Q2/ Determine the weight and number average molecular weights as well as degree of polymerization for the polypropylene materials. Number Range of Molecular weight in gram/mol and weight fractions X₁ Wi 8000- 16000 0.05 0.02 16000- 24000 0.16 0.1 24000- 32000 0.24 0.2 32000- 40000 0.28 0.3 40000- 48000 0.20 0.27 48000- 56000 0.07 0.11

Q2/ Determine the weight and number average molecular weights as well as degree of polymerization for the polypropylene materials. Number Range of Molecular weight in gram/mol and weight fractions X₁ Wi 8000- 16000 0.05 0.02 16000- 24000 0.16 0.1 24000- 32000 0.24 0.2 32000- 40000 0.28 0.3 40000- 48000 0.20 0.27 48000- 56000 0.07 0.11

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The Occupational Safety and Health Administration has set a Permissible Exposure Limit of 1000 parts per million (ppm) of acetone. You are an industrial hygienist doing personal sampling on a worker who is supervising a production process that uses acetone. The upcoming exposures can be measured: 700 ppm for three hours and 1300 ppm for two hours. 3 hours at 900 ppm What is the TWA as calculated? What advice would you provide plant management regarding acetone exposure and PEL adherence?
What is the composition, in weight percent, of an alloy that consists of 94 1 at% Ag and 5.9 at% Cu? The atomic weights for Ag and Cu are 107.87 gimol and 63.55 g/mol, respectively O A 96 4 WI% Ag and 3.6 wt% Cu O B. 3.6 wt% Ag and 96 4 wt% Cu O C.9.8 wt% Ag and 90 4 wt% Cu OD 90.4 wt% Ag and 96 w% Cu
In an electrochemical cell, a metal anode lost 0.227 g while a total volume of 0.08149 L of hydrogen gas was produced. The temperature was 298 K and the barometric pressure was 745.4 mm Hg. At 298 K, the vapor pressure of water is 23.8 mm Hg. How many moles of hydrogen gas were collected?
2. Given the following data: Weight of the crushed core sample in air: Wtdry = 20.0 gm: Weight of the crushed core sample in water: Wtimm = 15.0gm Density of water:pw = 1.0 gm сс Use Archimedes' Principle to calculate the grain volume of the sample.
Q1.) Consider the unit cell of Mg as shown below : Beskou die Mg eenheidsel hieronder Mg HCP structure HDG struktuur Atomic radius 0.160nm Atoom radius Atomic weight Atoommassa c/a ratio / verhouding 24.31g/mol 1.624 НСР a) Calculate the lattice parameter of this unit cell; Bereken die roosterafmeting van die eenheidsel
5. Figure shows the cooling curve for aNiO-MgO ceramic. (e) the super heat; 2800 2700 2600 2525 2500 28 2400 10 20 30 40 50 Time (min) Temperature (°C)
2. Figure shows the cooling curve for aNiO-MgO ceramic. (b) the solidus temperature 2800 2700 2600 2525 2500 28 2400 10 20 30 40 50 Time (min) Temperature (°C)
Calcium (Ca) has the FCC crystal structure. The atomic radius is R = 0.197 nm and the atomic mass is M = 40.08 g/mole. What is the density of Calcium in g/cm3? Given: Avogadro's Number NA = 0.6023 × 1024 (atoms/mole) Select one: a. 5.30 b. 7.5 c. 6.77 d. 12.14 e. 1.534
Scandium (Sc) has the FCC crystal structure. The atomic radius is R = 0.16 nm and the atomic mass is M = %3D 44.96 g/mole. What is the density of Scandium in g/cm3? Given: Avogadro's Number NA = 0.6023 × 1024 (atoms/mole) %3D Select one: a. 12.14 b. 5.30 c. 12.55 d, 3.22 e. 6.77
What is the volume of 3.00 moles of copper? Molar mass of copper is 63.546 g/mol and its density is 8.9 x 103 kg/m3.
Europium has the Body-Centered Cubic (BCC) crystal structure shown in the figure below. The radius of the Europium atom is r=D0.204 nm. What is the planar density in atoms/nm2 in plane (200)? Plane (200) Select one: Oa 16.19 O6.4.507 Oc 10.79 Od.11.64 O30.82 9:13 PM O d0) ENG 15-Apr-2021
Scandium (Sc) has the FCC crystal structure. The atomic radius is R = 0.16 nm and the atomic mass is M = 44.96 g/mole. What is the density of Scandium in g/cm3? Given: Avogadro's Number NA = 0.6023 x 1024 (atoms/mole) Select one: O a. 5.30 O b. 12.55 О с. 3.22 O d. 6.77 О е. 12.14