Q3: Analyze the following figure and answer the following question(Fe-C Diagram) ?1639Liquid1400 +y7+LL-Fec1146 CFe.C-9107- Fesc727 Co.025a- Fesc6.67ofHypo ectd- Hyper ectd0810SteelCast IronI- What are the % solubility and temperature of exist of a-ferrite?b- 0.025% and 273°c to 910 c.d- 0.05% and 910°c to 1124°c.a-0.05% and 273°c to 910°c.c- 2.1% and 910°c to 1394°c.2- What are the % solubility and temperature of exist of Austenite (Y)?a- 0.05% and 273°c to 910°c.c- 2.1% and 910°c to 1394°c.b- 0.025% and 273°c to 910°c.d- 0.09% and 1394°c to 1539°c.3- What are the % solubility and temperature of exist of 8-ferrite?a- 0.05% and 273°c to 910°c.b-0.025% and 273 e to 910°e.c- 2.1% and 910°c to 1394°c.d- 0.09% and 1394°c to 1539°c.4- What is the % C content in Cementite Fe3C?ABa- 6.67%.b- 0.025%.c- 2.1%.d- 0.09%.(aradu

Answered: Image /qna-images/answer/584d972a-5ea4-4f2e-b0e6-2bea07da202f.jpg

Q3: Analyze the following figure and answer the following question (Fe-C Diagram) ? 1639 Liquid 1400 8+y L-Fec 1146 C Fe.c- 910 7- Fesc 727 C o.025 a Fesc 6.67 0810 Hypo Steel Cast iron I- What are the % salubility and temperature of exist of a-ferrite? a-0.05% and 273°c to 910°c. c- 2.1% and 910°c to 1394°c. b-0.025% and 273°c to 910°c. d- 0.05% and 910°c to 1124°c. 2- What are the % solubility and temperature of exist of Austenite (Y)? a-0.05% and 273°c to 910°c. c- 2.1% and 910°c to 1394°c. b-0.025% and 273°c to 910°c. d- 0.09% and 1394°c to 1539°c. 3- What are the % solubility and temperature of exist of 8-ferrite? b- 0.025% and 273 e to 910°c. d- 0.09% and 1394°c to 1539°c. a- 0.05% and 273°c to 910°c. c- 2.1% and 910°c to 1394 c.

Q3: Analyze the following figure and answer the following question (Fe-C Diagram) ? 1639 Liquid 1400 8+y L-Fec 1146 C Fe.c- 910 7- Fesc 727 C o.025 a Fesc 6.67 0810 Hypo Steel Cast iron I- What are the % salubility and temperature of exist of a-ferrite? a-0.05% and 273°c to 910°c. c- 2.1% and 910°c to 1394°c. b-0.025% and 273°c to 910°c. d- 0.05% and 910°c to 1124°c. 2- What are the % solubility and temperature of exist of Austenite (Y)? a-0.05% and 273°c to 910°c. c- 2.1% and 910°c to 1394°c. b-0.025% and 273°c to 910°c. d- 0.09% and 1394°c to 1539°c. 3- What are the % solubility and temperature of exist of 8-ferrite? b- 0.025% and 273 e to 910°c. d- 0.09% and 1394°c to 1539°c. a- 0.05% and 273°c to 910°c. c- 2.1% and 910°c to 1394 c.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

