a) Determine the yield strength assuming a 0.2% offset. b) If a bar of this material has a length of 3 ft and cross-sectional area of 0.875 in², and is subjected to an axial load of 2.5 kip, determine its elongation. c) Determine the modulus of toughness just before it fractures if failure occurs at a = 0.12. σ (psi) a = 9.5(10³) €¹/3 € (in./in.)
A cylindrical specimen of stainless steel having a diameter of 12.8 mm (0.505 in.) and a gauge length of 50.800 mm (2.000 in.) is pulled in tension. Use the load–elongation characteristics shown in the following table to answer the following: a. Plot the data as engineering stress versus engineering strain. b. Compute the modulus of elasticity. 66 c. Determine the yield strength at a strain offset of 0.002. d. Determine the tensile strength of this alloy. e. What is the approximate ductility, in percent elongation? f. Compute the modulus of resilience
An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 780 mm. The cross-sectional dimensions of the beam are b₁ = 36 mm, d₁ = 104 mm, b₂ = 22 mm, d₂ = 22 mm, and a = 7 mm. For this material, the allowable tensile bending stress is 16 MPa, and the allowable compressive bending stress is 10 MPa. Determine the largest moment M that can be applied as shown to the beam. b2 ✓ a M d₁ B L N.m A Answer: M = d₂ b₁
Your answer is incorrect. An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 500 mm. The cross-sectional dimensions of the beam areb1 = 35 mm, d1= 115 mm, b2= 21 mm, d2 = 21 mm, and a =7 mm. For this material, the allowable tensile bending stress is 15 MPa, and the allowable compressive bending stress is 14 MPa. Determine the largest moment M that can be %3D %3D %3D %3D %3D %3D applied as shown to the beam. b2 a 不 d2 d1 b1 Answer: N-m M% =
A bar of length 2.0m is made of a structural steel having the stress-strain diagram shown in the figure. The yield stress of the steel is 250 MPa and the slope of the initial linear part of the stress-strain curve (modulus of elasticity) is 200GPa. The bar is loadded axially until it elongates 6.5mm, and then the load is removed. How does the final length of the bar compare with its original length? (Hint: Use the concepts illustrated in figure below)
2. A steel bar, whose cross section is 0.55 inch by 4.05 inches, was tested in tension. An axial load of P = 30,500 lb. produced a deformation of 0.105 inch over a gauge length of 2.05 inches and a decrease of 0.0075 inch in the 0.55-inch thickness of the bar. Determine the lateral strain. * Your answer Determine the axial strain. Your answer Determine the Poisson's ratio v. * Your answer Determine the decrease in the 4.05-in. cross-sectional dimension (in inches). * Your answer
An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 900 mm. The cross-sectional dimensions of the beam are b1 = 31 mm, d1 = 119 mm, b2 = 19 mm, d2 = 19 mm, and a = 6 mm. For this material, the allowable tensile bending stress is 17 MPa, and the allowable compressive bending stress is 10 MPa. Determine the largest moment M that can be applied as shown to the beam. b2 a M d2 |A В b1 Answer: M = i N-m
An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 500 mm. The cross-sectional dimensions of the beam are b₁ = 33 mm, d₁ = 109 mm, b₂ = 20 mm, d₂ = 20 mm, and a = 6.5 mm. For this material, the allowable tensile bending stress is 16 MPa, and the allowable compressive bending stress is 11 MPa. Determine the largest moment M that can be applied as shown to the beam. b₂ a M B A Answer: M = L d₂ N•m b₁ d₁
A steel bar, whose cross section is 0.60 inch by 4.10 inches, was tested in tension. An axial load of P = 31,025 lb. produced a deformation of 0.115 inch over a gauge length of 2.10 inches and a decrease of 0.0080 inch in the 0.60-inch thickness of the bar. a. Determine the lateral strain. b. Determine the axial strain. c. Determine the Poisson’s ratio v. d. Determine the decrease in the 4.05-in. cross-sectional dimension (in inches).
An elastoplastic material with strain hardening has the stress-strain relation shown below. The modulus of elasticity is 25 x 106 psi, yield strength is 70 ksi, and the slope of the strain-hardening portion of the stress-strain diagram is 3 x 106 psi. a. Calculate the strain that corresponds to a stress of 80 ksi. b. If the 80-ksi stress is removed, calculate the permanent strain.