A low-carbon steel has a yield strength of 622 MPa when the average grain diameter is 180 um. When the grain diameter is reduced to 22 um, the yield strength increases to 663 MPa. (a.) Calculate the yield strength when the grain diameter is reduced to 10 μm. Keep track of units, and show all work. (b.) Did we reach the "magical value" of 100 ksi?

A low-carbon steel has a yield strength of 622 MPa when the average grain diameter is 180 um. When the grain diameter is reduced to 22 um, the yield strength increases to 663 MPa. (a.) Calculate the yield strength when the grain diameter is reduced to 10 μm. Keep track of units, and show all work. (b.) Did we reach the "magical value" of 100 ksi?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The yield strength for an alloy that has an average grain diameter of 4.6 x 10-2 mm is 105 MPa. At a grain diameter of 7.7 × 103 mm, the yield strength increases to 248 MPa. At what grain diameter, in mm, will the yield strength be 234 MPa? d = i mm
The yield stresses (σY) have been measured using steel and aluminum specimens of various grain sizes given in the attached image.On the basis of data answer the following questions: (a) Determine the coefficients σ0 and kY in the Hall- Petch for these two materials.(b) Determine the yield stress in each material for a grain size of d=26 μm.
The yield strength for an alloy that has an average grain diameter of 4.1 × 10-2 mm is 131 MPa. At a grain diameter of 7.6 × 10-3 mm, the yield strength increases to 246 MPa. At what grain diameter, in mm, will the yield strength be 236 MPa?
4. The average grain diameter for a brass material was measured as a function of time at T, which is tabulated below at two different times: Time (min) Grain Diameter (mm) 30 90 3.9 × 10-2 6.6 × 10-2 (a) What was the original grain diameter (using n=2)? (b) What grain diameter would you predict after time, t, at temperature, T? Use T = 650 °C; t = 150 min; n = 2 in the grain size equation
A copper-zine alloy has the properties shown in the table below. Grain Diameter (mm) Strength (MPa) 0.015 170 MPa 0.025 158 MPa 0.035 151 MPa 0.050 145 MPa Determine (a) the constants in the Hall-Petch equa- tion; and (b) the grain size required to obtain a strength of 200 MPa.
The yield stress of AISI 1020 steel with a grain size of 200 μm is 200 MPa.Estimate the yield stress for a grain size of 10 μm if the Hall--Petch constantk = 0.8 MN/m3/2.
3. An uncold-worked brass specimen of average grain size 0.01 mm has a yield strength of 150 MPa (21,750 psi). Estimate the yield strength of this alloy after it has been heated to 500°C for 1000 s, if it is known that the value of σo is 25 MPa. (Note that the axis has logarithmic scale). Grain diameter (mm) (Logarithmic scale) 1.0 0.1 0.01 1 10 850°C 800°C 700°C 102 Time (min) (Logarithmic scale) 600°C 500°C 103 104
1. Two iron samples with different grain sizes are tensile tested. The grain size of sample A is 0.37 um and the grain size of sample B is 1.10 μm. (a) Sketch stress-strain curves of both samples on the same graph. (b) Compare the yield strength, tensile strength, ductility and elastic modulus. (c) Explain the effect of grain size on tensile properties.
In an engineering application, the material is a strip of iron with a fixed crystallographic structure subject to a tensile load during operation. The part failed (yielded) during operation and needs to be replaced with a component with better properties. You are told that two other iron strips had failed at yield stresses of 110 and 120 MPa, with grain sizes of 30 microns and 25 microns respectively. The current strip has a grain size of 20 microns. The diameter of the rod is 1 mm and the load applied is 100 N. What is the yield stress of the new part C and would you recommend it for operation? Select one: a.120.5 MPa, no b.140.5, no c.129.5, yes d.123.5 MPa, yes e.133.5 MPa, yes
In an engineering application, the material is a strip of iron with a fixed crystallographic structure subject to a tensile load during operation. The part failed (yielded) during operation and needs to be replaced with a component with better properties. You are told that two other iron strips had failed at yield stresses of 110 and 120 MPa, with grain sizes of 30 microns and 25 microns respectively. The current strip has a grain size of 20 microns. The diameter of the rod is 1 mm and the load applied is 100 N. What is the yield stress of the new part C and would you recommend it for operation? Select one: a. 140.5, no Ob. 129.5, yes OC. 120.5 MPa, no O d. 133.5 MPa, yes O e. 123.5 MPa, yes
In an engineering application, the material is a strip of iron with a fixed crystallographic structure subject to a tensile load during operation. The part failed (yielded) during operation and needs to be replaced with a component with better properties. You are told that two other iron strips had failed at yield stresses of 110 and 120 MPa, with grain sizes of 30 microns and 25 microns respectively. The current strip has a grain size of 20 microns. The diameter of the rod is 1 mm and the load applied is 100 N. What is the yield stress of the new part C and would you recommend it for operation? Select one: a. O b. 129.5, yes C. 133.5 MPa, yes e. 120.5 MPa, no d. 140.5, no 123.5 MPa, yes
an alloy with an avg grain diameter of 0.053 mm is l16 MPa. When the grain diameter is 0.008Amm, the yeild strength goesupto 231 MPa.lf the yeild strength is 207MPA, what would the grain diameter be?