Tensile test had made to cylinder shape with diameter 3.0 In and length 5.7 In It had maximum elastic was under load at (128425r x10-2) Ib and deformed with 6.2 In length and 2.85 In diameter. This is correspond 0.2 percent yield point. Compute modulus of elasticity (ib/in2). pls i need it solved fast

Tensile test had made to cylinder shape with diameter 3.0 In and length 5.7 In It had maximum elastic was under load at (128425r x10-2) Ib and deformed with 6.2 In length and 2.85 In diameter. This is correspond 0.2 percent yield point. Compute modulus of elasticity (ib/in2). pls i need it solved fast

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.3P: A tensile test was performed on a metal specimen having a circular cross section with a diameter 0....

See similar textbooks

Similar questions

A tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.
A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.
Tensile test had made to cylinder shape with diameter 3.0 In and length 5.7 InIt had maximum elastic was under load at (128425 x10-2) Iband deformed with 6.2 In length and 2.85 In diameter.This is correspond 0.2 percent yield point.Compute modulus of elasticity (ib/in2). pls i need it solved fast
Tensile test had made to cylinder shape with diameter 3.0 In and length 5.7 InIt had maximum elastic was under load at (128425x10-2) Iband deformed with 6.2 In length and 2.85 In diameter.This is correspond 0.2 percent yield point.Compute modulus of elasticity (ib/in2)
A 40 mm diameter steel bar is subjected to a tension test. Under a tension load of 276.46 kN, it was observed that the original gage length of 50 mm increased in length by 0.055 mm, & the diameter decreased by 0.0105 mm. Find the modulus of elasticity (MPa) (in whole number)
A steel bar of 22 mm diameter and 8 cm gage length was axially loaded in tension and the following load deformation diagram was obtained. Determine: a) The yield strength by 0.2% off-set method. b) Modulus of elasticity by initial tangent method. c) Modulus of elasticity by tangent method at 2/3 of the yield strength. d) Modulus of elasticity by secant method at 70% of ultimate strength. e) Strain in fracture. Answer: a) 6576.7 kgf cm² b) 2.3x10° kgf/cm² e) 1.11x10° kgf/cm? d)1.49 kgf/cm² e)1.6% Bon) 30 25 20 15 10 DL (om a018 0.032 0.040 0.004 0.000 O.112 0.120
A steel bar of 22 mm diameter and 8 cm gage length was axially loaded in tension and the following load deformation diagram was obtained. Determine: a) The yield strength by 0.2% off-set method. b) Modulus of elasticity by initial tangent method. c) Modulus of elasticity by tangent method at 2/3 of the yield strength. d) Modulus of elasticity by secant method at 70% of ultimate strength. e) Strain in fracture.
A tensile test is carried out on a steel rod of 14mm radius and gauge length of 140 mm. The yield strength ofthe steel (fy) is 500 MPa. At the tension load of 50KN, calculate stress and strain in the steel rod, taking Young’smodulus (E) as 200,000 MPa. Find out if the steel rod is in elastic region or has already yielded. Compute also forthe shear modulus of Elasticity.
Bar A was manufactured 2 mm less than bar B due to an error. The attachment of these bars to the rigid bar wouldcause a misfit of 2 mm. Calculate the initial stress in each assembly. Which of the two assembly configurationyou would recommend? Use modulus of elasticity of E = 80 GPa and diameter of the circular bars as 32 mm.
Please present FBD/s A tensile test is performed on a brass specimen 10mm in diameter using a gage lenght of 50mm. When the tensile load P reaches a valule of 20kN, the distance between the gage marks has increased by 0.122mm. What is the modulus of elasticitiy of the brass?
USE NSCP 2015 as reference: B. Minimum/maximum value of steel strain(st) (from nscp2015). C. Minimum/maximum value of steel stress (fs), (derived from nscp2015).
Stress amplitude, S (MPa) 500 400 300 200 100 180 70 60 50 40 30 20 10 Stress amplitude (ksi) 1045 steel 2014-T6 aluminum alloy Red brass 0 0 10³ 104 105 107 108 109 1010 106 Cycles to failure, N 3-S-N curve for several different engineering materials (mean A 6.4 mm diameter cylindrical rod fabricated form 1045 steel is subjected to fully reversed tensile-compression loading. If the maximum tensile and compressive loads are 10300N, determine the fatigue life.