A. Which material is considered as ductile and which one is considered as brittle? Explain. What is the difference between the two types? B. Knowing that one of these two specimens is polystyrene and the other is mild steel. Which of these tensile tests will be for polystyrene and which one will be for the mild steel? C. What is the Ultimate Tensile Strength (UTS) for the two specimens? Which one has higher UTS? Explain your answer. D. From the tensile test for Material A. What is the value of yield strength for this material? E. From the tensile test for Material A. Calculate the Modulus of Elasticity (Young's Modulus) for this material. F. Which material has higher plastic deformation before fracture?

A. Which material is considered as ductile and which one is considered as brittle? Explain. What is the difference between the two types? B. Knowing that one of these two specimens is polystyrene and the other is mild steel. Which of these tensile tests will be for polystyrene and which one will be for the mild steel? C. What is the Ultimate Tensile Strength (UTS) for the two specimens? Which one has higher UTS? Explain your answer. D. From the tensile test for Material A. What is the value of yield strength for this material? E. From the tensile test for Material A. Calculate the Modulus of Elasticity (Young's Modulus) for this material. F. Which material has higher plastic deformation before fracture?

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 6.9P

See similar textbooks

Similar questions

A student wants to measure the strain at a particular point K on a loaded specimen, so she affixes a 45° strain rosette at point K and obtains the following results: €A = 390 μrad EB = 275 μrad Ec = 325 prad After packing up and going home to analyse her results, she realises that the strain rosette was misaligned by 0 degrees CW (where a negative corresponds to CCW) from the x-y axes-ie. Gauge C is not parallel with the x-axis and is instead parallel with a different x' axis that is rotated by 0 degrees-where: 0 = 16 deg Instead of replacing the rosette and retaking measurements, the student realises she can use what she learned in ENGG2400 to find the strains she's interested in. b 45° 45° a) Draw a diagram of the situation, showing both the x-y axes and the strain rosette. b) Calculate Exx, Eyy and Yxy. c) Calculate the maximum in-plane shear strain and the associated average normal strain. I X
Fatigue test results of a material are shown in the diagram. a) Estimate the ultimate static strength of this material b) Estimate the fatigue (endurance) limit. c) If this test specimen has a cross-sectional area of 14 cm² and subjected to a maximum repeated load of 2800 kg over it, after how many repetitions will it fail? d) Determine the fatigue strength at 1000 cycles a (kgf/cm?) 500 400 300 200 100 2 3 4 5 6 logio N
5.7 During the test of a specimen in a tensile testing ma- chine, it is found that the specimen elongates 0.0024 inch between two punch marks that are initially two inches apart. Evaluate the strain.
The strains on the surface of an experimental device made of pure aluminum ( E=70 GPa, v=0.33 ) and tested in a space shuttle were measured by means of strain gages. The gages wereoriented as shown in the figure, and the measured strains were6a1100 10 ε−= × , and6b1496 10 ε−= × ,6c39.44 10 ε−= − × . What is the stressxσ in the x-direction ?
A tensile test was conducted on a specimen with a diameter of 0.5 in. A strain gage was bonded to the specimen so that the strain could be obtained directly. The following data were obtained: Load (lb) 2000 2500 3000 3500 4000 4500 5000 Strain 0.000047 0.000220 0.000500 0.000950 0.001111 0.001200 0.001702 Create a table of stress and strain values Plot these data point, and draw a best-fit straight line through them What is the slope of this line? What does this value represent?
Q.1 The yield stresses (oy) have been measured using steel and aluminum specimens of various grain sizes, as follows: Material D (µm) σΥ (MPa) Steel 60.5 160 136 128 Aluminum 11.1 235 100 223 (a) Determine the coefficients o and kỵ in the Hall- Petch for these two materials. (b) Determine the yield stress in each material for a grain size of d=26 um.
1. A vertical pressure of 70 MPa is applied to an aluminum cube sample with a length of 10 cm on each side. The modulus of elasticity of aluminum is 70000 MPa and the Poisson ratio is 0.3. a) Find the new dimensions of the cube b) What will be the new dimensions if 70 MPa pressure is applied in the horizontal directions in addition to the 70 MPa pressure in the vertical direction?
For a given material if the Young's modulus is 200 GN/m² and odulus of rigidity is 80 GN/m?, then the Poisson's ratio will be a. 0.40 b. 0.50 c. 0.25 d. 0.30
3. Consider iron and its elastic constants (Find them from the net or some book). An iron specimen consists of grains with texturing distribution of [110] (20%), [112] (20%), [111] (30%) and [103] (30%) (all percentages by volume) along the loading direction is serving under a static force of 10,000 N. The metal rod has a 20 mm diameter perpendicular to the loading direction. a) Find the strain response of the specimen.
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. 1-)-Determine the modulus of resilience (in N.mm/mm3) of the material. (Use at least five decimal units) 2-)- Determine the elastic energy absorption capacity (in N.mm) of that specimen. 3-)Determine the plastic energy absorption capacity (in N.mm) of that specimen.
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Calculate the fracture strength (in MPa) of the material. - Calculate the percent elongation of the specimen at fracture point. - Determine the modulus of resilience (in N.mm/mm3) of the material. (Use at least five decimal units) - Determine the toughness index number (in N.mm/mm3) of the material. - Determine the elastic energy absorption capacity (in N.mm) of that specimen. - Determine the plastic energy absorption capacity (in N.mm) of that specimen.
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Calculate the yield strength (in MPa) of the material. - Calculate the percent elongation of the specimen at yield point. (Use at least five decimal units) - Calculate the stiffness (in MPa) of the specimen material. - Calculate the ultimate strength (in MPa) of the material. - Calculate the percent elongation of the specimen at point of ultimate strength. - Calculate the fracture strength (in MPa) of the material. - Calculate the percent elongation of the specimen at fracture point. - Determine the modulus of resilience (in N.mm/mm3) of the…