Figure 1. shows the rolling operation. Determine the position bn. of the neutral point? Neglect front and back tensions. Additional data: Hardened steel 0.04 μm and rolling temperature -190°C. rolls, surface roughness of the rolls D 0.3 in. F-5tus R=4 in. Fig:1 0.1 in. 7 fus

Figure 1. shows the rolling operation. Determine the position bn. of the neutral point? Neglect front and back tensions. Additional data: Hardened steel 0.04 μm and rolling temperature -190°C. rolls, surface roughness of the rolls D 0.3 in. F-5tus R=4 in. Fig:1 0.1 in. 7 fus

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: An annealed copper strip 9 in wide having. K=80,000 psi, N=0.60, and a height of 1 in _was flat…

Q: Specify How to improve the structure of steel after hot rolling?

A: Hot rolling is the process of the metal is heated at high temperature and the compressed through…

Q: B. Write any four major forging defects and solution for those defects.

A: Defects in Forging: 1) Incomplete filling of dies: Undersize of forging due to less amount of…

Q: coefficient of friction between the roll and the plate i

A: Given; In a rolling operation using rolls of;Diameter,D=400 mmThickness, t=35mmFor the given…

Q: Determine the value of the extrusion pressure (P/o) for the manufacture of a bar with a square…

Q: Estimate the 10³-cycle fatigue strength for rotating bending and also the bending endurance limit…

Q: i still dont think i am getting the full working how you get to 0.32, am going to need to see the…

A: Given Data

Q: Fib the time period, if pure rolling is the condition

A: Given data: Roller connected to spring is released from the inclined plane To determine: Time…

Q: As James orbits, he slams into a space elevator, peals himself off, and gets in. On the way down, he…

A: Write down the given values using suitable variables. Here L signifies leg length, m signifies leg…

Q: How does torsional stress and angle of twist impact engineering design?

A: Importance of torsional stress in Engineering Design:- Torsional stress is induced in an element due…

Q: 9.17 For the die casting shown in Figure P9-17, determine the maximum stresses and their locations.…

A: It is asked to find the maximum stress and locations

Q: In drawing Process, consider the streng H Coefficient = 546-4 and Do=3.5 mm dF= 3.1mm, angle=…

Q: Using the rolling process significant improvement is accomplished in rolled parts in their various…

A: There are two types of rolling processes one is hot rolling and other one is cold rolling but the…

Q: rance for bl ce of 2% pe се

Q: Name the four basic bulk deformation processes.

A: Given:

Q: In a metal forming operation when the materia. has just started yielding, the principal stresses…

Q: In a 'tandem' rolling process, a wide metal strip passes continuously between four sets of rolls,…

Q: A round disk of 200-mm diameter is blanked from a strip of 3.0-mm, half-hard cold-rolled steel whose…

A: Given data: d=200 mmt=3 mmτ=300 MPaAc=0.075 Need to determine the punch, die diameters and blanking…

Q: What happens to the shear stress as flexural capacity increases?

A: It is the strength of any beam against transverse loads applied on them. It is given by 'EI', where…

Q: Check and state in your answer booklet which of the following statements is False and which is True.…

A: 1) False- Elastic region is characterised by proportional relationship between stress and strain.…

Q: A compression test is performed on a 2” diameter by 5” long bar of an unknown metal. At the end of…

A: Given:d1=2 inl1=5 inl2=3.5 inK=250 MPan=0.4a)Volume before compression=volume after compression…

Q: B) A machine part is made of forged steel with Su = 630 MPa, S'. = 0.5 Su. Estimate the life cycles…

A: When external load acting on a component is not static, but varying in magnitude with respect to…

Q: 4. In rolling operation, large diameter roll induces.. on the surface of the rolled part. b. tension…

A: Explanation : During rolling operation , due to rolling extrusion force applies over the surface to…

Q: Material: Carbon Steel C1018 (AISI 1018) Cold Draw Property: Yield Strength (psi) 53,700

A: GIVEN =C1018 CARBON STEEL MATERIAL [AISI 1018 ]

Q: A flat-rolling operation of 250 mm wide alloy stee Calculate roll torque

A: GIVEN: **Width (Wt)=250mm **Diameter of rollers (D)=600mm **Height before rolling (ho)=30mm**Height…

Q: I need the answer as soon as possible

A: Given data; hi=300 mmhf=295 mmR=300 mmN=100 rpmζavg=180 mpa

Q: A do = 50 mm and ho = 75 mm billet of a 2017 Al alloy is to be compressed to a hi = 20 mm height in…