-SC Show Attempt History Current Attempt in Progress Consider 6.8 kg of austenite containing 0.43 wt% C, cooled to below 727°C (1341°F). (a) What is the proeutectoid phase? (b) How many kilograms each of total ferrite and cementite form? (c) How many kilograms each of pearlite and the proeutectoid phase form? See Animated Figure 9.24 Part 1 Part 2 How many kilograms of total ferrite and cementite form? (a) ma = kg (b) mFe, C 1 i Save for Later Q = i F1 2 W F2 #3 kg 80 F3 E 4 000 000 F4 R % F5 T MacBook Pro < 6 A Attempts: 0 of 5 used 6 Y & 7 AA F7 U *
According to Reference [1], alloys of nickel (Ni) and tungsten (W) are can form substitutional solid solutions up to approximately 11 at% W. Consider two different alloy compositions: Ni-5W (5 at% W) and Ni-10.5W (10.5 at% W). A. Which composition should be more ductile? B. Which composition should be stronger? C. Using the oy~ C¹/2 relationship from the lecture slides, how many times larger should the yield strength be for Ni-10.5W compared to Ni-5W? D. Where should the tungsten atoms sit relative to the dislocation on or opposite the side with the extra half-plane? You will need information from Appendixes of the textbook.
800 A Eutectoid temperature H 1400 700 A H 1200 600 1000 500 B 800 400 A 300 600 M(start) 200 M + A 50% 400 M(50%) M(90%) 100 200 10-1 1 10 102 103 104 105 Time (s) Using the isothermal transformation diagram for an iron-carbon alloy of eutectoid composition, specify the final microstructure and approximate amount of each. Assume a small specimen has been held long enough to have achieved a complete and homogeneous austenitic structure prior to treatment. Sample (1): Quickly cool specimen from 800°C to 575°C, hold for 10 s, then quench to room temperature. Sample (2): Quickly cool specimen from 800°C to 500°C, hold for 100 s, then quench to room temperature. O after treatment, sample 1 is 50% pearlite, 50% austenite O after treatment, sample 2 is bauxite O after treatment, sample 1 is 25% pearlite O after treatment, sample 2 is bainite O after treatment, sample 2 is austenite O None of the answers is correct. O after treatment, sample 2 is coarse pearlite O after treatment, sample 1 is…
What is the composition, in at. %, of an alloy that contains 35g of Cu and 42g of Zn Acu= 63.55g/molAzn=65.41g/mol
For a Fe-C alloy with a eutectoid composition, an austenite was rapidly cooled down to 450°C, held for 10 sec, and quenched to room temperature. What is the final microstructure based on its TTT curve? Amount Temperature of Transformation, C 700 600 500 400 300 200 Ae₂! Ae₁ Austenite unstable Ms. 10 10² 103 104 105 seconds Austenite stable 50%- 100 MF TELEP P 100% completed F+B Coarse Pearlite - Fine Pearlite -Upper Bainite (Feathery) Lower Bainite → Martensite + Bainite Martensite 1 1sec 1 min 1hr Transformation Time (Log. Scale) O a. 50% bainite and 50% martensite O b. 50% austenite and 50% bainite O c. 100% bainite O d. 100% martensite Finer Lamellac Bainitic Pearlitic Austenite Fine more Acicular Rapid Etching Martensitic cicular, Slow Etching V.P.H. 210 320 450 700 750
These questions are based on a high carbon stell with a composition of 1.5%C and 98.5%Fe 1)Name the phases present and calculate the amounts of these phases just above the eutectoid temperature. 2)With equilibrium cooling just below the eutectoid temperature calculate the total ferrite.
0-10) Compare the equilibrium spacing of two partial dislocations between an Al alloy (G=28GPa bie 0.165nm, stacking fault energy 200MJM ) and Gold (G=38GPA, bpartial3D0.166nm, SFE- 9mJm).
Question 7: The illustration shows the iron-carbon phase diagram. 1600 1400 1200 1000 800 600 400 1538°C 0 (Fe) 1493°C 1394°C 912°C 7. Austenite 0.76 0.022 a, Ferrite Y+L 2.14 Composition (at%C) 15 10 1147 C a+FezC Y+FeyC 4 3 Composition (wt% C) 727 C Cementite (FeyC). 2500 2000 1500 1000 6.70 Temperature (°F) e) Describe the changes in phase compositions of a carbon steel with a carbon content of 1 % (weight-%) from 1500°C down to 727°C with the help of the attached phase diagram and appropriate equations/reactions.
(0.4 + () × (-1)**) wt% C alloy at a temperature just below the eutectoid, 100 For a determine the fraction of eutectoid ferrite x* = 10 Temperature (°C) 1600 1400 1200 1000 600 1538 C 800 a 400 S 0 (Fe) 912°C -1493 C 1394°C 7. Austenite 0.76 0.022 , Ferrite 2.14 Composition (at%C) 15 10 1147 C a+FeyC L 4.30 y+FejC 4 Composition (wt% C) 727°C 20 Cementite (FeyC) 6 2500 2000 1500 1000 6.70 Temperature (F
Au and Ag form a substitutional solid solution. This means that the crystal structure of an Au-Ag alloy consists of Ag atoms substituting for Au atoms in the regular atomic positions of the FCC structure. For an Au-50 wt% Ag alloy, what fraction of the atomic sites does Ni occupy? NA=6.022e23 A. None of the mentioned/ Geen van die genoemde B. 32.31% C. 50% D. 64.61%
Q1 / Two metals Beryllium (Be) and Silicon (Si) have melting points 1282°C and 1414 °C respectively, are completely soluble as liquids but completely insoluble as solids . They form a eutectic at 1090°C containing 61 wt% Si -39wt% Be? Determine the following:- 1- Draw the thermal equilibrium phase diagram and identify all phases are present in diagram ,then sketches what happens in microstructure when the alloys containing , a- 10wt% Si, b-70wt%Si , solidify completely. 2- Determine the composition and the amount of each phase for the alloy which contain 15 wt% Si-85wt% Be at 1150°C If the alloy is hypoeutectic determine the amount of eutectic at 600 °C? or hypereutectic and
1. What temperature does a Fe-C metal with less than 4 weight percent C melt at? 2. What temperature does a Fe-C metal with less than two weight percent C melt at? 3. What climate causes delta-Fe to change into gamma-Fe? 4. What percentage of proeutectoid Fe 3C is present in a steel with 1.15 wt% carbon at 727.1 o C?