An elastoplastic material with strain hardening has the stress– strain relation shown in Figure aside. The modulus of elasticity is 25 x 106 Psi. , yield strength is 70 ksi, and the slope of the strain-hardening portion of the stress–strain diagram is 3 x 106 Psi. a. Calculate the strain that corresponds to a stress of 85 ksi. b. If the 85-ksi stress is removed, calculate the permanent strain.

An elastoplastic material with strain hardening has the stress– strain relation shown in Figure aside. The modulus of elasticity is 25 x 106 Psi. , yield strength is 70 ksi, and the slope of the strain-hardening portion of the stress–strain diagram is 3 x 106 Psi. a. Calculate the strain that corresponds to a stress of 85 ksi. b. If the 85-ksi stress is removed, calculate the permanent strain.

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 6.2P

See similar textbooks

Similar questions

An elastoplastic material with strain hardening has the stress-strain relation shown below. The modulus of elasticity is 25 x 106 psi, yield strength is 70 ksi, and the slope of the strain-hardening portion of the stress-strain diagram is 3 x 106 psi. a. Calculate the strain that corresponds to a stress of 80 ksi. b. If the 80-ksi stress is removed, calculate the permanent strain.
Problem 11. [Concepts: Calculating stress from internal forces, nonlinear stress-strain response, elongation from strain.] Acetal plastic has a stress-strain diagram as shown. a) Determine the yield strength assuming a 0.2% offset. b) If a bar of this material has a length of 3 ft and cross-sectional area of 0.875 in², and is subjected to an axial load of 2.5 kip, determine its elongation. c) Determine the modulus of toughness just before it fractures if failure occurs at a = 0.12. σ (psi) a = 9.5(10³) €¹/3 € (in./in.)
An elastoplastic material with strain hardening has the stress–strain relationship shown in Figure . The modulus of elasticity is 25 * 106 psi, yield strength is 70 ksi, and the slope of the strain-hardening portion of the stress–strain diagram is 3 * 106 psi.a. Calculate the strain that corresponds to a stress of 80 ksi.b. If the 80-ksi stress is removed, calculate the permanent strain.
An elastoplastic material with strain hardening has the stress-strain relation shown in the figure. The yield point corresponds to 600 MPa stress and 0.003 m/m strain.Determine the following:a. If a bar made of this material is subjected to a stress of 650 MPa and then released, what is the permanent strain?b. What is the percent increase in yield strength that is gained by the strain hardening shown in part (a)?c. After strain hardening, if the material is subjected to a stress of 625 MPa, how much strain is obtained? Is this strain elastic, permanent, or a combination of both?
A cylindrical specimen of stainless steel having a diameter of 12.8 mm (0.505 in.) and a gauge length of 50.800 mm (2.000 in.) is pulled in tension. Use the load–elongation characteristics shown in the following table to answer the following: a. Plot the data as engineering stress versus engineering strain. b. Compute the modulus of elasticity. 66 c. Determine the yield strength at a strain offset of 0.002. d. Determine the tensile strength of this alloy. e. What is the approximate ductility, in percent elongation? f. Compute the modulus of resilience
Your answer is incorrect. An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 500 mm. The cross-sectional dimensions of the beam areb1 = 35 mm, d1= 115 mm, b2= 21 mm, d2 = 21 mm, and a =7 mm. For this material, the allowable tensile bending stress is 15 MPa, and the allowable compressive bending stress is 14 MPa. Determine the largest moment M that can be %3D %3D %3D %3D %3D %3D applied as shown to the beam. b2 a 不 d2 d1 b1 Answer: N-m M% =
An elastoplastic material with strain hardening has the stress–strain relationship shown in Figure . The yield point corresponds to 600 MPa stress and 0.003 m/m strain.a. If a bar made of this material is subjected to a stress of 650 MPa and then released, what is the permanent strain?b. What is the percent increase in yield strength that is gained by the strain hardening shown in part (a)?c. After strain hardening, if the material is subjected to a stress of 625 MPa,how much strain is obtained? Is this strain elastic, permanent, or a combination of both?
1. An elastoplastic material with strain hardening has the stress strain relationship shown below. The yield point is as a stress of 600 MPa and strain of 0.003 mm/mm. a. If a bar of this material was loaded to a stress of 650 MPa and then released, what would be the permanent strain? b. What would be the percent increase in yield strength gained by the strain hardening for a? c. A second load to a stress of 625 MPa is then applied. How much strain is expected? Is the deformation elastic, plastic, or a combination? Stress, MPa 11 ■ 1000 800 600 400 200 Od 0 0.02 0.04 Strain, m/m 0.06 0.08
2. A steel bar, whose cross section is 0.55 inch by 4.05 inches, was tested in tension. An axial load of P = 30,500 lb. produced a deformation of 0.105 inch over a gauge length of 2.05 inches and a decrease of 0.0075 inch in the 0.55-inch thickness of the bar. Determine the lateral strain. * Your answer Determine the axial strain. Your answer Determine the Poisson's ratio v. * Your answer Determine the decrease in the 4.05-in. cross-sectional dimension (in inches). * Your answer
PROBLEM 1 A steel rod with a cross sectional area of 150 mm? is stretched between two fixed points. The tensile load at 20°C is 5000 N. a.) What will be the stress at -20°C? b.) At what temperature will the stress be zero? Assume a = 11 .7 µm/m°C, and E = 200 Gpa *Show geometry of deformation ©sidewar
Which of these elastic moduli describes the ratio between volumetric stress and volumetric strain?a. Young’s Modulusb. Shear Modulusc. Bulk Modulusd. Poisson’s Ratio
An aluminum alloy cylinder with a diameter of 76 mm and a height of150 mm. is subjected to a compressive load of 220 kN. Assume that the material is within the elastic region and a modulus of elasticity of 75 GPa.a. What will be the lateral strain if Poisson’s ratio is 0.33?b. What will be the diameter after load application?c. What will be the height after load application?