Need asap Given the stress-strain behavior of a brass specimen below, estimate its Brinell hardness value.50070Tensile strength450 MPa (65,000 psi)60400A10° psi50300MPа 404030200Yield strength30200250 MPa (36,000 psi)2010010100100.0.005010.400.100.200.30StrainStress (MPa)20Stress (10° psi)

Answered: Image /qna-images/answer/bfb72771-dfa1-432c-8c2c-ed53845f96df.jpg

Given the stress-strain behavior of a brass specimen below, estimate its Brinell hardness value. 500 70 Tensile strength 450 MPa (65,000 psi) 60 400 50 103 psi 300 MPa 40 40 30 200 Yield strength 250 MPa (36,000 psi) 30 200 20 100 20 10 100 10 0.005 0.10 0.20 0.30 0.40 Strain Stress (MPa) Stress (103 psi)

Given the stress-strain behavior of a brass specimen below, estimate its Brinell hardness value. 500 70 Tensile strength 450 MPa (65,000 psi) 60 400 50 103 psi 300 MPa 40 40 30 200 Yield strength 250 MPa (36,000 psi) 30 200 20 100 20 10 100 10 0.005 0.10 0.20 0.30 0.40 Strain Stress (MPa) Stress (103 psi)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

200 stress (MPa) L00 50 0.1 0-2 strain From the tensile stress-strain behavior for the brass specimen ,d the diameter is 12-8 mm Calcalate the folbuding - |- The Yield stress. 2-Modulus of elasticity. 3- The Tensile strength.
The engineering stress-strain curve below was obtained for a precipitation hardened Aluminum alloy. What is the approximate Yield Strength for this alloy in psi? Engineering Stress Based on Original Area (psi) 50,000 45,000 40,000 35,000 30,000 25,000 20,000 15,000 10,000 5,000 0 O 0.02 0.04 0.06 Aluminum 6061-T6 0.08 0.1 0.12 Engineering Strain (in/in) 0.14 X 0.16 0.18
In tensile test a plain carbon steel specimen has a (40mm) gauge length and the Final area (A final) of specimen after tensile test was 264.327. The load which caused fracture was (122.5 KN). After fracture, the final length was 47.516mm True stress at fracture is. * O 463.441 N/mm2, O 525.441 N/mm2, O 254.441 N/mm2, 498.441 N/mm2,
Specimen (Rebar) Original Length Length when it was clamped Diameter (mm) Internal Diameter (mm) External 1 300 mm 163mm 10 15.030 2 300 mm 180 mm 10.020 14.386 3 300 mm 197mm 9.40 15.028 Dimension of Specimen Specimen A0 P max Tensile strength Modulus of elasaticity Percent Elongation 1 474 N 179.381 2.776 MPa 19.76 MPa 13.4% 2 475 N 159.070 2.895 MPa 18.74 MPa 16.67% 3 485 N 179.381 2.706 MPa 20.058 Mpa 13.4% Result of testing Observation What is the possible discussion of these tablesP.S THIS IS NOT GRADED, ITS JUST EXAMPLES
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 158 kN. - Length of the specimen is 26 mm. - The yield strength is 75 kN/mm?. - The percentage of elongation is 40 %. Determine the following iv) Young's Modulus if the elongation is 1 mm at 15 kN and Young's Modulus of the Specimen (in N/mm?)
Stress Strain Diagram The Data shown in the table have been obtained from a tensile test conducted on a high-strength steel. The test specimen had a diameter of 0.505 inch and a gage length of 2.00 inch. Using software. plot the Stress-Strain Diagram for this steel and determine its: A= TTdT(050s A %3D 1. Proportional Limit, 2. Modulus of Elasticity, 3. Yield Strength (SY) at 0.2% Offset, 4. Ultimate Strength (Su), 5. Percent Elongation in 2.00 inch, 6. Percent Reduction in Area, 7. Present the results (for Steps 1-6) in a highly organized table. e Altac ie sheet (as problelle 4 A = 0.2.002 BEOINNING of the effort Elongation (in) Elongation (In) Load Load #: #3 (Ib) (Ib) 1 0.0170 15 12,300 0.0004 1,500 16 12,200 0.0200 0.0010 3. 3,100 17 12,000 0.0275 0.0016 4,700 18 13,000 0.0335 5. 6,300 0.0022 19 15,000 0.0400 0.0026 6. 8,000 20 16,200 0.055 0.0032 9,500 21 17,500 0.0680 0.0035 8. 11,000 22 18,800 0.1080 0.0041 11,800 23 19,600 0.1515 0.0051 24 20,100 0.2010 10 12,300 0.0071 25…
Determine the load on the specimen that causes yielding. Express your answer to three significant figures and include appropriate units. The stress-strain diagram for a steel alloy having an original diameter of 0.40 in. and a gage length of 9 in. is shown in the figure below. (Figure 1) ? Py = Value Units Submit Request Answer Part C Figure < 1 of 1 Determine the ultimate load the specimen will support. Express your answer to three significant figures and include appropriate units. o (ksi) 80 HA ? 70 60 Value Units 50 Pu = 40 30 Submit Request Answer 20 10 € (in./in.) 0 0.04 0.08 0.12 0,16 0,20 0,24 028 O 0.0005 0.001 0.0015 0.002 0.0025 0.0030.0035 Provide Feedback
The following stresses were measured for a specimen: 011 = 94 MPa; 022 = 155 MPa; ơ12 = 85 MPa Determine whether not yielding occurred using both the Tresca and von Mises criteria, given that oys = 180 MPa. Which criterion is more conservative?
A ul ? KBIS M 1:11 O photo_2021-0... -> 200 stress 150 (MPa) (00 50 0-2 strain From the tensile stress-strain behavior for the brass specimen d the diamcter is 12-8 mm Calculate the folluding:- 1- The Yield stress. 2- Modulus of elasticity. 3 - The Tensile strength . II
. From the tensile stress-strain behaviour for a casted iron as shown in the following curve. Please answer the following questions (1) Estimate the modulus of elasticity, (2) Calculate the change in length of a specimen with original length of 100mm that is subjected to a tensile stress of 300MPa. (Hint: Using the Hooke's law to get the strain.) 600 500 400 - 300 - 200 - 100 - 2 4 6. 8 10 12 14 16 Strain Strength (MPa)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 158 kN. - Length of the specimen is 26 mm. - The yield strength is 75 kN/mm?. - The percentage of elongation is 40 %. Determine the following (v) Final diameter if the percentage of reduction in area is 21 %. Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
Asiacell l. ZA0 @ 团 / photo_2021-02-18_13-04... 200 stress 150 (MPa) 100 50 0.1 0-2 0.3 strain From the tensile stress -strain behavior for the brass specimen ,cP the diameter is 12-8 mm Calculat e the follouding :- 1- The Yield stress , 2-Modulus of elasticity. - The Tensile strength .