A tensile load of 150 kN is applied to a round metal bar with a diameter of 16 mm and a gage length of 80 mm. Under this load the bar elastically deforms so that the gage length increases to 80.1192 mm and the diameter decreases to 15.89 mm. Determine the modulus of elasticity (in MPa) and Poisson's ratio for this metal.

A tensile load of 150 kN is applied to a round metal bar with a diameter of 16 mm and a gage length of 80 mm. Under this load the bar elastically deforms so that the gage length increases to 80.1192 mm and the diameter decreases to 15.89 mm. Determine the modulus of elasticity (in MPa) and Poisson's ratio for this metal.

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

PROBLEM 1) An aluminum bar carries the axial loads at the positions shown. If E=70GPA, compute the total deformation of the bar. Assume that the bar is suitably braced to prevent buckling. 0.4m D 10KN 0.8m 0.4m 5KN 0.6m A 20KN 3) What is the deformation &cn in mm? A=800 mm? A=1,200 mm²
If Poisson's ratio is 0.42, the Modulus of rigidity is 70.4225 GPa, and the bulk modulus is 416.66 GPa, then the elastic modulus of elasticity is (3 Points) 300 GPa 300 MPa 200 MPa None 200 GPa
Please answer d,e,f
Please solve fast!
1. The tensile strength vs. temperature curves of aluminum are plotted below. Explain the meaning of these two curves. 400 Ultimate strength 300 Yield strength 200 100 -200 -150 -100 -50 50 100 150 200 250 Temperature, °C Strength, kPa
A steel bar, whose cross section is 0.60 inch by 4.10 inches, was tested in tension. An axial load of P = 31,025 lb. produced a deformation of 0.115 inch over a gauge length of 2.10 inches and a decrease of 0.0080 inch in the 0.60-inch thickness of the bar. a. Determine the lateral strain. b. Determine the axial strain. c. Determine the Poisson’s ratio v. d. Determine the decrease in the 4.05-in. cross-sectional dimension (in inches).
The stress-strain diagram for a steel alloy having an original diameter of 0.5 in. and a gage length of 2 in. is given in the figure. If the specimen is loaded until it is stressed to 70 ksi, determine the approximate amount of elastic recovery and the increase in the gage length after it is unloaded. o (ksi) 80 70 60 50 40 30 20 10 e (in./in.) 0 04 0.08 0.12 0.16 0.20 0.24 0.28 0 0005 0.0010.0015 0.002 0.0025 0.0030.0035
SITUATION. As shown in the figure below, a rigid bar with negligible mass is pinned at O and attached to two vertical rods. Assume that the rods were initially stress-free. Allowable stress in steel is 120 MPa and in bronze is 60 MPa. For this problem, a = 1.8m; b = 1.3m; c= 1.7m. a b C P Steel: A-900 mm² Bronze: A=1200 mm² E = 83 GPa L=2.0 m E = 200 GPa L=1.5m What is the value of P without exceeding the allowable stress of bronze, in kN? O 161 O 174 O 145 124 4
A cylindrical specimen of brass that has a diameter of 20 mm, a tensile modulus of 110 GPa, and a Poisson's ratio of 0.35 is pulled in tension with force of 40,000 N. If the deformation is totally elastic, what is the strain experienced by the specimen? O 0.00463 O 0.00116 O 0.0029 O 0.01350
X Your answer is incorrect. An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 760 mm. The cross-sectional dimensions of the beam are bị = 33 mm, di = 102 mm, bz = 20 mm, d2 = 20 mm, and a = 6.5 mm. For this material, the allowable tensile bending stress is 10 MPa, and the allowable compressive bending stress is 13 MPa. Determine the largest moment M that can be applied as shown to the beam. b2 d2 A В b1 Answer: M = 457.082 N-m Save for Later Attempts: 2 of 3 used Submit Answer Usine mutinle attemnts has imnacted vour score
A cylindrical bar of steel 9.9 mm (0.3898 in.) in diameter is to be deformed elastically by application of a force along the bar axis. Determine the force that will produce an elastic reduction of 3.0×10-3 mm (1.181 ×10-4 in.) in the diameter. For steel, values for the elastic modulus (E) and Poisson's ratio (v) are, respectively, 207 GPa and 0.30. i N
A 100 mm x 100 mm x 100 mm cube made with glass polymers in the y- direction is subjected to a tensile load of 100 kN along the y-direction. However, the cube is constrained against deformation in the x and z directions. Given the following properties: Ex = 20 GPa Ey = 50 GPa Ez = 20 GPa Vxy = 0.25 Vxz = 0.5 Vyz = 0.25 (a) Compute for the change in length of the cube in the y-direction and; (b) Determine the stresses, ox,Oy,Oz•