A 50 wt% Ni-50 wt% Cu alloy is slowly cooled from 1400°C to 1200°C. (a) At what temperature does the first solid phase form? (b) What is the composition of this solid phase? 96 of Ni (c) At what temperature does the liquid solidify? (d) What is the composition of this last remaining liquid phase? °C °C 96 of Ni 4

icon
Related questions
Question
7
t of
A 50 wt% Ni-50 wt% Cu alloy is slowly cooled from 1400°C to 1200°C.
(a) At what temperature does the first solid phase form?
(b) What is the composition of this solid phase?
(c) At what temperature does the liquid solidify?
% of Ni
°C
(d) What is the composition of this last remaining liquid phase?
°C
96 of Ni
Transcribed Image Text:7 t of A 50 wt% Ni-50 wt% Cu alloy is slowly cooled from 1400°C to 1200°C. (a) At what temperature does the first solid phase form? (b) What is the composition of this solid phase? (c) At what temperature does the liquid solidify? % of Ni °C (d) What is the composition of this last remaining liquid phase? °C 96 of Ni
Temperature (°C)
1600
1500
1400
1300
1200
1100
1000
1085C
0
(Cu)
20
Liquid
Liquidus line
40
a +L
a
60
Composition (wt% Ni)
1453°C
Solidus line
80
2800
Time left 2:1
2600
2400
2200
2000
100
(Ni)
Temperature (°F)
Transcribed Image Text:Temperature (°C) 1600 1500 1400 1300 1200 1100 1000 1085C 0 (Cu) 20 Liquid Liquidus line 40 a +L a 60 Composition (wt% Ni) 1453°C Solidus line 80 2800 Time left 2:1 2600 2400 2200 2000 100 (Ni) Temperature (°F)
Expert Solution
steps

Step by step

Solved in 3 steps with 2 images

Blurred answer