A welding operation on an aluminum alloy makes a groove weld. The cross-sectional area of the weld is 30.0 mm2. The welding velocity is 4.0 mm/sec. The heat transfer factor is 0.92 and the melting factor is 0.48. The melting temperature of the aluminum alloy is 650°C. Determine the rate of heat generation required at the welding source to accomplish this weld.

A welding operation on an aluminum alloy makes a groove weld. The cross-sectional area of the weld is 30.0 mm2. The welding velocity is 4.0 mm/sec. The heat transfer factor is 0.92 and the melting factor is 0.48. The melting temperature of the aluminum alloy is 650°C. Determine the rate of heat generation required at the welding source to accomplish this weld.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Two 1.2 mm thick flat copper sheets are being spot welded using a current of 6000A and a current flow time of 0.18 s. The electrodes are 5 mm in diameter. Estimate the generated in the weld zone. Take effective resistance as 150 ohm. also calculate temperature rise assuming that the heat generated is confined to the volume ogf materials directly between two electrodes and temperature is uniformly distributed.
A corner fillet weld with cross sectional area of 75 mm is made using oxyacetylene welding. Material of the welded plates is low carbon steel (Um = 10.3 J/mm'. Travel speed at which the bead is formed = 5 mm/s. Assume that only 40% of the energy generated by the torch is used for melting the metal; the rest is dissipated. If heat of combustion for acetylene is= 54.8 MJ/m³ , determine the volume flow rate of acetylene required to perform this OAW operation.
8) The correct ways to control liquation cracking tendency in fusion weld joint are I. Use of filler metal that solidifies before the partially melted zone I. Use of single pass welding with higher net heat input instead of multipass welding III. Use of high energy density processes IV. Preheating the substrates V. Use of base metals with fine grain structure OI, II, and III II, and IV OII, IV, and V O II, III and IV
I need the answer as soon as possible
Welding is a process that is used to attach pieces of metal to one another. In a certain welding process, small pieces of Al (s) and CuO (s) are placed in a crucible and ignited, causing the following highly exothermic reaction to occur. 2 Al+ 3 Cuo - 3 Cu + Al,O3 The copper and aluminum oxide melt. The molten aluminum oxide floats to the top of the crucible. When the steel disk below the crucible melts, the molten copper flows into the weld cavity and welds the pieces of metal together as it cools and solidifies. The setup is represented in the following diagram. Mixture of Al(s) and CuO(s) Crucible Steel Disk Weld Cavity Pieces of Metal to Be Connected
ANSWER FAS WITH A SUMMARIZED SOLUTION
During a TIG welding process, the arc current and arc voltage were 50 A and 60 V, respectively, when in the welding speed was 150 mm/min. In another process, the TIG welding is carried out at a welding speed of 120 mm/min at the same arc voltage and heat input to the material so that weld quality remains the same. The welding current (in A) for this process is
5. A steel cylindrical air receiver with 5 feet diameter and pressure load of 180 psi, design stress of 9500 psi maximum. The pressure vessel is to be provided with a 1.5 in diameter drain valve installed at the bottom of the vessel and a safety pressure relief valve is installed either at the topmost or at the side with a pop-out rating of 200 psi. Assume a 100% weld joint efficiency. The lap welding tensile strength is 65,000 psi. Determine the bursting pressure of this air receiver. psi
I need the answer as soon as possible
An arc welding operation on nickel performs a groove weld, whose cross-sectional area = 20.0 mm2. The melting point of nickel Tm = 1725° Travel velocity = 4.0 mm/sec. Heat transfer factor = 0.82, and melting factor = 0.70. Determine the rate of heat generation required at the welding source to accomplish this weld.
During arc welding, the heat input per unit length reduces, with increase of