A: billet specifications,d0=50 mm ,ho=75 mm ,After compression,h1=20 mmT=500o C

Q: In the open die forging ,a high precision is obtained. Select one: True False

A: In Open die forging, a rough or precision machining is regularly advance required after the open…

Q: What is the true sliding strain for a low carbon steel bar which is doubled

A: Given:Low carbon steel

Q: Estimate the power for annealed low carbon steel strip 200 mm wide and 10 mm thick, rolled to a…

A: Rolling is a metal forming process in which a material is plastically deformed by passing it between…

Q: Identify at least FIVE (5) factors that affect the Force, F in Figure

A: factors affect the force in above fig these factors leads to improper process and non uniform force…

Q: Compare the differences between hot and cold rolled steel in terms of their processing and…

A: COLD Rolled Hot Rolled done below recrystallization temperature, done above recrystallisation…

Concept explainers

Forming and Shaping

Metal forming is a category of metalworking process through which the material can be given the desired shape and size by subjecting it to plastic deformation, where the component undergoes bulk deformation process upon application of loads. Unlike the shearing and machining process, the material does not undergo up to a failure point as indicated in the stress-strain curve. Hence, the stresses induced during the forming process are greater than yield strength but less than the failure strength of the material. The process does not lead to the loss of material, so it can be said to be an economical process. During forming, the material is subjected to tensile forces, compressive forces, bending, and shearing loading conditions. The material should possess the property of ductility to undergo the forming process.

Question

Figure 1. shows the rolling operation. Determine the position bn. of the neutral point? Neglect front and back tensions. Additional data: Hardened steel
0.04 μm and rolling temperature -190°C.
rolls, surface roughness of the rolls
0.3 in.
1=Stl/s
R=4 in.
Fig:1
0.1 in.
7 ft/s

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1: Determine the given data

VIEW

Step 2: Calculate the position

VIEW

Solution

VIEW

Step by step

Solved in 3 steps with 5 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

The engineering stress-engineering strain tensile curve for a stainless steel type 304 alloy is shown. Calculate the constants K and n for the true stress and true strain curve before necking (or = K (&)"). Engineering Stress (MPa) 1000 900- 800- 700- 600- 500- 400- 300- 200- 100- of 0.0 02 0.4 Enginering Strain (mm/mm) 0.6 0.8 1.0
Homework: In hot rolling process, the following data was collected: N=20rpm, R=20cm, to=40mm, tF35mm, C=415MPA, m=0.02, w-60cm one pass rolling. Find Froll, T and Power.
Hi, can you help me solve the attached problem where I am asked to calculate the total force to obtain a component from an initial aluminum bar by using the manufacturing process of cold rolling.
An annealed copper strip 9 in wide having .2 K=80,000 psi, N=0.60, and a height of 1 in _was flat rolled to a height of 0.90 in with 12 in roller radius rotating at 120 rpm a) Calculate the force and the power .needed to operate this Process
3XPL@!N THE PROCESS @ND PROVIDE EXAMPLES FORMING OPERATIONS 1. Forging is mechanically working or deforming a single piece of a usually hot metal; this may be accomplished by the application of successive blows or by continuous squeezing. 2. Rolling, the most widely used deformation process, consists of passing a piece of metal between two rolls; a reduction in thickness results from compressive stresses exerted by the rolls. 3. Extrusion, a bar of metal is forced through a die orifice by a compressive force that is applied to a ram; the extruded piece that emerges has the desired shape and a reduced cross-sectional area. 4. Drawing is the pulling of a metal piece through a die having a tapered bore by means of a tensile force that is applied on the exit side.
Q4: Proof the validity true strain additive feature in compression deformation?
3- A planned extrusion operation involves cold-rolled steel at 1000° C to diameter of 75 mnm with length 65 mm and a final length 70 mm Two presses, one with capacity (extrusion force) of 30 MiN and the other with a capacity (extrusion force) of 20 MN, are available for the operation. Is the smaller press sufficient for this operation? K"=35x10*3 N [Hint: Calculate the extrusion force and compare it to the available two presses!
i need the answer quickly
5 Hot rolling of mild steel is carried out. a. Between recrystallization temperature b. Above recrystallization temperature c. Between 100⁰C to 150⁰C d. At recrystallization temperature
Name the following terms
calculte the position of the nuetral point, xn
Choose the best