A mild steel specimen is under uniaxial tensile stress. Young's modulus and yield stress for mild steel are 2 x 105 MPa and 250 MPa respectively. The maximum amount of strain energy per unit volume that can be stored in this specimen without permanent set is

A mild steel specimen is under uniaxial tensile stress. Young's modulus and yield stress for mild steel are 2 x 105 MPa and 250 MPa respectively. The maximum amount of strain energy per unit volume that can be stored in this specimen without permanent set is

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

Engineering strain of a mild steel sample is recorded as 0.100%. The true strain is 1. 2. 3. 4. 0.010% 0.055% 0.099% 0.101%
Please solve it fast A mild steel specimen having Young’s modulus of 200 GPa and original length of 300 mm is tested for a stress of value 500 MPa. Find the resultant elongation in the specimen.
The lowest stress at which permanent .deformation can be measured
A mild steel specimen with an original length of 300 mm long is acted on with a tensile stress of 500 MPa. If the deformation is entirely elastic, compute the resultant elongation? The modulus of elasticity of mild steel is 200 GPa.
The following information about the o-e curve is given for a steel alloy. E = 0.001527 at o = 300 MPa and ɛ = 0.003054 for o = 600 MPa. (a) Draw the stress-strain diagram and calculate the E for this alloy.
A single zinc crystal is loaded in tension with the normal to its slip plane at 60° to the tensile axis and the slip direction at 40° to the tensile axis. a) Calculate the resolved shear stress when a tensile stress of0.69 MPa is applied. b) What tensile stress is necessary to reach the critical resolved shear stress of 0.94 MPa?
"Engineering Stress-Strain Curve" for a low carbon steel obtained as a result of the tensile test test. In terms of plastic forming by drawing important points on it (rolling, forging, machining ... etc.) Explain its importance.
A steel plate used for polymer forming is to be bent into a circular shape having an inside radius of 10 m. What maximum thickness can be used for the plate if the normal stress is not to exceed 267 MPa? Assume that the modulus of elasticity for the steel is 201 GPa.
A hollow steel cylinder 3.5m which has an inside diameter and outside diameter of 55mm and 35mm. If the steel carry a load (17) KN find the stress in the cylinder also find the deformation in the cylinder if the Modulus of Elasticity is 90 GPA.
For some metal alloy, a true stress of 345 MPa (50040 psi) produces a plastic true strain of 0.02. How much will a specimen of this material elongate when a true stress of 411 MPa (59610 psi) is applied if the original length is 450 mm (17.72 in.)? Assume a value of 0.22 for the strain-hardening exponent, n. i mm
Determine induced stress
Narrow bars of aluminum are bonded to the two sides of a thick steel plate as shown. Initially, at T₁ = 70°F, all stresses are zero. Knowing that the temperature will be slowly raised to T₂ and then reduced to T₁, determine (a) the highest temperature T₂ that does not result in residual stresses, (b) the temperature T₂ that will result in a residual stress in the aluminum equal to 58 ksi. Assume aa = 12.8 x 10-6/°F for the aluminum and a = 6.5 × 10-6/°F for the steel. Further assume that the aluminum is elastoplastic with E = 10.9 × 106 psi and ay = 58 ksi. (Hint: Neglect the small stresses in the plate.) Fig. P2.121