3. Consider a test specimen with the shape of cylindrical rod, 120 mm long to be deformed by tensile load of 28000 N without experiencing plastic deformation or diameter reduction more than 8.5x10-3 mm. Which among the aluminium alloy, brass alloy, steel alloy and titanium alloy are possible candidates with yield strengths 200 MPa, 300 MPa, 400 MPa and 650 MPa, respectively.

3. Consider a test specimen with the shape of cylindrical rod, 120 mm long to be deformed by tensile load of 28000 N without experiencing plastic deformation or diameter reduction more than 8.5x10-3 mm. Which among the aluminium alloy, brass alloy, steel alloy and titanium alloy are possible candidates with yield strengths 200 MPa, 300 MPa, 400 MPa and 650 MPa, respectively.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The stress for low alloys steel at which plastic deformationbegins Is 475 MPa, and the modulus or elastlcity ls 315 PA What is the maximum load that may be applied to a specimenwith a eras sectional area of 300 mm2 without plastic deformed If the original specimen length is 120 mm what is the maximumlength to with may be stretched without causing plastic deformation?
specimen of stainless steel having a diameter of 12.8mm and gauge lengh of A cylindrical the following: (6) Extend the table to include engincering strain and engineering stress and plot the Engineering stress-strain curve Determine the yield stress at 0.002 strain offset (i1) (in) Determine the Modulus of Elasticity What is the tensile strength of the Alloy? What is the ductility in percent elongation: What is the Modulus of Resilience? (iv) (v) (vi) ble 1. Load-Extension Test Data of Stainless Stee! LOAD (N) LENGTH(mm) 50.800 50.825 12700 25400 38100 50800 76200 89100 92700 102500 107800 119400 128300 50.851 50.876 0001 50.902 50.952 51.003 CCOn 12-8 51.054 51.181 51.308 51.562 51.816 149700- 52.832 159500- 53.848 160400 54.365 159500- 151500 124700 14. 54.864 55.880 56.642 1 000 05 Pcu/coer 0.00
(a) A core sample having length to diameter ratio of 2.5 experienced a strain of 0.94 after being stretched. If the core had an initial length of 8 cm and was able to withstand a load of 500 N before breaking, calculate: The resulting length before failure The tensile strength (b) If the core sample above is subjected to a uniaxial compression test resulting in load, axial deformation and circumferential deformation of 350 N, 1.5 and 0.47 respectively at failure, calculate: The uniaxial compressive strength, σc The Young’s modulus, E The Poisson’s ratio,μ
A three-point bending test was performed on an aluminum oxide specimen having a circular cross section of radius = 5 mm, the specimen fractured at a load of 1400 N when the distance between the support points L = 100 mm. Another test is to be performed on a specimen of this same material, but one that has a square cross section of 12 mm on each edge. At what load would you expect this specimen to fracture if L = 50 mm? i need clear ans by hand and solve very very fast in 20 min and thank you DYBALARI |
A metallic rod with an initial diameter of 10 mm and an initial length of 50 mm is subjected to the tensile test. After the fracture, the final length was measured as 51.8 mm, and the final diameter was measured as 9.5 mm.(a) Calculate modulus of elasticity, ultimate tensile strength, elongation at fracture in %,reduction of area in %, true stress at maximum load, true strain at maximum load, strain hardening exponent, strength coefficient.?
information: "When performing a tensile test of a metal, these values were found for stress and strain. the yield strength (YS) is stress at 0.2% plastic strain" The task: A 5 meter long rod of this material is loaded axially with a stress of 244 MPa.i. How long is the rod under load?ii. Then the bar is relieved, how long is it now?
specimen of a 4340 steel alloy with a plane strain fracture toughness of 54.8 MPa√m is exposed to a stress of 1030 MPa. Will this specimen experience fracture if it is known that the largest surface crack is 0.5 mm long? Why or why not? Assume that the parameter Y has a value of 1.0.
Two cylindrical specimens of an alloy are to be strain hardened by reducing their cross- sectional areas. for one specimen. the initial and deformedradii are 17 mm and 12 mm, respectively. The second specimen. with an initial radius of 13 mm, must have the same deformed hardness as the firstspecimen What is the second specimen's radius affer deformation”
Draw two schematic graphs using pencil showing a typical stress-strain curve for aluminum. The first graph should show engineering stress vs engineering strain, and the second graph should show true stress vs true strain. Label the showing: (i) elastic modulus (ii) proportional limit (iii) yield stress (iv)yield strain (v) fracture stress (vi) fracture strain on each graph. You may showboth graphs on one plot. Explain the difference between engineering stress and true stress.
A high-strength steel was subjected to a tensile test. It failed under a stress of 1600 MPa with a total strain of 2.7%. (E = 200 GPa, oy = 1400 MPa.) (a) What is the ductility of this steel in terms of % elongation? (b) Estimate the diameter of a specimen made of this material that can carry a load of 5000 N while remaining in the elastic regime.
Given a example of copper specimen that has had a tensile test conducted on it. Diameter of 6.4mm Max force of 11112.5N Max extension of 7.79mm Calculate: 1) modulus of elasticity 2) tensile strength 3) the ductility, in percent elongation 4) yield strength at a strain of 0.002
A square specimen of is loaded using a three-point bend test. The load during the test is 419.6 N while the separation between the load points is 53.1mm. The flexural strength of MgO is equal to 103.4MPa . Compute the minimum possible thickness the specimen should have to avoid fractures during the bend test. Round your answer to three significant figures.